Thermoplastic biodegradable plastic and preparation method thereof

A biodegradable plastic and thermoplastic technology, applied in the field of thermoplastic biodegradable plastic and its preparation, can solve the problems of difficult large-scale industrialization of PPC, low glass transition temperature, poor processing performance, etc. Good performance and enhanced thermal stability

Pending Publication Date: 2021-11-30
吴春秋
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing biodegradable plastics have many problems such as poor plasticity. For example, polymethylethylene carbonate (PPC) has the advantages of good flexibility, high elongation at break, high barrier properties, etc., but PPC has vitrification. Low transition temperature, relatively flexible, poor processability and other shortcomings make it difficult for PPC to achieve large-scale industrialization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermoplastic biodegradable plastic and preparation method thereof
  • Thermoplastic biodegradable plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A thermoplastic biodegradable plastic, comprising the following raw materials in parts by mass: 20 parts of starch, 20 parts of polybutylene adipate terephthalate, 60 parts of propylene oxide, 30 parts of methylene chloride, 30 parts of hydrochloric acid, 30 parts of methanol solution, 1 part of maleic anhydride, 10 parts of calcium carbonate, 5 parts of crosslinking agent, and 1 part of catalyst;

[0027] The preparation method of described thermoplastic biodegradable plastics, comprises the following steps:

[0028] Step 1: Add mass parts of catalyst to stainless steel autoclave, dry at 80°C for 24 hours, add mass parts of propylene oxide and maleic anhydride, and introduce CO 2 Gas, make the pressure reach 4MPa, the stirring speed is 100r / min, the reaction temperature is 70°C, react for 24h, after the reaction stops, cool to room temperature to obtain a viscous substance;

[0029] Step 2: Rinse the viscous matter twice with dichloromethane, hydrochloric acid, and di...

Embodiment 2

[0032] A thermoplastic biodegradable plastic, comprising the following raw materials in parts by mass: 40 parts of starch, 60 parts of polybutylene adipate terephthalate, 100 parts of propylene oxide, 50 parts of methylene chloride, 50 parts of hydrochloric acid, 50 parts of methanol solution, 10 parts of maleic anhydride, 20 parts of calcium carbonate, 15 parts of crosslinking agent, 10 parts of catalyst;

[0033] The preparation method of described thermoplastic biodegradable plastics, comprises the following steps:

[0034] Step 1: Add mass parts of catalyst to stainless steel autoclave, dry at 90°C for 24 hours, add mass parts of propylene oxide and maleic anhydride, and introduce CO 2 Gas, so that the pressure reaches 6MPa, the stirring speed is 300r / min, the reaction temperature is 90°C, and the reaction is for 24h. After the reaction stops, cool to room temperature to obtain a viscous substance;

[0035] Step 2: Rinse the viscous matter three times with dichloromethane...

Embodiment 3

[0038] A thermoplastic biodegradable plastic, comprising the following raw materials in parts by mass: 30 parts of starch, 40 parts of polybutylene adipate terephthalate, 80 parts of propylene oxide, 40 parts of methylene chloride, 40 parts of hydrochloric acid, 40 parts of methanol solution, 5 parts of maleic anhydride, 15 parts of calcium carbonate, 10 parts of crosslinking agent, 5 parts of catalyst;

[0039]The preparation method of described thermoplastic biodegradable plastics, comprises the following steps:

[0040] Step 1: Add mass parts of catalyst to stainless steel autoclave, dry at 85°C for 24 hours, add mass parts of propylene oxide and maleic anhydride, and introduce CO 2 Gas, so that the pressure reaches 5MPa, the stirring speed is 200r / min, the reaction temperature is 80°C, react for 24h, after the reaction stops, cool to room temperature to obtain a viscous substance;

[0041] Step 2: Rinse the viscous matter three times with dichloromethane, hydrochloric aci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of degradable plastics, and in particular, relates to a thermoplastic biodegradable plastic and a preparation method thereof. The thermoplastic biodegradable plastic comprises the following raw materials in parts by mass: 20-40 parts of starch, 20-60 parts of poly(butylene adipate-co-terephthalate), 60-100 parts of epoxypropane, 30-50 parts of dichloromethane, 30-50 parts of hydrochloric acid, 30-50 parts of a methanol solution, 1-10 parts of maleic anhydride, 10-20 parts of calcium carbonate, 5-15 parts of a cross-linking agent and 1-10 parts of a catalyst. The raw materials have good compatibility, and the plastic has good biodegradability, good thermoplasticity, high mechanical strength, simple production and low production cost, and has positive significance for environmental protection and actual production application.

Description

technical field [0001] The invention relates to the technical field of degradable plastics, in particular to a thermoplastic biodegradable plastic and a preparation method thereof. Background technique [0002] With the advantages of low cost, strong plasticity and light weight, plastics quickly occupy an extremely important market in the world industry. The market demand for plastic products mainly focuses on agricultural plastic products, packaging plastic products, construction plastic products, industrial transportation and engineering plastic products, etc. . With the widespread use of plastic products and the discarding of plastic product waste, because traditional plastics are difficult to degrade and plastic waste brings serious environmental problems, more and more people realize the importance of developing degradable plastics to replace traditional plastics . [0003] Biodegradable plastics are considered to be one of the important ways to solve the "white pollu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L67/02C08L3/04C08L77/12C08K3/26C08K5/14C08G64/34
CPCC08L69/00C08G64/34C08L2201/08C08K2201/011C08K2003/265C08L2201/06C08L67/02C08L3/04C08L77/12C08K3/26C08K5/14
Inventor 吴春秋李玲群
Owner 吴春秋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap