Sealing protection rubber coating material and preparation method thereof

A rubber coating and coating technology, applied in rubber derivative coatings, cleaning methods and utensils, chemical instruments and methods, etc., can solve the problems of lower coating production efficiency, slow mixing between raw materials, and short sealing protection period, so as to improve sealing Protective effect and adhesion, improve coating anti-corrosion performance, optimize the effect of powder addition process

Inactive Publication Date: 2021-09-17
NANJING YUSONG MATERIAL TECH CO LTD
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a sealing and protective rubber coating and a preparation method thereof, which can effectively solve the problem that the weather resistance and adhesion of the rubber coating proposed in the above-mentioned background technology are average, and the hardness of the paint film is low, and the performance of the rubber coating declines rapidly in open-air corrosive environments. As a result, the sealing protection period is short, which limits its practical application. At the same time, during the powder addition process during the production of rubber coatings, the powder is easy to adhere to the inner wall of the reaction tank, and at the same time, the raw materials cannot be mixed during the mixing process. Efficient stirring, which leads to slow mixing between raw materials and reduces the production efficiency of coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sealing protection rubber coating material and preparation method thereof
  • Sealing protection rubber coating material and preparation method thereof
  • Sealing protection rubber coating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Such as Figure 1-2 As shown, the present invention provides a kind of technical scheme, a kind of preparation method of sealing protective rubber coating, comprises the steps:

[0042] S1. Material preparation: select and weigh the required raw materials according to the production target, and transport the raw materials to the side of the reaction tank 1 for addition in the subsequent production process;

[0043] S2. Soaking and mixing: add chlorosulfonated polyethylene, chlorinated rubber, styrene-based elastomer, dispersant, and solvent into reaction tank 1, soak for 12 hours, and then stir at 600 rpm for 30 minutes;

[0044] S3. Stirring and grinding: ceramic whiskers, ceramic powder, carbon nanotubes, titanium dioxide, fumed silica, coupling agents, ultraviolet absorbers, and antioxidants are added to the interior of the reaction tank 1 through the convenient feeding and stirring mechanism 9 , and disperse at a high speed of 800 rpm for 10 minutes, then add the m...

Embodiment 2

[0077] Such as Figure 1-2 As shown, the present invention provides a kind of technical scheme, a kind of preparation method of sealing protective rubber coating, comprises the steps:

[0078] S1. Material preparation: select and weigh the required raw materials according to the production target, and transport the raw materials to the side of the reaction tank 1 for addition in the subsequent production process;

[0079] S2. Soaking and mixing: add chlorosulfonated polyethylene, chlorinated rubber, styrene-based elastomer, dispersant, and solvent into reaction tank 1, soak for 12 hours, and then stir for 40 minutes at 700 rpm;

[0080] S3. Stirring and grinding: ceramic whiskers, ceramic powder, carbon nanotubes, titanium dioxide, fumed silica, coupling agents, ultraviolet absorbers, and antioxidants are added to the interior of the reaction tank 1 through the convenient feeding and stirring mechanism 9 , and adopt 900 rpm high-speed dispersion for 13 minutes, then add the m...

Embodiment 3

[0090] Such as Figure 1-2 As shown, the present invention provides a kind of technical scheme, a kind of preparation method of sealing protective rubber coating, comprises the steps:

[0091] S1. Material preparation: select and weigh the required raw materials according to the production target, and transport the raw materials to the side of the reaction tank 1 for addition in the subsequent production process;

[0092] S2. Soaking and mixing: add chlorosulfonated polyethylene, chlorinated rubber, styrene-based elastomer, dispersant, and solvent into reaction tank 1, soak for 12 hours, and then stir for 50 minutes at 800 rpm;

[0093] S3. Stirring and grinding: ceramic whiskers, ceramic powder, carbon nanotubes, titanium dioxide, fumed silica, coupling agents, ultraviolet absorbers, and antioxidants are added to the interior of the reaction tank 1 through the convenient feeding and stirring mechanism 9 , and use 1000 rpm high-speed dispersion for 15 minutes, then add the mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sealing protection rubber coating material and a preparation method thereof. The preparation method comprises the following steps: material preparing, wherein raw materials needing to be used are selected and weighed according to production targets, and are carried to the side of a reaction tank for addition in a subsequent production process; and soaking mixing, wherein chlorosulfonated polyethylene, a chlorinated rubber, a styrene elastomer, a dispersing agent and a solvent are added into the reaction tank and soaked for 12 hours, and then stirring is conducted for 30-50 minutes at a speed of 600-800 r / min. According to the invention, the chlorosulfonated polyethylene, the chlorinated rubber and the styrene elastomer are mixed for modification, so that the sealing protection effect and the adhesive force are improved; and the ceramic whiskers, the carbon nanotubes, the ceramic powder and the ceramic whiskers effectively improve the corrosion resistance of the coating and improve the toughness, hardness and scratch resistance of the coating, and the aluminum paste effectively improves the weather resistance of the coating, so that the sealing protection coating with excellent comprehensive performance is formed.

Description

technical field [0001] The invention relates to the technical field of rubber coatings, in particular to a sealing and protective rubber coating and a preparation method thereof. Background technique [0002] Rubber coating is a type of coating with natural rubber derivatives or synthetic rubber as the main film-forming substance. It is sprayed on the surface of the object and is in a matte or semi-matte state. It feels very delicate and smooth, and has an elegant and solemn appearance. Natural rubber derivatives Mainly chlorinated rubber, cyclized rubber, etc. Synthetic rubber mainly includes styrene-butadiene, neoprene, polysulfide, nitrile and other rubber varieties, among which chlorinated rubber is more, especially neoprene is more important; [0003] However, at present, the weather resistance and adhesion of rubber coatings are average, and the hardness of the paint film is low. In the open-air corrosive environment, the performance of various aspects decreases rapidl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/34C09D115/02C09D153/02C09D7/61B01F7/18B01F7/32B01F11/00B01F15/00B01F15/02B01J4/00B01J19/18B08B9/087B01F27/96
CPCC09D123/34C09D115/02C09D153/025C09D7/61C09D7/70B01J19/18B01J4/00B08B9/087B01F2215/0495C08K2003/0806C08K2003/0812C08K2201/011C08L15/02C08L53/025C08K7/08C08K3/041C08K3/08C08K3/22C08K13/04C08L23/34
Inventor 钟继东王锡玲
Owner NANJING YUSONG MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap