Abdominal wall tissue repair patch and preparation method thereof

A tissue repair and abdominal wall technology, which is applied to the micro-nanofiber-hydrogel three-dimensional interpenetrating network abdominal wall tissue repair patch and its preparation, and the field of abdominal wall tissue repair patch and its preparation, which can solve the problem of insufficient fatigue resistance of hydrogel , unfavorable defect repair, easy tearing off of the hydrogel, etc., to achieve the effect of promoting adhesion infiltration and nutrient transmission, beneficial to tissue regeneration, and high mechanotransduction efficiency

Active Publication Date: 2021-08-13
DONGHUA UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the following problems still exist: 1. The mechanical compatibility is poor; 2. The degradation rate of decellularized tissue is often faster than the growth rate of human new abdominal wall tissue, which often leads to the failure of such patches
3. When the decellularized tissue is directly used for surgical repair, the material is too dense, and it is difficult for host cells and new tissues to grow into the material, which is not conducive to defect repair
Under the cutting action of sutures or fixation nails during implantation, the hydrogel is easy to tear off, resulting in failure
After implantation, the fatigue resistance of the hydrogel is also insufficient under the repeated stretching motion of the abdominal wall tissue
Moreover, as a scaffold material for abdominal wall tissue engineering, hydrogel itself has shortcomings in promoting tissue regeneration. Abdominal wall tissue has an oriented structure, while hydrogel is a disordered polymer network structure, which is not conducive to the oriented growth of cells, and eventually forms There are also structural differences between the tissue of the human body and the abdominal wall tissue of the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A method for preparing a micro-nano fiber-hydrogel three-dimensional interpenetrating network abdominal wall tissue repair patch, the specific steps are as follows:

[0045] (1) Use polyester as raw material, dissolve in dichloromethane, prepare a spinning solution with a mass concentration of 10%, and then perform electrospinning, and use a drum with a surface line speed of 5m / s as the electrospinning receiving device , performing electrospinning for a period of time to obtain an insulating layer with an oriented structure;

[0046] (2) Continue electrospinning with the same spinning solution and spinning process parameters as step (1) on the insulating layer, and add hydrogel precursor (gelatin powder) while receiving micro-nano fibers to obtain Composite layer; in the composite layer, the amount of hydrogel precursor added is 100wt% of the micro-nano fiber;

[0047] (3) Submerging the product obtained in step (2) in 0.1wt% 1-(3-dimethylaminopropyl)-3-ethylcarbodiimi...

Embodiment 2

[0050] A method for preparing a micro-nano fiber-hydrogel three-dimensional interpenetrating network abdominal wall tissue repair patch, the specific steps are as follows:

[0051] (1) Use polypropylene as a raw material, dissolve it in N-N dimethyl benzamide to obtain a spinning solution with a mass concentration of 15%, and then perform electrospinning, and use a drum with a surface line speed of 6m / s as the electrospinning A silk receiving device is used to perform electrospinning for a period of time to obtain an insulating layer with an oriented structure;

[0052] (2) Continue electrospinning with the same spinning solution and spinning process parameters as step (1) on the insulating layer, and add hydrogel precursor (chitosan powder) while receiving micro-nano fibers, A composite layer is prepared; in the composite layer, the addition amount of the hydrogel precursor is 200wt% of the micro-nano fiber;

[0053] (3) Submerge the product obtained in step (2) in a glutara...

Embodiment 3

[0056] A method for preparing a micro-nano fiber-hydrogel three-dimensional interpenetrating network abdominal wall tissue repair patch, the specific steps are as follows:

[0057] (1) Take polytetrafluoroethylene as raw material, dissolve in chloroform, and prepare a spinning solution with a mass concentration of 12.5%, then carry out electrospinning, and adopt a drum with a surface line speed of 7m / s as the electrospinning The receiving device performs electrospinning for a period of time to obtain an insulating layer with an oriented structure;

[0058] (2) Continue electrospinning with the same spinning solution and spinning process parameters as step (1) on the insulating layer, and add a hydrogel precursor (sodium alginate powder) while receiving micro-nano fibers, A composite layer is prepared; in the composite layer, the addition amount of the hydrogel precursor is 300wt% of the micro-nano fiber;

[0059] (3) Submerging the product obtained in step (2) in a calcium ch...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
tensile strength at breakaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an abdominal wall tissue repair patch and a preparation method thereof. The repair patch comprises a growth layer and an isolation layer, wherein the growth layer is a micro-nano fiber-hydrogel interpenetrating three-dimensional network composed of a micro-nano fiber three-dimensional network and hydrogel, and the isolation layer is a micro-nano fiber membrane; the average included angle between the axial direction of the micro-nano fibers in the growth layer and the isolation layer and the longitudinal direction of the repair patch is 5-30 degrees; the micro-nano fiber three-dimensional network is a self-locking three-dimensional network constructed by micro-nano fibers with high length-diameter ratio, and more than 99% of the fibers are in a monodisperse state; The method comprises the following steps: firstly, performing electrostatic spinning to prepare the isolation layer, and adding a hydrogel precursor to prepare a composite layer while receiving micro-nano fibers on the isolation layer; and expanding the hydrogel precursor to prepare the micro-nano fiber-hydrogel three-dimensional interpenetrating network abdominal wall tissue repair patch. The method is simple and controllable in process; and the patch has good mechanical strength, force conduction performance and tensile fatigue resistance, and cells can be induced to be aligned along the patch under force stimulation.

Description

technical field [0001] The invention belongs to the technical field of tissue engineering, and relates to an abdominal wall tissue repair patch and a preparation method thereof, in particular to a micro-nano fiber-hydrogel three-dimensional interpenetrating network abdominal wall tissue repair patch and a preparation method thereof. Background technique [0002] Abdominal wall defect is a clinically common disease. When the abdominal wall defect is large, it is usually necessary to use implant materials to suture the abdominal wall defect to reduce the tension of the abdominal wall and speed up the wound repair of the patient. The implant materials currently used for the repair of abdominal wall defects can be divided into the following two types: synthetic mesh and biological mesh. [0003] Synthetic patches mainly include microporous membrane patches and mesh patches. Among them, the mesh patch is one of the common artificial patches due to its light weight and excellent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/18A61L27/16A61L27/20A61L27/22A61L27/52D04H1/74D04H1/413
CPCA61L27/18A61L27/16A61L27/20A61L27/222A61L27/52D04H1/74D04H1/413A61L2400/12A61L2430/34
Inventor 王璐高立恒刘星星毛迎李超婧王富军李彦
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products