Fatty acid modified adsorption resin, preparation method and method for treating anionic surfactant wastewater by using fatty acid modified adsorption resin

A fatty acid modification and adsorption resin technology, which is applied in the fields of adsorption water/sewage treatment, water/sewage treatment, chemical instruments and methods, etc. The effect of desorption efficiency, reduction of desorption cost and improvement of adsorption efficiency

Active Publication Date: 2021-07-23
WANHUA CHEM GRP CO LTD
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of adsorption resins to treat wastewater containing anionic surfactants still has the problems of insufficient adsorption capacity and high consumption of desorption solution.
The above problems have restricted the application of the adsorption resin method in the treatment of washing, bleaching and dyeing wastewater containing anionic surfactants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] At room temperature, a premixed water phase was added, and the composition was 572.2 g of deionized water, 30.2 g of sodium chloride, 0.6 g of polyvinyl alcohol, and 0.6 mg of methylene blue. Add the premixed oil phase, and the composition is 30g of divinylbenzene, 25g of methyl methacrylate, 45g of oleic acid, 50g of toluene, 50g of 3# white oil, 0.5g of AIBN, and 0.5g of BPO. Start stirring, raise the temperature to 85° C., keep the temperature constant for 6 hours, wash with water, extract the porogen, and wash with water to obtain fatty acid-modified porous white balls.

[0049] Take 50.0 g of the fatty acid modified porous white balls and place them in 150 mL of calcium chloride solution (concentration: 1 mol / L), stir and soak at 60° C. for 4 hours, wash with water, and filter to obtain fatty acid modified adsorption resin. The calcium ion distribution density in the fatty acid modified adsorption resin is 10mmol / g, the particle size is 400-1200μm, and the specific...

Embodiment 2

[0055] At room temperature, add the premixed water phase, and the composition is 1507 g of deionized water, 3 g of gelatin, and 15 mg of methylene blue. Add the premixed oil phase, and the composition is 25g of trivinylbenzene, 15g of allyl itaconate, 60g of linoleic acid, 50g of xylene, 150g of 200# mineral spirits, 1g of ABVN, and 1g of TBCP. Start stirring, raise the temperature to 65°C, keep the temperature constant for 12 hours, wash with water, extract the porogen, and wash with water to obtain fatty acid-modified porous white balls.

[0056] Take 50.0 g of the fatty acid-modified porous white balls and place them in 250 mL of magnesium chloride solution (concentration: 5 mol / L), stir and soak at 80° C. for 2 h, wash with water, and filter to obtain the fatty acid-modified adsorption resin. The distribution density of magnesium ions in the fatty acid modified adsorption resin is 15mmol / g, the particle size is 300-1000μm, and the specific surface area is 200m 2 / g, the a...

Embodiment 3

[0060] At room temperature, the premixed water phase was added, and the composition was 270.7 g of deionized water, 30.1 g of sodium chloride, and 0.2 g of hydroxypropyl methylcellulose. Add the pre-mixed oil phase, the composition is 20g divinylbenzene, 25g trivinylbenzene, 10g methyl acrylate, 25g methyl methacrylate, 10g linolenic acid, 10g arachidonic acid, 10g ethylbenzene, cyclohexanol 20g, isooctyl alcohol 20g, LPO 0.5g. Start stirring, raise the temperature to 95° C., keep the temperature constant for 4 hours, wash with water, extract the porogen, and wash with water to obtain fatty acid-modified porous white balls.

[0061] Take the above 50.0g fatty acid modified porous white balls and place them in 150mL aluminum chloride and ferric chloride mixed solution (the concentration of aluminum chloride is 0.05mol / L, the concentration of ferric chloride is 0.05mol / L), stir and soak at 40°C for 6h, wash with water and filtering to obtain the fatty acid modified adsorption r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a fatty acid modified adsorption resin and a preparation method thereof. The preparation method comprises the following steps of 1) carrying out suspension copolymerization on an aromatic polyvinyl monomer, an acrylate monomer and an unsaturated fatty acid monomer to obtain a fatty acid modified porous white ball, and (2) immersing the fatty acid modified porous white balls obtained in the step (1) into cation exchange liquid to obtain the fatty acid modified adsorption resin. The resin provided by the invention is especially suitable for treating the adsorption and recovery of wastewater containing an anionic surfactant, the treated wastewater reaches the standard and is discharged, and a feasible solution is provided for the treatment of civil and industrial washing, bleaching and dyeing wastewater.

Description

technical field [0001] The invention belongs to the technical field of sewage treatment, specifically relates to a fatty acid modified adsorption resin and a preparation method thereof, and also relates to a method for using the resin to treat waste water, especially washing waste water containing anionic surfactants. Background technique [0002] Anionic surfactants are the products with the largest output and the most varieties among surfactants. Among them, the straight-chain sulfonic acid / sodium sulfate represented by sodium dodecylbenzenesulfonate and sodium dodecylsulfate is one of the most widely used washing and dyeing reagents in civil and industrial fields. Good sex, stable performance, low price and other advantages, its output accounts for more than 90% of the total output of synthetic detergents. At the same time, the above-mentioned substances are also an important harmful component in washing, bleaching and dyeing wastewater, and the direct discharge of a lar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/26B01J20/28B01J20/30B01J20/32C02F1/28C02F101/30
CPCB01J20/265B01J20/28019B01J20/28061B01J20/28064B01J20/28083B01J20/28073B01J20/28076B01J20/3085B01J20/3236C02F1/288C02F2101/301
Inventor 欧洋牛艳丽赵伟国孙家宽
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com