Production process of reinforced silver pot

A production process and technology of silver pots, applied in the field of metal pot processing, can solve the problems of increased consumption of raw materials, easy deformation of silver pot products, high quality of silver pots, etc., achieve high brightness and long-lasting maintenance, reduce material costs, and bright and durable Effect

Active Publication Date: 2021-07-16
程明阳
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the silver teapot production process in the prior art, there is a low hardness of the produced silver teapot, which causes the silver teapot product to be easily deformed and lacks durability. In addition, the silver teapot will change color due to oxidation reaction after being used for a period of time , so that the brightness is reduced. In addition, the quality of the silver pot in the existing production process is relatively large, which increases the consumption of raw materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of strengthened silver pot production process, comprises the following steps:

[0026] (1) Using silver ingots as raw materials, first cut the silver ingots into blocks of appropriate size, the weight of the cut silver ingot blocks is 1.2 times the weight of the silver pot to be made;

[0027] (2) Put the prepared silver block into the ceramic crucible, put the ceramic crucible together with the silver material to be melted into the muffle furnace for heating and melting, so that all the silver material is melted into a liquid state; the crucible requires pre-treatment to remove metal impurities , the crucible can melt about 2kg of silver material at one time, and is specially used for melting high-purity silver material; the temperature of the muffle furnace is controlled at 1000°C;

[0028] (3) injecting the liquid silver material in step (2) into a rectangular parallelepiped ceramic container free from metal element pollution, so that the liquid silver materia...

Embodiment 2

[0036] A kind of strengthened silver pot production process, comprises the following steps:

[0037] (1) Using silver ingots as raw materials, first cut the silver ingots into blocks of appropriate size, the weight of the cut silver ingot blocks is 1.2 times the weight of the silver pot to be made;

[0038] (2) Put the prepared silver block into the ceramic crucible, put the ceramic crucible together with the silver material to be melted into the muffle furnace for heating and melting, so that all the silver material is melted into a liquid state; the crucible requires pre-treatment to remove metal impurities , the crucible can melt about 2kg of silver material at one time, and is specially used for melting high-purity silver material; the temperature of the muffle furnace is controlled at 1100°C;

[0039] (3) injecting the liquid silver material in step (2) into a rectangular parallelepiped ceramic container free from metal element pollution, so that the liquid silver materia...

Embodiment 3

[0047] A kind of strengthened silver pot production process, comprises the following steps:

[0048] (1) Using silver ingots as raw materials, first cut the silver ingots into blocks of appropriate size, the weight of the cut silver ingot blocks is 1.2 times the weight of the silver pot to be made;

[0049] (2) Put the prepared silver block into the ceramic crucible, put the ceramic crucible together with the silver material to be melted into the muffle furnace for heating and melting, so that all the silver material is melted into a liquid state; the crucible requires pre-treatment to remove metal impurities , the crucible can melt about 2kg of silver material at one time, and is specially used for melting high-purity silver material; the temperature of the muffle furnace is controlled at 1050°C;

[0050] (3) injecting the liquid silver material in step (2) into a rectangular parallelepiped ceramic container free from metal element pollution, so that the liquid silver materia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a production process of a reinforced silver pot. According to the production process, silver and zinc on the surface of a semi-finished product permeate mutually to form an alloy layer, and generally, the hardness of alloy is higher than that of pure metal. High-temperature quenching treatment and cold beating treatment are adopted, so that atom arrangement in a metal lattice structure is stabilized before reaching a stable state, and metal is not prone to deformation. Thus, the hardness of the silver pot produced by using the production process is nearly doubled compared with that of a conventional silver pot, the product is not prone to deformation and has stronger durability, the Vickers hardness of common silver is 50-70, and the Vickers hardness of the silver pot produced by using the production process can reach 90-110.

Description

technical field [0001] The invention belongs to the technical field of metal pot processing, and relates to a production process for strengthening silver pots. Background technique [0002] Chinese silverware culture has a long history and a long history. As early as the Spring and Autumn Period and the Warring States Period, the ancients began to use silver to make utensils. Boiling water in a silver pot has many benefits: (1) Purify water quality, sterilize, and the mechanism of silver killing microorganisms is that silver can inactivate specific enzymes in pathogens, block the respiratory pathway of cells, and kill microorganisms. (2) Moisten the intestines and detoxify. Silver can absorb toxic substances such as lead in water and food, and has the effect of disinfection and detoxification. (3) Dehumidification beauty, the silver ions released in the water can enter the blood circulation system of the human body, speed up the blood migration speed, help to quickly disch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00C21D9/00C22F1/14C25D3/46C25D7/00
CPCB23P15/00C25D7/00C22F1/14C22F1/002C21D9/0068C25D3/46
Inventor 程明阳
Owner 程明阳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap