A kind of preparation method of polyacrylonitrile fiber

A polyacrylonitrile fiber and ionic liquid technology, applied in the direction of fiber chemical characteristics, rayon manufacturing, single-component synthetic polymer rayon, etc., can solve the problems of increased internal defects of fibers, complex process flow, and low production efficiency , to achieve the effects of low solvent residue, lower dissolution temperature, and lower energy consumption

Active Publication Date: 2022-03-18
SHANDONG RENFENG SPECIAL MATERIALS
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the fibers prepared by this patent have good bundle property and are not easy to scatter, the preparation method has complex process flow and low production efficiency, and the spinning stock solution is directly solidified after being extruded from the spinneret hole. With the increase of the traction speed, the spinning As the drafting ratio increases, broken filaments are likely to occur at the spinneret hole, and the internal defects of the fiber increase during the drying and densification process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of polyacrylonitrile fiber
  • A kind of preparation method of polyacrylonitrile fiber
  • A kind of preparation method of polyacrylonitrile fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 10

[0031] The main solvent (i.e. the benign solvent of polyacrylonitrile) is dimethylformamide, the secondary solvent is dichloromethane, and the ionic liquid is 1-ethyl-3-methylimidazolium tetrafluoroborate, according to the raw materials in the table Ratio, preparation method is identical with embodiment 1.

Embodiment 11

[0033] The main solvent (i.e. the benign solvent of polyacrylonitrile) is dimethylformamide, the secondary solvent is n-hexane, and the ionic liquid is 1-ethyl-3-methylimidazolium tetrafluoroborate, according to the raw material composition in Table 1 Ratio, preparation method is identical with embodiment 1.

Embodiment 12

[0035] Taking the main solvent (i.e. the benign solvent of polyacrylonitrile) as dimethyl sulfoxide, the secondary solvent as dichloromethane, and the ionic liquid as N-alkylpyridine chloroaluminate as an example, according to the ratio of raw materials in Table 1, prepare The method is the same as in Example 1.

[0036] The performance tests of the polyacrylonitrile fibers prepared in Examples and Comparative Examples are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

In the present invention, polyacrylonitrile is first swelled and dissolved in a certain proportion of ionic liquid and high boiling point (150-190°C) solvent under high temperature and high pressure conditions, and then added with volatile or low boiling point (30-60°C) solvent to obtain a homogeneous Spinning liquid, then spinning, drawing and opening to prepare polyacrylonitrile fiber, which has the technical effect of making the solvent less likely to be wrapped inside the fiber and improving fiber defects; the prepared fiber is denser and has a finer diameter.

Description

technical field [0001] The invention belongs to the technical field of fiber preparation, and relates to a method for preparing polyacrylonitrile fibers. Background technique [0002] Carbon fiber is a new material developed to meet the needs of cutting-edge industries such as aerospace, aviation, and atomic energy. It has high tensile strength, high tensile modulus, low density, high temperature resistance, ablation resistance, corrosion resistance, high Excellent properties such as electrical and thermal conductivity, low thermal expansion, self-lubrication and good biocompatibility. There are many precursors for preparing carbon fibers, such as polyacrylonitrile (PAN), viscose fiber, pitch polyacrylonitrile, polyethylene, lignin, polyimide, phenolic resin, polybenzothiazole, etc., as raw materials, but so far So far, only three kinds of polyacrylonitrile, viscose and asphalt have been produced on an industrial scale. Among them, the performance of pitch-based carbon fibe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/18D01F6/38D01F1/02
CPCD01F6/18D01F6/38D01F1/02
Inventor 何冬梅宋佃凤郁国强汤秀秀刘娜吴立群
Owner SHANDONG RENFENG SPECIAL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com