A preparation method of negative electrode slurry and negative electrode slurry

A negative electrode slurry and slurry technology, which is applied in the field of electrochemistry, can solve problems such as cleaning difficulties, and achieve the effects of shortening the total time, appropriate fineness, and good stability

Active Publication Date: 2022-04-08
HUBEI JINQUAN NEW MATERIALS CO LTD
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, in the slurry preparation system of large-scale equipment in the production line, during the automatic feeding process of glue, the glue will form accumulations on the pipe wall after long-term transportation through the pipeline, making cleaning difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of negative electrode slurry and negative electrode slurry
  • A preparation method of negative electrode slurry and negative electrode slurry

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] This embodiment provides a method for preparing negative electrode slurry, the method comprising the following steps:

[0071] S1: Add the negative electrode active material and conductive agent powder into the mixing equipment in proportion, and stir evenly. The stirring parameters are: revolution 20rpm, dispersion 1000rpm, stirring time 15min;

[0072] S2: Add an appropriate amount of deionized water, stir evenly, the stirring parameters are: revolution 20rpm, dispersion 650rpm, stirring time 35min, to obtain a wet slurry with a solid content of 70%;

[0073] S3: Add thickener powder accounting for 50% of the total mass of CMC powder, stir evenly, the stirring parameters are revolution 15rpm, dispersion 300rpm, stirring time 10min;

[0074] S4: Add thickener powder accounting for 20% of the total mass of CMC powder, and stir evenly. The stirring parameters are 15 rpm for revolution, 150 rpm for dispersion, and 5 min for stirring time;

[0075] S5: Add thickener powde...

Embodiment 2

[0082] S1: Add the negative electrode active material and conductive agent powder into the mixing equipment in proportion, and stir evenly. The stirring parameters are: revolution 30rpm, dispersion 1250rpm, stirring time 8min;

[0083] S2: Add an appropriate amount of deionized water, stir evenly, the stirring parameters are: revolution 25rpm, dispersion 500rpm, stirring time 40min, to obtain a wet slurry with a solid content of 65%;

[0084] S3: Add thickener powder accounting for 55% of the total mass of CMC powder, and stir evenly. The stirring parameters are revolution 25rpm, dispersion 800rpm, and stirring time 5min;

[0085] S4: Add thickener powder accounting for 20% of the total mass of CMC powder, and stir evenly. The stirring parameters are 20 rpm for revolution, 200 rpm for dispersion, and 20 min for stirring time;

[0086] S5: Add thickener powder accounting for 25% of the total mass of CMC powder, and stir evenly. The stirring parameters are revolution 20rpm, disp...

Embodiment 3

[0093] S1: Add the negative electrode active material and conductive agent powder into the mixing equipment in proportion, and stir evenly. The stirring parameters are: revolution 15rpm, dispersion 800rpm, stirring time 30min;

[0094] S2: Add an appropriate amount of deionized water, stir evenly, the stirring parameters are: revolution 20rpm, dispersion 400rpm, stirring time 60min, to obtain a wet slurry with a solid content of 60%;

[0095] S3: Add thickener powder accounting for 50% of the total mass of CMC powder, stir evenly, the stirring parameters are revolution 25rpm, dispersion 600rpm, stirring time 20min;

[0096] S4: Add thickener powder accounting for 30% of the total mass of CMC powder, and stir evenly. The stirring parameters are revolution 15rpm, dispersion 700rpm, and stirring time 10min;

[0097] S5: Add thickener powder accounting for 20% of the total mass of CMC powder, and stir evenly. The stirring parameters are revolution 25rpm, dispersion 450rpm, and sti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of negative electrode slurry and the negative electrode slurry. The method comprises the following steps: (1) mixing negative electrode active material, conductive agent powder and water to obtain a wet slurry; (2) adding thickener powder in three steps; (3) adding water and stirring to obtain a pre-prepared slurry. Set the slurry with solid content; (4) add the aqueous solution of the binder and stir to obtain the negative electrode slurry. The method of the present invention does not need to carry out the preparation process of the glue solution before the preparation of the negative electrode slurry, which can meet the preparation effect of the slurry, the slurry viscosity is suitable, the stability is good, the fineness is suitable, the filtration is smooth, and the slurry preparation system can be reduced at the same time. The equipment cost and floor space can greatly shorten the total time of slurry preparation and reduce labor costs.

Description

technical field [0001] The invention relates to the field of electrochemical technology, and relates to a preparation method of negative electrode slurry and the negative electrode slurry. Background technique [0002] For lithium-ion batteries, graphite is generally used as the negative electrode active material, and the current preparation process of lithium-ion battery negative electrode slurry is roughly divided into two types: (1) wet mixing process, the basic process is to prepare glue—add conductive agent to mix— Adding active substances and mixing—adding SBR and mixing, this is the mainstream process in China at present. (2) Dry mixing process, the basic process is to prepare the glue for later use—first mix the active material and conductive agent dry powder—add an appropriate amount of glue for wetting—add solvent to disperse and crush—dilute to adjust viscosity—add SBR for mixing. For example CN109638287A discloses a kind of preparation method of negative electro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/04H01M4/1393H01M4/133
CPCH01M4/04H01M4/1393H01M4/133Y02E60/10
Inventor 伍山松杜双龙卢涛吕正中刘金成
Owner HUBEI JINQUAN NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap