Reinforced concrete release agent and preparation method thereof

A concrete release agent, enhanced technology, applied in the petroleum industry, climate sustainability, sustainable waste treatment, etc., can solve the problems of affecting the appearance of concrete, concrete surface damage, air bubbles cannot be discharged, etc., to increase the resistance to rain erosion properties, eliminate air bubbles, and improve the apparent performance

Active Publication Date: 2021-04-27
KZJ NEW MATERIALS GROUP CO LTD +1
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the forming process of concrete, the air bubbles inside the concrete will adhere to the interface between the concrete and the formwork. Since the concrete / formwork interface is in an airtight environment, the air bubbles cannot be discharged. As the concrete solidifies, the air bubbles will form bubble marks on the concrete surface. A large number of bubble marks not only Affect the appearance of concrete, and also cause damage to the concrete surface and reduce the rebound strength;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reinforced concrete release agent and preparation method thereof
  • Reinforced concrete release agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The invention provides a kind of preparation method of reinforced concrete release agent, and its specific steps are as follows:

[0032] Step 1: First mix water, heat transfer oil and surfactant in a certain proportion, and stir in a mixer at a speed of 1000-3000r / min for 20-30min to obtain emulsified oil;

[0033] Step 2: Add emulsifier and co-emulsifier to the emulsified oil obtained in Step 1, and stir for 30-50 minutes under the condition of 800-2000r / min to obtain completely emulsified oil;

[0034] Step 3: Add a certain proportion of enhancer, lubricant, antirust agent, defoamer to the fully emulsified oil obtained in step 2, and stir for 10-20min under the condition of 800-2000r / min to obtain the decomposed oil without adjusting the pH value. molding agent;

[0035] Step 4: adding a certain amount of pH regulator to the release agent obtained in step 3, and adjusting the pH value of the release agent to between 6-7 to obtain a reinforced concrete release agent;...

Embodiment 1

[0043] In terms of parts by mass, the specific steps are as follows:

[0044] Add 25 parts of heat transfer oil, 60 parts of water, 2 parts of sorbitan monostearate, and 3 parts of polyoxyethylene sorbitan tristearate into the reaction kettle, and stir for 20 minutes at 2000 r / min. An emulsified oil is obtained.

[0045] Add 1 part of diethylbutyl succinate and 1 part of diethylbutyl glutarate into the reaction kettle and stir for 30 minutes under the condition of 1000 r / min to obtain completely emulsified oil.

[0046] Add 0.02 parts of activated calcium silicate hydrate, 1 part of water-soluble fatty acid amide, 1 part of synthetic ester, 1 part of fatty acid, 2 parts of alcohol amine, and 2 parts of polyether modified silicone oil into the reactor, and stir at 1000r / min 10min.

[0047] Add 1 part of 2-amino-2-methylpropanol into the reaction kettle, stir slowly, adjust the pH value of the release agent to 7, and configure it as a concrete release agent for aluminum formwo...

Embodiment 2

[0050] In terms of parts by mass, the specific steps are as follows:

[0051] Add 35 parts of heat transfer oil, 68 parts of water, 3 parts of sorbitan monostearate, and 5 parts of polyoxyethylene sorbitan tristearate into the reaction kettle, and stir for 25 minutes at 2000 r / min. An emulsified oil is obtained.

[0052] Add 1 part of diethylbutyl succinate and 2 parts of diethylbutyl glutarate into the reaction kettle and stir for 40 minutes under the condition of 1000r / min to obtain completely emulsified oil.

[0053] Add 0.05 parts of activated calcium silicate hydrate, 3 parts of water-soluble fatty acid amide, 1 part of fatty acid, 2 parts of sodium nitrite, and 5 parts of polyether modified silicone oil into the reaction kettle, and stir for 15 minutes at 1000 r / min.

[0054] Add 2 parts of 2-amino-2-methylpropanol into the reaction kettle, stir slowly, adjust the pH value of the release agent to 7, and configure it as a concrete release agent for aluminum formwork.

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of building admixtures, in particular to a reinforced concrete release agent and a preparation method thereof. The concrete release agent is prepared from completely emulsified oil and a reinforcing agent, the completely emulsified oil is prepared from heat conduction oil through emulsification under participation of an emulsifier, wherein the co-emulsifier comprises an emulsifier and a co-emulsifier; and the reinforcing agent is active calcium silicate hydrate. The invention provides the reinforced concrete mold release agent, which can improve the mold release strength of concrete and the adhesion of the mold release agent on a template, improve the rain wash resistance of the mold release agent, reduce the adhesion amount during mold release and eliminate bubbles on a concrete / template interface.

Description

technical field [0001] The invention relates to the technical field of building admixtures, in particular to a reinforced concrete release agent and a preparation method thereof. Background technique [0002] Concrete in engineering often needs to be formed with the help of formwork. Common formwork includes steel formwork, wood formwork, bamboo formwork and plastic formwork. Compared with the above formwork, aluminum alloy formwork has high specific strength, high specific stiffness, corrosion resistance, and easy Advantages such as disassembly have been more and more widely used in the construction industry. However, physical and chemical reactions will occur when the surface of the aluminum formwork is in direct contact with concrete, and problems such as peeling of the concrete surface and adhesion of the formwork to the cement slurry are prone to occur during demoulding. Therefore, the method of applying a release agent to the formwork is often used in engineering to a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10M177/00C10N40/36C10N30/18C10N30/12
CPCC10M169/048C10M177/00C10M2215/08C10M2229/04C10M2215/042C10M2209/104C10M2209/109C10M2209/108C10M2207/282C10M2207/283C10M2201/082C10M2207/126C10M2201/102Y02W30/91
Inventor 史艳娜柯余良方云辉郭元强关基灿
Owner KZJ NEW MATERIALS GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com