Carbon aerogel/metal organic framework composite material, preparation method and application thereof in gas storage

A metal-organic framework and metal-organic framework technology, applied in the field of polymer materials and gas storage, can solve the problems of no contribution and increase the storage density of ANG

Pending Publication Date: 2021-04-23
NEW MATERIAL INST OF SHANDONG ACADEMY OF SCI
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, since MOFs are powder adsorbents, they are filled in storage tanks, and there are many gaps between the particles. The density of natural gas in these gaps is actually the density of pure compressed natural gas under the pressure of the storage tank (3-6MPa). Storage density of ANG does not contribute

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon aerogel/metal organic framework composite material, preparation method and application thereof in gas storage
  • Carbon aerogel/metal organic framework composite material, preparation method and application thereof in gas storage
  • Carbon aerogel/metal organic framework composite material, preparation method and application thereof in gas storage

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] In another specific embodiment of the present invention, the preparation method of the above-mentioned carbon airgel / metal organic framework composite material is provided, including:

[0042] 1) Preparing the precursor of the airgel material, adding a chemical crosslinking agent to it to form a sol solution;

[0043] 2) adding the MOF material into the solvent to form a MOF suspension;

[0044] 3) Mix the sol solution prepared in step 1) with the MOF suspension prepared in 2), and prepare the airgel / metal organic framework through the following steps a) or b), and then carbonize it under a protective atmosphere to obtain .

[0045] a) Hydrothermal synthesis to form a hydrogel, after aging and solvent replacement, then perform supercritical drying;

[0046] b) Freeze-drying after freezing for a period of time.

[0047] In yet another specific embodiment of the present invention, in the step 1), the precursor includes resorcinol, formaldehyde, and natural polysaccharide...

Embodiment 1

[0065] Example 1 (Cu-MOF / konjac glucomannan-based carbon aerogel)

[0066] Ethylenediamine was dissolved in 100mL of ultrapure water, and the prepared 10%wt (relative to the mass fraction of ethylenediamine) HKUST-1 powder was dispersed in the above solution, and ultrasonically dispersed for 30min. Dissolve 1.5g of konjac glucomannan powder in the above mixed suspension solution, stir for 10min, bathe in water at 90°C for 1h, then transfer to a container, cool to 25°C, transfer to a freezer at minus 40°C for 24h, and then transfer to a freeze dryer Freeze-dry in medium for 1d until all moisture is removed, in N 2 Under protection, the composite material was heated up to 800°C at a rate of 5°C / min in a tube furnace, kept for 2 hours, then cooled and taken out to obtain Cu-MOF / konjac glucomannan-based carbon aerogel.

[0067] After nitrogen adsorption and desorption tests, the composite adsorbent exhibits microporous characteristics with a pore size of 1.2nm-1.8nm, and a pore v...

Embodiment 2

[0069] Embodiment 2 (ZIF-8 / gelatin-based carbon aerogel)

[0070] Dissolve 0.5g of gelatin in 100ml of water, stir for 1 hour, place at 60 degrees until completely dissolved, then add 0.7ml of 37-40wt% formaldehyde solution, stir at 50 degrees for 5 hours, then transfer to the refrigerator for overnight, prepare the next day Good 10% wt (relative to the mass fraction of gelatin) ZIF-8 powder was dispersed in the above solution, and the mixed solution was ultrasonically dispersed for 2 hours, cooled rapidly in liquid nitrogen, and freeze-dried. Then transfer to a freeze dryer and freeze dry for 2 days until all the water is removed. Under the protection of Ar, the composite material is heated to 900 degrees Celsius at a rate of 5 degrees Celsius / min in a tube furnace, and after being kept for 3 hours, it is cooled and taken out to obtain gelatin. Carbon based airgel / ZIF-8 derived carbon.

[0071] After nitrogen adsorption and desorption tests, the composite adsorbent exhibits ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Pore volumeaaaaaaaaaa
Apertureaaaaaaaaaa
Login to View More

Abstract

The invention provides a carbon aerogel / metal organic framework composite material, a preparation method and application thereof in gas storage, and belongs to the technical field of high polymer materials and gas storage. The composite material is composed of an MOFs material with good adsorption capacity and a carbon aerogel framework material, wherein the MOFs material is used as an object material to be directly assembled into an aerogel framework, a blocky composite adsorbent material without a binder is obtained after joint carbonization, and methane gas can be effectively adsorbed and stored, therefore, the carbon aerogel / metal organic framework composite material has good practical application value.

Description

technical field [0001] The invention belongs to the technical field of polymer materials and gas storage, and in particular relates to an airgel / metal organic framework composite material, a preparation method thereof and an application in gas storage. Background technique [0002] The information disclosed in this background section is only intended to increase the understanding of the general background of the present invention, and is not necessarily taken as an acknowledgment or any form of suggestion that the information constitutes the prior art already known to those skilled in the art. [0003] Metal-organic frameworks (MOFs) are a new type of porous material that has developed very rapidly in the past two decades. It has the characteristics of ultra-high specific surface area, adjustable pore size, and ultra-large porosity. Catalysis, photoelectric materials and other fields. At present, a considerable number of MOFs have been applied to gas adsorption, and exhibit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/22B01J20/28B01J20/30B01D53/02
CPCB01J20/226B01J20/28057B01J20/28047B01J20/28011B01D53/02Y02C20/20Y02C20/40
Inventor 张晶尚梦鸽伊希斌于诗摩张新恩沈晓冬
Owner NEW MATERIAL INST OF SHANDONG ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com