Fuel cell composite proton exchange membrane and preparation method thereof

A proton exchange membrane and fuel cell technology, applied in fuel cells, electrolytes, circuits, etc., can solve difficult problems, reduce the thickness of the proton exchange membrane, etc., achieve small film thickness, reduce hydrogen permeation current density, and excellent performance Effect

Active Publication Date: 2021-04-13
NANJING UNIV
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, how to effectively reduce the thickness of the proton exchange membrane while ensuring the excellent performance of the proton exchange membrane, so as to achieve the purpose of reducing costs, is extremely difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fuel cell composite proton exchange membrane and preparation method thereof
  • Fuel cell composite proton exchange membrane and preparation method thereof
  • Fuel cell composite proton exchange membrane and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] This embodiment prepares perfluorosulfonic acid resin / polytetrafluoroethylene / resveratrol (PFSA / PTFE / resveratrol) composite proton exchange membrane, and its preparation method comprises the following steps:

[0052] (1) Cut a piece of polytetrafluoroethylene (PTFE) film (PTFE) with a thickness of 10cm*10cm and a thickness of 7 μm with scissors, and fix it with a mold; take 500ml of ethanol solution in a crystallization dish with a diameter of 180mm, and slowly put the fixed PTFE into In the ethanol solution, let it stand and soak in a cool place for 24 hours; weigh 500mg of dopamine hydrochloride reagent and 788mg of trishydroxymethylaminomethane hydrochloride in a crystal dish with a diameter of 180mm, add 500ml of deionized water to prepare the solution, and add dropwise 1mol / L NaOH solution until the pH of the solution is 8.5; put the PTFE soaked for 24 hours into the dopamine buffer solution at a constant speed, keep it parallel to the horizontal plane, and place i...

Embodiment 2

[0059] This example prepares a perfluorosulfonic acid resin / polytetrafluoroethylene / quercetin (PFSA / PTFE / quercetin) composite proton exchange membrane, the preparation method of which is basically the same as in Example 1, except that step (1) 1mg of resveratrol in the drug was replaced by 1mg of quercetin.

Embodiment 3

[0061] This embodiment prepares perfluorosulfonic acid resin / polytetrafluoroethylene / resveratrol (PFSA / PTFE / resveratrol) composite proton exchange membrane, and its preparation method is basically the same as in Example 1, except that the step ( In 1), polytetrafluoroethylene is perpendicular to the horizontal plane in the dopamine buffer solution, and the included angle is 90°, and it is also perpendicular to the horizontal plane during the cleaning step.

[0062] The prepared proton exchange membrane is subjected to performance analysis, the results are as follows:

[0063] image 3 It is a scanning electron microscope image before and after modification of the polytetrafluoroethylene film in Example 1. It can be seen from Figure a) and c) that compared with before modification, the internal microporous structure of polytetrafluoroethylene after modification is orderly, indicating that polydopamine treatment can effectively optimize the internal microporous structure of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fuel cell composite proton exchange membrane and a preparation method thereof. PTFE is placed in a dopamine buffer solution for modification treatment, the coating conditions are accurately controlled by adjusting the angle of the membrane in the solution and the like, the hydrophilicity of the treated PTFE is remarkably improved, a high-boiling-point solvent can be directly used for casting the membrane, and the composite proton exchange membrane is prepared and obtained. The prepared fuel cell composite proton exchange membrane has the advantages of being low in thickness, long in service life and good in performance. The operation process has the characteristics of simplicity, safety, easiness in scale expansion and industrialization, and can be used for producing the proton exchange membrane of the fuel cell.

Description

technical field [0001] The invention relates to a membrane material and a preparation process thereof, in particular to a fuel cell proton exchange membrane and a preparation method thereof. Background technique [0002] Hydrogen energy is a renewable energy with great development potential. Hydrogen fuel cell, as one of the main applications of hydrogen energy, has attracted people's attention due to its high efficiency and environmental friendliness. However, the large-scale commercial application of proton exchange membrane fuel cells is still limited by its high cost, and the cost of proton exchange membranes needs to be solved urgently. [0003] Proton exchange membranes are usually made of perfluorosulfonic acid resins, the most representative of which is the Nafion resin developed by DuPont in the late 1960s. At present, in order to reduce costs, reducing the film thickness by reducing the amount of resin is the fastest and most effective method. However, it is extr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M8/1041H01M8/1023H01M8/1072H01M8/1086H01M8/1088C08J5/22C08L27/18
CPCH01M8/1041H01M8/1023H01M8/1072H01M8/1088H01M8/1093C08J5/2287H01M2300/0094C08J2327/18C08J2479/04Y02E60/50
Inventor 刘建国霍有修李佳芮志岩
Owner NANJING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com