Method for modifying polyaniline polymer

A technology of polyaniline and polymer, which is applied in the field of polyaniline polymer modification, and can solve problems such as the electrical conductivity not meeting the requirements

Pending Publication Date: 2021-04-02
SUZHOU INST OF TRADE & COMMERCE
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when it is used as a raw material for technical products, the conductivity cannot meet the requirements, so it is necessary to improve the conductivity of polyaniline

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for modifying polyaniline polymer
  • Method for modifying polyaniline polymer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Take a 25mL two-necked flask, add 300mg of C in sequence 60 and 3mL of fuming sulfuric acid, heated to 55°C, and reacted for 70h under nitrogen protection to obtain a suspension; after cooling to room temperature, add the suspension dropwise to absolute ethanol in an ice bath, and centrifuge After standing still, the intermediate product can be obtained; take a 50mL round bottom flask, add ultrapure water to the intermediate product for hydrolysis reaction, N 2 Heat to 85°C and react for 8 hours; use a sand core filter device to obtain a brown solid, and wash it repeatedly with ultrapure water for 3 times, and finally place it in a vacuum drying oven to obtain a fullerene derivative C 60 (OH) 12 .

[0022] 170mg of aniline was added to a two-necked flask, followed by 100mg of sodium dodecylsulfonate (as an emulsifier), 4mL of 2mol / L hydrochloric acid and 15mL of ultrapure water, and finally (0mg, 20mg, 100mg) of Fullerene Derivative C 60 (OH) 12 , stirred vigorousl...

Embodiment 2

[0029] 170mg of aniline was added to a two-necked flask, followed by 100mg of sodium dodecylsulfonate (as an emulsifier), 4mL of 2mol / L hydrochloric acid and 15mL of ultrapure water, and finally (0mg, 20mg, 100mg) of Fullerene C 60 , stirred vigorously for 2 h under ice-water bath conditions.

[0030] Dissolve 0.4g of ammonium persulfate in 15mL of ultrapure water, add dropwise into the reaction flask to control the temperature at 80-90°C and continue the reaction for 3h; finally add polylactic acid solution (a solution formed by dissolving 1.2g of polylactic acid solid in chloroform solvent) ), 90-95 ° C vigorously stirred and reacted for 3 hours, the reaction product was washed with ethanol and ultrapure water until the water phase was colorless, to remove remaining monomers and ammonium persulfate, etc.; use a rotary evaporator to extract the obtained oil The phase product was spin-dried to obtain the target product, which was placed in a vacuum drying oven for 12 hours to...

Embodiment 3

[0036] 170mg of aniline was added to a two-necked flask, followed by 100mg of sodium dodecylsulfonate (as an emulsifier), 4mL of 2mol / L hydrochloric acid and 15mL of ultrapure water, and finally (40mg, 60mg, 80mg) of Fullerene C 60 or fullerene derivative C 60 (OH) 12 , stirred vigorously for 2 h under ice-water bath conditions.

[0037] Dissolve 0.4g of ammonium persulfate in 15mL of ultrapure water, add dropwise into the reaction flask to control the temperature at 80-90°C and continue the reaction for 3h; finally add polylactic acid solution (a solution formed by dissolving 1.2g of polylactic acid solid in chloroform solvent) ), 90-95 ° C vigorously stirred and reacted for 3 hours, the reaction product was washed with ethanol and ultrapure water until the water phase was colorless, to remove remaining monomers and ammonium persulfate, etc.; use a rotary evaporator to extract the obtained oil The phase product was spin-dried to obtain the target product, which was placed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polyaniline polymer modification method, which comprises: S1, sequentially adding an emulsifier, hydrochloric acid and purified water to aniline, adding a fullerene derivative, and carrying out violent stirring for 2-3 h under an ice-water bath condition, with the mass ratio of aniline to C60 or the fullerene derivative being 14-18: 4-6; and S2, adding an initiator solution into the mixed solution obtained in the step S1, controlling the temperature to be 80-90 DEG C, continuously reacting for 3 hours, then adding a polylactic acid solution, violently stirring and reacting for 3-5 hours at the temperature of 90-95 DEG C, evaporating the solution to obtain a product, and finally drying to obtain a polyaniline modified product. By adding polylactic acid and fullerene C60 or a fullerene derivative into polyaniline, the conductivity of polyaniline can be enhanced.

Description

technical field [0001] The invention belongs to the technical field of polyaniline modification, and in particular relates to a method for modifying polyaniline polymers. Background technique [0002] Conductive polymers have shown potential application prospects in the fields of optoelectronics and biomedicine, and have been widely used in high-end smart fabrics in recent years. In conductive polymers, polyaniline monomer has been widely used because of its low price, simple synthesis process, high conductivity, stability in air and solution, unique doping phenomenon and good electrochemical reversibility. Applications. However, when it is used as a raw material for technical products, its conductivity cannot meet the requirements, so it is necessary to improve the conductivity of polyaniline. Contents of the invention [0003] The invention provides a method for modifying polyaniline polymers, which can improve the conductivity of polyaniline. [0004] To achieve the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G81/00C08K3/04
CPCC08G81/00C08K3/045C08K2201/001
Inventor 许磊张蓉曹天天杨雷
Owner SUZHOU INST OF TRADE & COMMERCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com