A kind of solvent glue for sebs-based plastic track bonding and preparation method thereof

A technology based on plastics and runways, applied in the direction of adhesives, adhesive types, rosin adhesives, etc., can solve the problems of low strength and slow bonding speed, and achieve high strength, fast bonding speed, and good bonding performance. Effect

Active Publication Date: 2022-01-28
江苏瑞弗橡塑材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above technical problems, the present invention provides a solvent glue for bonding SEBS-based plastic runways and a preparation method thereof, which can solve the problems of low strength and slow bonding speed in the bonding process of SEBS-based runways.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] A kind of preparation method of the solvent glue that is used for SEBS base plastic runway bonding, comprises the following steps:

[0039] Step 1: Weigh 10-30 parts of thermoplastic elastomer TPE, 10-40 parts of tackifying resin, 20-30 parts of mineral spirits, and 10-20 parts of ester solvent in parts by weight, and pour them into the reaction kettle in turn as the bottom Material, control the reaction temperature at 78°C-82°C by reflux to completely dissolve it.

[0040] Step 2: React 100 parts of hydroxyl-terminated polybutadiene, 10-30 parts of isocyanate molecules, and 0.1-1.0 parts of organotin catalyst under nitrogen protection at 60°C for 6 hours to control the relationship between hydroxyl-terminated polybutadiene and isocyanate molecules. The molar ratio is 1:2-1:3 to obtain isocyanate-terminated polybutadiene.

[0041] Step 3: Weigh 20-60 parts of isocyanate-terminated polybutadiene, add it into the mixed system dissolved in Step 1, stir evenly under nitrog...

specific Embodiment 1

[0044] A solvent glue used for SEBS-based plastic runway bonding is prepared by the following steps:

[0045] (1) Weigh 10 parts of SEBS, 20 parts of naphthenic oil 4006, 40 parts of terpene resin, and 20 parts of butyl acetate in parts by weight, and pour them into a heating stainless steel reaction kettle in turn as a base material, through Reflux to control the reaction temperature at 80°C to completely dissolve and form a dissolved mixed system.

[0046] (2) Weigh 100 parts of hydroxyl-terminated polybutadiene (M n =2000), 17.4 parts of toluene diisocyanate, 0.2 parts of stannous octoate were reacted for 6 hours at 60°C under nitrogen protection, and the molar ratio of hydroxyl-terminated polybutadiene to isocyanate molecules was controlled to be 1:2 to obtain isocyanate-terminated polybutylene Diene.

[0047] (3) Weigh 30 parts of isocyanate-terminated polybutadiene, add it into the above-mentioned dissolved mixing system, stir evenly under the protection of nitrogen, a...

specific Embodiment 2

[0050]A solvent glue used for SEBS-based plastic runway bonding is prepared by the following steps:

[0051] (1) Weigh 30 parts of SBS, 30 parts of mineral spirits, 10 parts of C5 petroleum resin, and 10 parts of butyl acetate in parts by weight, and pour them into a heating stainless steel reaction kettle in turn as a base material, controlled by reflux The reaction temperature is 80°C to make it dissolve completely to form a dissolved mixed system.

[0052] (2) Weigh 100 parts of hydroxyl-terminated polybutadiene (M n =2000), 22.2 parts of isophorone diisocyanate, 0.3 parts of stannous octoate were reacted for 6 hours at 60°C under nitrogen protection, and the molar ratio of hydroxyl-terminated polybutadiene to isocyanate molecules was controlled to be 1:2 to obtain isocyanate-blocked terminal polybutadiene.

[0053] (3) Weigh 50 parts of isocyanate-terminated polybutadiene, add it into the above-mentioned dissolved mixing system, stir evenly under the protection of nitrog...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
initial bond strengthaaaaaaaaaa
initial bond strengthaaaaaaaaaa
initial bond strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a solvent glue used for bonding SEBS-based plastic runways and a preparation method thereof. The solvent glue is mainly prepared from the following raw materials in parts by weight: 10-30 parts of thermoplastic elastomer TPE, 10-40 parts Tackifying resin, 20-30 parts mineral spirits, 10-20 parts ester solvent, 20-60 parts isocyanate-terminated polybutadiene. The isocyanate-terminated polybutadiene is obtained by reacting 100 parts of hydroxyl-terminated polybutadiene, 10-30 parts of isocyanate molecules, and 0.1-1.0 part of an organotin catalyst. The solvent adhesive relies on the thermoplastic elastomer TPE, tackifying resin and the runway to achieve rapid initial adhesion within 10 minutes after the solvent volatilizes, and later relies on isocyanate water vapor curing to improve the bonding strength. The solvent glue developed by the invention has the characteristics of fast initial adhesion, strong adhesion, stable properties after curing, and the like.

Description

technical field [0001] The invention relates to the field of chemical process solvent glue, in particular to a solvent glue used for bonding SEBS-based plastic runways and a preparation method thereof. Background technique [0002] With the country's vigorous advocacy of national sports, the demand for sports venues, especially plastic tracks, has increased year by year, and higher requirements have been put forward for the durability and construction methods of plastic tracks. The prefabricated SEBS-based plastic runway, as a new type of fully recyclable and environmentally friendly plastic runway, can replace the traditional on-site paved runway and has better stability. It has been popularized and applied in various sports venues. However, how to achieve stable side bonding between prefabricated plastic runways is a problem that the industry needs to solve urgently. [0003] At present, there is no mature solution for the side bonding between prefabricated plastic runway...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J153/02C09J145/00C09J193/04C09J115/00C09J157/02C09J11/08C09J11/00
CPCC09J115/00C09J145/00C09J11/08C09J11/00C08L2205/03C08L2207/04C08L53/025C08L15/00C08L53/02C08L57/02C08L93/04C08L45/00
Inventor 高文通韩冰陈韶郭晓明赵辉黄玉安曹潇周松乐罗彦余保寅张波张奕磊
Owner 江苏瑞弗橡塑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com