A kind of steel-bonded hard alloy and its preparation method and application

A technology of steel-bonded hard alloy and mass percentage content, which is applied in the field of steel-bonded hard alloy and its preparation, can solve the problems of performance change and easy cracking, and achieve good impact resistance, wear resistance, and mechanical properties The effect of high stability and excellent thermal stability

Active Publication Date: 2022-06-14
常熟市电力耐磨合金铸造有限公司
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The main technical problem to be solved by the present invention is to provide a steel-bonded hard alloy and its preparation method and application, which can solve the problems of the cast nails of the existing cast nail casting rollers after heat treatment, their performance changes, and cracks are prone to occur.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of steel-bonded hard alloy and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A steel-bonded cemented carbide, calculated by mass percentage, including each component with a mesh number of 60 to 100, specifically 35% titanium carbide, 40% reduced iron powder, 5% reduced molybdenum powder, and 3 reduced nickel powder. %, manganese powder 12%, chromium powder 2%, ferrovanadium powder 2%, ferroniobium powder 1%.

[0029] The preparation method is:

[0030] (1) Wet grinding: Weigh 150kg of titanium carbide, reduced iron powder, reduced molybdenum powder, reduced nickel powder, manganese powder, chromium powder, ferrovanadium powder and ferroniobium powder in a ball mill, and then add 120kg of anhydrous ethanol As a wet grinding agent, wet grinding in a ball mill for 20h;

[0031] (2) Press molding: discharge the wet grinding material from the ball mill, then dry the wet grinding agent, add a molding agent whose mass ratio is 1 / 5, and mix and stir evenly. The molding agent is nitrile rubber. Gasoline solution, in which the mass fraction of nitrile r...

Embodiment 2

[0034] A steel-bonded cemented carbide, calculated by mass percentage, including each component with a mesh number of 100 to 150, specifically titanium carbide 38%, reduced iron powder 42%, reduced molybdenum powder 5%, reduced nickel powder 1 % %, manganese powder 10%, chromium powder 1%, ferrovanadium powder 0%, ferroniobium powder 3%.

[0035] Its preparation method is:

[0036] (1) Wet grinding: Weigh 150kg of titanium carbide, reduced iron powder, reduced molybdenum powder, reduced nickel powder, manganese powder, chromium powder, ferrovanadium powder and ferroniobium powder in a ball mill, and then add 120kg of anhydrous ethanol As a wet grinding agent, wet grinding in a ball mill for 19 hours;

[0037] (2) Press molding: discharge the wet grinding material from the ball mill, then dry the wet grinding agent, add a molding agent whose mass ratio is 1 / 6, and mix and stir evenly. The molding agent is nitrile rubber. Gasoline solution, in which the mass fraction of nitril...

Embodiment 3

[0040] A steel-bonded cemented carbide, calculated by mass percentage, including each component with a mesh number of 150 to 200, specifically titanium carbide 40%, reduced iron powder 40%, reduced molybdenum powder 2%, reduced nickel powder 3% %, manganese powder 10%, chromium powder 1%, ferrovanadium powder 2%, ferroniobium powder 2%.

[0041] Its preparation method is:

[0042] (1) Wet grinding: Weigh 150kg of titanium carbide, reduced iron powder, reduced molybdenum powder, reduced nickel powder, manganese powder, chromium powder, ferrovanadium powder and ferroniobium powder in a ball mill, and then add 120kg of anhydrous ethanol As a wet grinding agent, wet grinding in a ball mill for 18h;

[0043] (2) Press molding: discharge the wet-milled material from the ball mill, then dry and remove the wet-grinding agent, add a molding agent with a mass ratio of 1 / 10, and mix and stir evenly. The molding agent is nitrile rubber. Gasoline solution, in which the mass fraction of n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a steel-bonded hard alloy and its preparation method and application. The steel-bonded hard alloy comprises the following components in mass percentage: 35-45% of titanium carbide, 40-50% of reduced iron powder, Reduced molybdenum powder 2-5%, reduced nickel powder 2-5%, manganese powder 10-15% and chromium powder 0-3%. The invention discloses a steel-bonded hard alloy and its preparation method and application, through the selection and proportioning design of the hard phase and the binding phase, as well as the proportioning design of the adhesive component, and through a reasonable preparation process, the prepared The obtained steel-bonded cemented carbide has good impact resistance and wear resistance, and also has excellent thermal stability. After water toughening treatment, there is no cracking phenomenon, and the stability of mechanical properties is high. It is suitable for casting roller sleeves of integrated roller presses. or roll-hide liners.

Description

technical field [0001] The invention relates to the technical field of alloy preparation, in particular to a steel-bonded cemented carbide and a preparation method and application thereof. Background technique [0002] The development of roller sleeves for roller presses has experienced surfacing rollers, centrifugal composite rollers, tungsten carbide stud rollers and cast nail rollers. At present, surfacing rolls, stud rolls and inlaid stud rolls are widely used on the market, but inlaid stud rolls are gradually replacing surfacing rolls and stud rolls. [0003] The inlaid casting nail roller adopts forging the parent body (roller sleeve) first, then carries out numerical control opening on the parent body, and then fixes the tungsten carbide cemented carbide in the hole through glue. When the sleeve is heated during use, the glue will vaporize, causing the cemented carbide nails to loosen or even fall off, reducing the service life. [0004] Chinese patent CN 207722863 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/58C22C38/44C22C38/48C22C38/46C22C30/00C22C32/00C22C33/02
CPCC22C38/58C22C38/44C22C38/48C22C38/46C22C30/00C22C32/0052C22C33/0292C22C33/0228B22F2998/10B22F2009/043B22F3/02B22F3/1007
Inventor 陈玉祥肖平安陈焕潘宇平
Owner 常熟市电力耐磨合金铸造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com