A kind of magnesium alloy building formwork semi-solid die casting and double fluorination joint manufacturing method

A construction formwork and manufacturing method technology, applied in the direction of metal material coating process, etc., can solve the problems that the gas in the formwork cavity cannot be discharged smoothly, affect the surface quality of concrete molding, and be easily corroded by the atmosphere and water environment. Construction quality and mold release effect, excellent scratch resistance and water repellency, preventing chemical reaction and physical adsorption effect

Active Publication Date: 2022-03-18
重庆建谊祥科技有限公司
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Extrusion technology is difficult to realize the overall manufacturing of magnesium alloy templates, and the welding process must be used to manufacture field usable templates. However, due to the characteristics of the magnesium alloy material itself, it is difficult to achieve reliable template manufacturing with the existing welding process
Using the traditional die-casting technology to die-cast the magnesium alloy template, it is easy to cause the problem that the gas in the mold cavity and the gas generated by the die-casting coating in the template cannot be discharged smoothly. These gases either dissolve in the magnesium alloy under high pressure, or form many high-pressure micro-pores to disperse. Distributed within the die-cast formwork
[0005] In addition, the magnesium alloy die-casting formwork is easily corroded by the atmosphere and water environment during storage and use, and the surface of the formwork is easily scratched and damaged by concrete during construction. The surface quality of concrete molding; and the existing surface treatment methods are difficult to effectively solve the problems existing on the surface of magnesium alloy building formwork

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of magnesium alloy building formwork semi-solid die casting and double fluorination joint manufacturing method
  • A kind of magnesium alloy building formwork semi-solid die casting and double fluorination joint manufacturing method
  • A kind of magnesium alloy building formwork semi-solid die casting and double fluorination joint manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0040]The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention. Apparently, the described embodiments are only some of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0041] A semi-solid die-casting and double fluorination combined manufacturing method of a magnesium alloy building formwork of the present invention comprises the following steps:

[0042] Step 1, using a semi-solid die-casting method to prepare a magnesium alloy building formwork;

[0043] Step 2, immersing the magnesium alloy building formwork prepared in step 1 into a double fluoride treatment liquid to perform double fluorination combined treatment to obtain a double fluo...

Embodiment 1

[0046] A semi-solid die-casting and double fluorination combined manufacturing method of a magnesium alloy building formwork, comprising the following steps:

[0047] S1: Preheat the upper mold, design the mold for the template, and complete it according to the mold processing process (sample-part digital model-compilation and stamping process-mold structure design-making model-machining-grinding assembly-test mode-final inspection) Mold opening and mold testing. Install the formwork mold on the die-casting machine, connect the formwork mold with the corresponding required peripheral equipment, spray water-soluble mold release agent on the mold, and preheat the formwork mold through the mold temperature machine if there is a mold temperature requirement.

[0048] S2: Preparation and heating, prepare magnesium alloy particles with a diameter of 3-5mm and a length of about 10mm, put them into the hopper through the automatic feeding system, and forcefully transport them into the...

Embodiment 2

[0055] A semi-solid die-casting and double fluorination combined manufacturing method of a magnesium alloy building formwork, comprising the following steps:

[0056] S1: Preheat the upper mold, design the mold for the template, and complete it according to the mold processing process (sample-part digital model-compilation and stamping process-mold structure design-making model-machining-grinding assembly-test mode-final inspection) Mold opening and mold testing. Install the formwork mold on the die-casting machine, connect the formwork mold with the corresponding required peripheral equipment, spray water-soluble mold release agent on the mold, and preheat the formwork mold through the mold temperature machine if there is a mold temperature requirement.

[0057] S2: Preparation and heating, prepare magnesium alloy particles with a diameter of 3-5mm and a length of about 10mm, put them into the hopper through the automatic feeding system, and forcefully transport them into the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
hardnessaaaaaaaaaa
impact resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a semi-solid die-casting and double fluorination joint manufacturing method of a magnesium alloy building formwork, comprising the following steps: step 1, preparing a magnesium alloy building formwork by using a semi-solid die-casting method; step 2, using the magnesium alloy building formwork prepared in step 1 Immerse in the double fluoride treatment solution to carry out double fluoride combined treatment to obtain a double fluoride combined treated magnesium alloy building formwork. The magnesium alloy formwork plate produced by the present invention is flat and free of defects, has high tensile strength, high elongation, high surface hardness, small friction coefficient, excellent scratch resistance and hydrophobicity, and can effectively reduce the risk of concrete aggregates. The friction damage and corrosion damage from the external erosive medium prevent the chemical reaction and physical adsorption caused by cement, and ensure the construction quality and demoulding effect of the building wall.

Description

technical field [0001] The invention belongs to the field of preparation of concrete engineering construction templates, in particular to a semi-solid die-casting and double fluorination combined manufacturing method of magnesium alloy building templates. Background technique [0002] Concrete form work is one of the leading types of work in building construction. Formwork is an important turnover material in the construction of concrete structures, and it is an important factor that determines the quality of concrete forming, the strength of formwork support, construction efficiency and cost. In recent years, in order to better promote the efficient development of my country's concrete construction industry, my country has established the development of new formwork application technology as one of the "10 new technologies in the construction industry", which is enough to show that the country attaches great importance to the innovation and development of the formwork indus...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D17/00C23C22/34
CPCB22D17/007C23C22/34C23C2222/20
Inventor 曹献龙赵贵川向和定
Owner 重庆建谊祥科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com