A kind of production method of acid-resistant pipeline steel

A production method and pipeline steel technology, applied in the field of metallurgy, can solve the problems of long production cycle, high cost, and large difference in online quenching, and achieve the effects of low production cost, short production cycle, and reduced hardening effect

Active Publication Date: 2022-03-01
HUNAN VALIN XIANGTAN IRON & STEEL CO LTD
View PDF15 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The method of controlled rolling is only suitable for the production of low-grade pipeline steel, and it is difficult to meet the requirements of high strength. The production method of TMCP is widely used, but the production under this process may have defects such as poor plate shape and uneven structure. Off-line quenching +Although the production method of tempering solves the above two shortcomings, the manufacturing cost is high, the production cycle is long, and it is not suitable for industrial production
[0004] Chinese patent CN108342655A discloses "a quenched and tempered acid-resistant pipeline steel and its manufacturing method".
[0005] Chinese patent CN110541109A announced "A seabed acid-resistant pipeline steel X60MOS and its production method", its chemical composition mass percentage is: C: 0.06%-0.08%, Mn: 1.40%-1.70%, and the carbon content is relatively high , directly affects the anti-HIC performance, and the mass fraction of Mn is also high, which is easy to form Mn segregation and banded structure, reducing the anti-HIC performance of the material
[0006] Chinese patent CN108893678A announced "A kind of acid-resistant pipeline steel and its rolling method". The chemical composition and mass percentage of the invention are C: 0.014%~0.024%, Mn: 0.60%~0.80%, and the mass fractions of carbon and manganese are both low , is only suitable for the production of low-grade acid-resistant pipeline steel, and it is difficult to meet the strength requirements of high-grade acid-resistant pipeline steel. At the same time, the production process of this invention is TMCP, which is quite different from the online quenching of the present invention, and the cooling effect and uniformity are not as good as the present invention. it is good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of production method of acid-resistant pipeline steel
  • A kind of production method of acid-resistant pipeline steel
  • A kind of production method of acid-resistant pipeline steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1: Production of 9.5mmX65MS tempered pipeline steel

[0020] Steel smelting chemical composition content C=0.04%, Si=0.20%, Mn=1.18%, P=0.009%, S=0.0001%, Alt=0.026%, Nb=0.042%, Ti=0.014%, Mo=0.08% , Ni=0.13%, Cu=0.17%, Pcm=0.14%, the balance is Fe and unavoidable impurities.

[0021] (1) Heating: Furnace temperature 1100~1260°C, gas flow rate 4250Nm3 / h~4450 Nm3 / h, air-fuel ratio 1.16, furnace pressure 4Pa, total time in the furnace 286min, heating speed 6min / cm, furnace core temperature 1228°C.

[0022] (2) Rough rolling: the intermediate billet is set to 65mm, and the cumulative reduction rate is 73.1%. Longitudinal rolling is adopted to expand the width. %, 24.3%, 28.9%, and the rolling temperature is controlled at 1100~980°C.

[0023] (3) Finish rolling: the starting rolling temperature is 960°C, the cumulative reduction rate is 85.4%, the single pass reduction rate is 15%~20%, the rolling speed is 4~6m / s, and the final rolling temperature is 820~860°C.

...

Embodiment 1

[0026] Example 1 The mechanical properties of 9.5mmX65MS tempered pipeline steel are shown in Table 1.

[0027] Table 1 Mechanical properties of 9.5mmX65MS tempered pipeline steel

[0028]

Embodiment 2

[0029] Example 2: Production of 25.4mmX65MS tempered pipeline steel

[0030] Steel smelting chemical composition content C=0.03%, Si=0.22%, Mn=1.16%, P=0.008%, S=0.0001%, Alt=0.024%, Nb=0.043%, Ti=0.016%, Mo=0.09% , Ni=0.13%, Cu=0.16%, Pcm=0.13%, the balance is Fe and unavoidable impurities.

[0031] (1) Heating: furnace temperature 1100~1260℃, gas flow 4250Nm3 / h~4500 Nm3 / h, air-fuel ratio 1.21, furnace pressure 3.5Pa, total time in the furnace 292min, heating speed 6.2min / cm, furnace core temperature 1216 ℃.

[0032] (2) Rough rolling: the intermediate billet is set to 80mm, and the cumulative reduction rate is 69.2%. Longitudinal rolling is adopted to expand the width. %, 23.6%, 26.8%, and the rolling temperature is controlled at 1100~980°C.

[0033] (3) Finish rolling: the starting rolling temperature is 920°C, the cumulative reduction rate is 68.25%, the single pass reduction rate is 13%~20%, the rolling speed is 3.5~5.5m / s, and the final rolling temperature is 810~850°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

A production method of acid-resistant pipeline steel, the chemical composition of the steel is C=0.02%-0.04%, Si=0.15%-0.35%, Mn=1.10%-1.25%, P≤0.010%, S≤ 0.0015%, Alt=0.020%~0.045%, Nb=0.015%~0.045%, Ti=0.010%~0.020%, Mo=0.08%~0.15%, Ni=0.08%~0.15%, Cu=0.08%~0.20% , B≤0.0005%, Pcm=0.12%~0.14%, the balance is Fe and inevitable impurities. Using online quenching + tempering process, the production thickness is 8~26.4mmX65MS, the steel plate has high strength and super low temperature toughness, yield strength 480~530MPa, tensile strength 570~630MPa, elongation A 50 =35%~55%, yield ratio≤0.88, impact at ‑60℃=300~400J, drop weight at ‑40℃ is 85%~100%.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and relates to an on-line quenching + off-line tempering pipeline steel and a production method thereof. Background technique [0002] With the development of economy and the advancement of science and technology, the safety of pipes used in oil and gas transportation projects has been paid more and more attention. h 2 S is one of the harmful media in oil and gas transportation. The H atoms generated during the transportation process continuously penetrate into the steel, which is easy to corrode the pipeline and lead to hydrogen-induced cracking (HIC) of the pipeline, which can easily lead to pipeline safety accidents. Therefore, pipeline steel with HIC and SSCC resistance is more and more popular. At present, the oil and gas produced internationally are all degassed and directly transported through oil and gas pipelines. [0003] Acid-resistant pipeline steel for oil and gas engineering i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/14C22C38/16C21D8/02C22C33/04
CPCC22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C22C38/08C22C38/16C22C38/002C22C33/04C21D8/0205C21D8/0226C21D8/0263C21D2211/001C21D2211/005
Inventor 杜江李中平张勇伟张成元彭宁琦史术华
Owner HUNAN VALIN XIANGTAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com