Hole sealing method for micro-arc oxidation film layer

A micro-arc oxidation and film layer technology, applied in anodizing, coating, surface reaction electrolytic coating, etc., can solve the problems of unfavorable magnesium alloy matrix isolation, gas accompanying material injection, etc., and achieve good effect and hydrophilicity, Improve corrosion resistance and slow down corrosion

Active Publication Date: 2020-12-11
GUANGDONG MECHANICAL & ELECTRICAL COLLEGE
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the general micro-arc oxidation process will be accompanied by severe high temperature, and there will be a situation where the generated gas is accompanied by material injection, which will eventually cause an inherent microporous structure on the surface of the micro-arc oxidation film (specifically, the porosity from the inside to the outside From small to large), it is not conducive to maintaining the isolation of the magnesium alloy matrix from the external corrosive environment for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hole sealing method for micro-arc oxidation film layer
  • Hole sealing method for micro-arc oxidation film layer
  • Hole sealing method for micro-arc oxidation film layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A method for sealing pores of a micro-arc oxidation film layer, comprising the following steps:

[0040] 1) Put the magnesium / magnesium alloy with the micro-arc oxidation film layer into ultrapure water for 20 seconds, take it out, blow it dry with cold wind, put it into 75% alcohol and ultrasonically clean it for 8 minutes, and then take it out;

[0041] 2) mixing polycaprolactone (number average molecular weight 20000g / mol) and tetrahydrofuran according to a mass ratio of 1:3.5, stirring to fully dissolve polycaprolactone to obtain a polycaprolactone solution;

[0042] 3) immerse the magnesium / magnesium alloy with the micro-arc oxidation film layer treated in step 1) in the polycaprolactone solution, and ultrasonically treat it for 30s;

[0043] 4) Take out the magnesium / magnesium alloy with the micro-arc oxidation film layer treated in step 3), place it in an airtight container, evacuate until the pressure in the airtight container is 0.02MPa, and treat for 5 minutes...

Embodiment 2

[0048] A method for sealing pores of a micro-arc oxidation film layer, comprising the following steps:

[0049] 1) Put the magnesium / magnesium alloy with the micro-arc oxidation film layer into ultrapure water for 15 seconds, take it out, dry it with cold wind, put it into 75% alcohol for 10 minutes and take it out;

[0050] 2) mixing polycaprolactone (number average molecular weight 20000g / mol) and tetrahydrofuran according to a mass ratio of 1:9.5, stirring to fully dissolve the polycaprolactone to obtain a polycaprolactone solution;

[0051] 3) immerse the magnesium / magnesium alloy with the micro-arc oxidation film layer treated in step 1) in the polycaprolactone solution, and ultrasonically treat it for 15s;

[0052] 4) Take out the magnesium / magnesium alloy with the micro-arc oxidation film layer treated in step 3), place it in an airtight container, evacuate until the pressure in the airtight container is 0.04MPa, and treat for 8 minutes;

[0053] 5) Repeat steps 3) and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
boiling pointaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hole sealing method for a micro-arc oxidation film layer. The hole sealing method for the micro-arc oxidation film layer comprises the following steps of 1) cleaning and drying magnesium / magnesium alloy with the micro-arc oxidation film layer; 2) preparing a polycaprolactone solution; 3) dipping the magnesium / magnesium alloy with the micro-arc oxidation film layer in thepolycaprolactone solution; 4) performing vacuum drying on the dipped magnesium / magnesium alloy with the micro-arc oxidation film layer; 5) repeating the steps 3) and 4) for multiple times; and 6) putting the magnesium / magnesium alloy with the micro-arc oxidation film layer treated in the step 5) into a closed container, heating until the temperature in the closed container exceeds a melting pointof polycaprolactone, pressurizing and holding, cooling to the room temperature, and reducing the pressure. According to the hole sealing method for the micro-arc oxidation film layer provided by the invention, the micro-arc oxidation film layer is subjected to hole sealing through a dipping-dip coating-curing method, so that the macroscopic surface of the material can be smooth, and hole sealing is firm; and then micropores are sealed through heating, pressurizing, cooling and pressure reducing operation, so that the corrosion resistance of the magnesium / magnesium alloy is greatly improved onthe basis of the micro-arc oxidation film layer.

Description

technical field [0001] The invention relates to a hole sealing method for a micro-arc oxidation film layer, and belongs to the technical field of micro-arc oxidation film layer sealing. Background technique [0002] As a bone implant material, magnesium / magnesium alloy has many advantages such as biodegradability, good biocompatibility, high specific strength and specific stiffness, and has a good development prospect. Generally, it takes 4 to 8 weeks for bone tissue to heal due to disease conditions and individual differences, and magnesium / magnesium alloy implants need to provide sufficient mechanical support and good biocompatibility during this period. Therefore, in the early stage of implantation, the degradation rate of magnesium / magnesium alloys should be kept slow enough to ensure the stability of mechanical properties. In the later stages of bone tissue healing, magnesium / magnesium alloys should be degraded as soon as possible under the premise of meeting the biocom...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D11/30A61L27/04A61L27/34A61L27/56A61L27/58A61L27/50
CPCA61L27/047A61L27/34A61L27/50A61L27/56A61L27/58A61L2420/02A61L2420/08C25D11/026C25D11/30C08L67/04
Inventor 刘志聃黎花单志胡晓岳戴护民
Owner GUANGDONG MECHANICAL & ELECTRICAL COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com