Asphalt modifier and preparation process thereof

An asphalt modifier and preparation technology, which is applied to building components, building insulation materials, buildings, etc., can solve the problems of poor dispersion of modifiers, no dust and easy cleaning, and insignificant improvement of asphalt anti-aging performance, to achieve improved Stability, improve compatibility, improve anti-oxidative aging effect

Active Publication Date: 2020-09-01
CHINA ROAD & BRIDGE
View PDF13 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In order to speed up the construction process of traffic roads, the previous concrete road technology was gradually eliminated by asphalt pavement technology. Asphalt pavement is the most widely used high-grade road surface in road construction at present. It has the advantages of short construction period, easy maintenance and maintenance, no dust and easy cleaning At the same time, the existing asphalt pavement still has many shortcomings such as poor temperature stability, brittleness at low temperature, easy flow at high temperature, and poor aging resistance. In order to ensure the comfort and safety of traffic driving and reduce traffic noise, it is necessary to mix the Modifiers are added to the material to achieve the purpose of improving the temperature resistance and aging resistance of asphalt
[0003] Currently commonly used asphalt modifiers have the following defects: (1) poor adhesion with asphalt, prone to segregation; (2) poor dispersibility of each component of the modifier, resulting in low effective material utilization; (3) The anti-aging performance of asphalt is not significantly improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Asphalt modifier and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The invention provides an asphalt modifier, comprising the following raw materials in parts by weight: 20 parts of graphene, 10 parts of carbon nanotubes, 4 parts of dopamine, 15 parts of vegetable oil polyols, 30 parts of polytetrafluoroethylene fiber and 1 part stabilizer.

[0028] Wherein, the stabilizer is sulfur.

[0029] The graphene has been pretreated, specifically:

[0030] S1, disperse the graphene in the ethanol solution, control the mass concentration of the graphene to 0.3 mg / mL, and obtain a colloidal solution after ultrasonic treatment for 2 hours;

[0031] S2, add surfactant in colloidal solution, stir colloidal solution under the stirring velocity of 1000r / min and carry out foaming 40min, obtain foam suspension, wherein the weight ratio of the add-on of surfactant and graphene in colloidal solution is 0.03 :1;

[0032] S3. Freeze-drying and pulverizing the foam suspension to obtain pretreated graphene.

[0033] The surfactant in step S2 is sodium do...

Embodiment 2

[0040] The invention provides an asphalt modifier, comprising the following raw materials in parts by weight: 30 parts of graphene, 15 parts of carbon nanotubes, 8 parts of dopamine, 25 parts of vegetable oil polyols, 40 parts of polytetrafluoroethylene fiber and 3 parts stabilizer.

[0041] Wherein, the stabilizer is sulfur.

[0042] The graphene has been pretreated, specifically:

[0043] S1, disperse graphene in ethanol solution, control the mass concentration of graphene to be 0.7mg / mL, after ultrasonic treatment for 2.5h, obtain colloidal solution;

[0044]S2, add surfactant in colloidal solution, stir colloidal solution under the stirring speed of 1500r / min and carry out foaming 60min, obtain foam suspension, wherein the weight ratio of the add-on of surfactant and graphene in colloidal solution is 0.1 :1;

[0045] S3. Freeze-drying and pulverizing the foam suspension to obtain pretreated graphene.

[0046] The surfactant in step S2 is sodium dodecylsulfonate.

[00...

Embodiment 3

[0053] The invention provides an asphalt modifier, comprising the following raw materials in parts by weight: 25 parts of graphene, 13 parts of carbon nanotubes, 6 parts of dopamine, 20 parts of vegetable oil polyols, and 35 parts of polytetrafluoroethylene fiber and 2 parts stabilizer.

[0054] Wherein, the stabilizer is sulfur.

[0055] The graphene has been pretreated, specifically:

[0056] S1, disperse the graphene in the ethanol solution, control the mass concentration of the graphene to 0.5 mg / mL, and obtain a colloidal solution after ultrasonic treatment for 2.3 hours;

[0057] S2, add surfactant in colloidal solution, stir colloidal solution under the stirring speed of 1300r / min and carry out foaming 50min, obtain foam suspension, wherein the weight ratio of the add-on of surfactant and graphene in colloidal solution is 0.07 :1;

[0058] S3. Freeze-drying and pulverizing the foam suspension to obtain pretreated graphene.

[0059] The surfactant in step S2 is sodiu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses an asphalt modifier. The asphalt modifier comprises, by weight, 20-30 parts of graphene, 10-15 parts of carbon nanotubes, 4-8 parts of dopamine, 15-25 parts of vegetable oil polyol, 30-40 parts of polytetrafluoroethylene fibers and 1-3 parts of a stabilizer. The asphalt modifier has good compatibility with asphalt, the adhesion with asphalt is improved, and the segregationphenomenon is avoided; the vegetable oil polyol is used as a solvent, so that the dispersity of other components can be improved, and the utilization rate of effective substances is increased; and dopamine and graphene which have an obvious effect of improving the oxidation and aging resistance of the asphalt are added, so that the aim of improving the durability of the asphalt is fulfilled.

Description

technical field [0001] The invention relates to the field of asphalt technology, more specifically, the invention relates to an asphalt modifier and a preparation process thereof. Background technique [0002] In order to speed up the construction process of traffic roads, the previous concrete road technology was gradually eliminated by asphalt pavement technology. Asphalt pavement is the most widely used high-grade road surface in road construction at present. It has the advantages of short construction period, easy maintenance and maintenance, no dust and easy cleaning At the same time, the existing asphalt pavement still has many shortcomings such as poor temperature stability, brittleness at low temperature, easy flow at high temperature, and poor aging resistance. In order to ensure the comfort and safety of traffic driving and reduce traffic noise, it is necessary to mix the Modifiers are added to the material to achieve the purpose of improving the temperature resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L27/18C08L91/00C08K13/06C08K9/04C08K3/04C08K3/06D06M10/02
CPCC08L95/00D06M10/025C08L2205/16C08L2205/03C08L2205/08C08K2201/011C08L27/18C08L91/00C08K13/06C08K9/04C08K3/042C08K3/041C08K3/06
Inventor 王随原曾峰蔡文浩程昊
Owner CHINA ROAD & BRIDGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com