A kind of graphite negative electrode material, lithium ion battery and its preparation method and application

A graphite anode and raw material technology, applied in battery electrodes, secondary batteries, circuits, etc., can solve the problems of low charging capacity and poor low-temperature performance, and achieve the effects of high battery capacity, improved low-temperature electrical performance, and simple process

Active Publication Date: 2021-11-26
NINGBO SHANSHAN NEW MATERIAL TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to overcome the low charging capacity and poor low-temperature performance of the lithium-ion battery graphite negative electrode material in the prior art, and provide a graphite negative electrode material, lithium-ion battery and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphite negative electrode material, lithium ion battery and its preparation method and application
  • A kind of graphite negative electrode material, lithium ion battery and its preparation method and application
  • A kind of graphite negative electrode material, lithium ion battery and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] In the crushing equipment, the calcined needle coke is crushed to obtain powder, the median particle size of the powder is controlled at 8-8.5 μm, the crushed material is shaped, and the shaped powder is mixed evenly . Under the protection of chlorine gas, the mixed powder was subjected to graphitization treatment. The graphitization temperature is 2900°C, and the graphitization time is 90h. The material after graphitization treatment is screened, and the mesh number of the screen is 250 mesh, to remove the lumps that coke quickly at high temperature during the graphitization process. Fully mix the sieved material with the binder asphalt according to the ratio of 100:3, and mix for 45 minutes, so that the asphalt is evenly distributed in the sieved material to prepare a mixture. The mixture was subjected to surface coating modification treatment, including two stages. The temperature of the first stage was 350°C and the time was 3h; the temperature of the second stage...

Embodiment 2

[0058] In the crushing equipment, the calcined needle coke is crushed to obtain powder, the median particle size of the powder is controlled at 8-8.5 μm, the crushed material is shaped, and the shaped powder is mixed evenly . Under the protection of chlorine gas, the mixed powder was subjected to graphitization treatment. The graphitization temperature is 2900°C, and the graphitization time is 90h. The material after graphitization treatment is screened, and the mesh number of the screen is 250 mesh, to remove the lumps that coke quickly at high temperature during the graphitization process. Fully mix the sieved material with the binder asphalt according to the ratio of 100:4, and mix for 45 minutes, so that the asphalt is evenly distributed in the sieved material to prepare a mixture. The mixture was subjected to surface coating modification treatment, including two stages. The temperature of the first stage was 350°C and the time was 3h; the temperature of the second stage...

Embodiment 3

[0061] In the crushing equipment, the calcined needle coke is crushed to obtain powder, the median particle size of the powder is controlled at 8-8.5 μm, the crushed material is shaped, and the shaped powder is mixed evenly . Under the protection of chlorine gas, the mixed powder was subjected to graphitization treatment. The graphitization temperature is 2900°C, and the graphitization time is 90h. The material after graphitization treatment is screened, and the mesh number of the screen is 250 mesh, to remove the lumps that coke quickly at high temperature during the graphitization process. Fully mix the sieved material with the binder asphalt according to the ratio of 100:5, and mix for 45 minutes, so that the asphalt is evenly distributed in the sieved material to prepare a mixture. The mixture was subjected to surface coating modification treatment, including two stages. The temperature of the first stage was 350°C and the time was 3h; the temperature of the second stage...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a graphite negative electrode material, a lithium ion battery, a preparation method and an application. The preparation method of the material comprises the following steps: ① pulverizing and shaping the artificial graphite raw material to obtain powder; ② graphitizing the powder to obtain material A; ③ sieving material A to obtain material B; ④ surface coating and modifying the mixture of material B and binder to obtain material C; ⑤ subjecting material C to carbonization treatment. The graphite negative electrode material of the present invention has high tap density, relatively high battery capacity, and the interaction of various features improves the comprehensive advantages of the material, ensures high capacity and high compaction characteristics, and improves the high rate performance of the material; it is beneficial to improve The lithium-ion battery graphite negative electrode material has low-temperature electrical properties, simple process, low production cost, and is suitable for industrial production.

Description

technical field [0001] The invention relates to a graphite negative electrode material, a lithium ion battery, a preparation method and an application. Background technique [0002] With its advantages of high specific energy, high working voltage, fast charging and discharging, long cycle life, safety and pollution-free, lithium-ion batteries have successfully replaced other secondary batteries and become the main energy source in the 3C market, and have greatly promoted the development of electric vehicles. The industrialization process of automobile EV and HEV, with our country's strong support in the field of new energy, a series of related subsidy policies are advancing; [0003] At present, the first obstacle facing the large-scale industrialization of pure electric vehicles is the problem of "mileage anxiety". For pure electric vehicles, the cruising range is determined by the energy density of the power battery system, so the energy density of the power system has b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/587H01M10/0525
CPCH01M4/366H01M4/587H01M10/0525Y02E60/10
Inventor 顾凯丁晓阳李虹王旭峰杜飞兰珊张淼
Owner NINGBO SHANSHAN NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com