Magnetostrictive material and preparation method thereof

A technology of magnetostrictive materials and raw materials, which is applied in the direction of material selection and device material selection for magnetostrictive devices, and achieves the effects of easy process control, good magnetostrictive performance and comprehensive usability, and simple operation.

Inactive Publication Date: 2020-06-09
XIHUA UNIV
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for a non-oriented polycrystalline bulk material, the change in linearity is about 1 / 3 of the change in volume, and only about 667ppm of magnetostriction can be produced during the magnetization process, which is much smaller than that of rare earth giant magnetostrictive materials. Magnetostrictive value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnetostrictive material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A preparation method of the above-mentioned magnetostrictive material, comprising the following steps:

[0033] a. Weigh the raw materials according to the stoichiometric ratio Mn:Ni:Co:Si:Y:Eu=0.9:0.1:1:1:1:0.35, mix evenly, pour the prepared raw materials into a beaker, add distilled water to wash the raw materials, Pour off the distilled water;

[0034] b. Pour the raw materials into the copper crucible of the arc melting furnace. Put the elemental Zr into the copper crucible, number them sequentially, and close the furnace chamber. The electric arc furnace is cooled by a circulating water cooling system. Before smelting, use a mechanical pump to evacuate to below 9Pa, and then use a molecular pump to continue evacuating to 5×10 -5 Pa, turn off the molecular pump, fill with argon to 0.6 atmosphere. Start the vacuum arc melting furnace, first align the tungsten electrode with Zr, press the start button to start the arc, and then increase the current to 250A, and sta...

Embodiment 2

[0039] A preparation method of the above-mentioned magnetostrictive material, comprising the following steps:

[0040] a. Weigh the raw materials according to the stoichiometric ratio Mn:Ni:Co:Si:Y:Tm=0.92:0.08:1:1:1:0.22, mix evenly, pour the prepared raw materials into a beaker, add distilled water to wash the raw materials, Pour off the distilled water;

[0041] b. Pour the raw materials into the copper crucible of the arc melting furnace. Put the elemental Zr into the copper crucible, number them sequentially, and close the furnace chamber. The electric arc furnace is cooled by a circulating water cooling system. Before smelting, use a mechanical pump to evacuate to below 9Pa, and then use a molecular pump to continue evacuating to 5×10 -5 Pa, turn off the molecular pump, fill with argon to 0.6 atmosphere. Start the vacuum arc melting furnace, first align the tungsten electrode with Zr, press the start button to start the arc, and then increase the current to 250A, and...

Embodiment 3

[0046] A preparation method of the above-mentioned magnetostrictive material, comprising the following steps:

[0047] a. Weigh the raw materials according to the stoichiometric ratio Mn:Ni:Co:Si:Y:Ho=0.95:0.05:1:1:1:0.55, mix evenly, pour the prepared raw materials into a beaker, add distilled water to wash the raw materials, Pour off the distilled water;

[0048] b. Pour the raw materials into the copper crucible of the arc melting furnace. Put the elemental Zr into the copper crucible, number them sequentially, and close the furnace chamber. The electric arc furnace is cooled by a circulating water cooling system. Before smelting, use a mechanical pump to evacuate to below 9Pa, and then use a molecular pump to continue evacuating to 5×10 -5 Pa, turn off the molecular pump, fill with argon to 0.6 atmosphere. Start the vacuum arc melting furnace, first align the tungsten electrode with Zr, press the start button to start the arc, and then increase the current to 250A, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a magnetostrictive material and a preparation method thereof, which belongs to the technical field of new materials. The molecular formula of the magnetostrictive material is Mn<1-x>Ni<x>CoSiYM<y>, wherein the value range of x is 0.05 to 0.10, the value range of y is 0 to 0.85, and M is selected from one or more of Nd, Tm, Ho, Eu, Ta. The MnCoSi-based alloy prepared by thepreparation method disclosed by invention has a room temperature saturation magnetostriction of 1900 ppm, and the critical field can be reduced to a minimum of 0.3T; and compared with the positive MnCoSi alloy, the magnetostriction value is increased by 500 ppm, and the critical field is reduced by 2.3T, which promotes the application process of the MnCoSi material in magnetostriction.

Description

technical field [0001] The invention relates to the technical field of new materials, in particular to a magnetostrictive material and a preparation method thereof. Background technique [0002] As an important class of ferromagnetic functional materials, magnetostrictive materials will reversibly change their geometric dimensions in all directions with changes in the magnetization state. This reversible deformation induced by a magnetic field is called magnetostriction. Since Joule proposed the magnetostrictive effect in 1842, magnetostrictive materials have been widely used in aviation, navigation, robotics, new energy, biomedicine and many other fields, playing an important role in the national economy and industrial production. [0003] Famous magnetostrictive material, rare earth-transition alloy Tb 0.3 Dy 0.7 Fe 2 (Terfenol-D), under a 1T magnetic field, obtained a large magnetostriction of 1600ppm in the direction of the easy axis. However, such materials have pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C30/00C22C1/02H01L41/20
CPCC22C30/00C22C1/02H10N35/85
Inventor 周廷栋
Owner XIHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com