A kind of slag system for smelting GH3625 nickel-based alloy containing rare earth CE and its electroslag remelting smelting method

A nickel-based alloy and slag-based technology, applied in the field of metallurgy, can solve the problems of Ce element burning loss, achieve the effects of good composition quality, solve the burning loss of easily oxidized elements, and evenly distribute the elements

Active Publication Date: 2021-10-22
上海一郎合金材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the GH3625 alloy containing rare earth Ce has certain problems in smelting, that is, the burning loss of Ce element and other easily oxidizable elements in the alloy after the secondary refining of electroslag remelting, so it is necessary to develop a new electroslag remelting process to solve this problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of slag system for smelting GH3625 nickel-based alloy containing rare earth CE and its electroslag remelting smelting method
  • A kind of slag system for smelting GH3625 nickel-based alloy containing rare earth CE and its electroslag remelting smelting method
  • A kind of slag system for smelting GH3625 nickel-based alloy containing rare earth CE and its electroslag remelting smelting method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] In the present embodiment, the crystallizer diameter is 150mm, and the chemical composition of the slag system used is configured according to the following mass percentages: CaF 2 : 38%, CaO: 24%; Al 2 o 3 : 20%; NaF: 6%; MgO: 4%; TiO 2 : 2%; CeO 2 : 5%; SiO 2 :1%.

[0038] During the smelting process using the above-mentioned slag system, smelting is carried out according to the smelting method of the present invention. During the smelting process, aluminum particles are added into the slag pool, and the addition amount is 1 g per kilogram of alloy.

[0039] At the same time, another group of notoginseng slag is smelted, and the chemical composition of notoginseng slag is configured according to the following mass percentage: CaF 2 : 70%; Al 2 o 3 : 30%.

[0040] In the smelting process using notoginseng slag, no aluminum particles are added.

[0041] After smelting, the ingots were detected by ICP and nitrogen and oxygen analyzers, and the chemical analysis ...

Embodiment 2

[0046] In the present embodiment, the crystallizer diameter is 260mm, and the chemical composition of the slag system used is configured according to the following mass percentages: CaF 2 : 38%, CaO: 24%; Al 2 o 3 : 20%; NaF: 6%; MgO: 4%; TiO 2: 2%; CeO 2 : 5%; SiO 2 :1%.

[0047] In this example, three GH3625 alloys with different Ce contents were used for electroslag remelting.

[0048] During the smelting process using the above-mentioned slag system, smelting is carried out according to the smelting method of the present invention. During the smelting process, aluminum particles are added into the slag pool, and the addition amount is 1 g per kilogram of alloy.

[0049] The composition of the cast ingot after smelting was detected by ICP and nitrogen and oxygen analyzer, and the chemical analysis results are shown in Table 2.

[0050] Table 2 GH3625 alloy components content

[0051]

[0052] The smelting results show that the slag system and smelting method of th...

Embodiment 3

[0054] In this embodiment, the diameter of the crystallizer is 260 mm, and the chemical components of the three slag systems used are configured according to the following mass percentages: S1: CaF 2 : 42%, CaO: 24%; Al 2 o 3 : 20%; NaF: 7%; MgO: 4%; TiO 2 : 2%; SiO 2 : 1%; S2: CaF 2 : 39%, CaO: 24%; Al 2 o 3 : 20%; NaF: 7%; MgO: 4%; TiO 2 : 2%; CeO 2 : 3%; SiO 2 : 1%; S3: CaF 2 : 36%, CaO: 24%; Al 2 o 3 : 20%; NaF: 7%; MgO: 4%; TiO 2 : 2%; CeO 2 : 6%; SiO 2 :1%.

[0055] In this embodiment, the GH3625 alloy with the same composition is used for electroslag remelting.

[0056] During the smelting process using the above-mentioned slag system, smelting is carried out according to the smelting method of the present invention. During the smelting process, aluminum particles are added into the slag pool, and the addition amount is 1 g per kilogram of alloy.

[0057] After smelting, the ingots were detected by ICP and nitrogen and oxygen analyzers, and the chemical ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a slag system for smelting GH3625 nickel-based alloy containing rare earth Ce and its electroslag remelting smelting method. The composition of the slag system includes 20-25% of CaO and 17-21% of Al by weight percentage 2 o 3 , 5-7% NaF, 3-5% MgO, 1-2% TiO 2 , 4-6% CeO 2 , 1~2% SiO 2 , the balance is CaF 2 . The slag system is suitable for electroslag remelting of GH3625 alloy containing rare earth, and can well solve the problem of Ce, Al and Ti burning loss in the process of electroslag remelting of GH3625 alloy containing Ce.

Description

technical field [0001] The invention relates to the technical field of metallurgy, in particular to a slag system for smelting a GH3625 nickel-based alloy containing rare earth Ce and an electroslag remelting smelting method thereof. Background technique [0002] Nickel-based alloy GH3625 is a solid-solution-strengthened nickel-based deformed superalloy. It was originally developed internationally as a boiler steam pipe material for high-strength supercritical thermal power units. However, due to its excellent mechanical properties, machinability, The combination of corrosion resistance, stability and weldability makes it one of the most successful nickel-based superalloys for long-term engineering applications. [0003] The current smelting process for producing GH3625 alloy is vacuum induction melting (VIM) + vacuum arc melting (VAR). However, VAR has almost no ability to remove impurity elements, and it is easy to bring into the crucible material during smelting, causing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B9/18C22C1/03C22C19/05
CPCC22B9/18C22C1/023C22C1/03C22C19/058
Inventor 付华清司周祥刘小佩徐晓平姜周华董艳伍李毓硕董君伟
Owner 上海一郎合金材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com