Molybdenum disulfide-based nano composite material with hollow sandwich laminated structure and preparation method thereof

A technology of nanocomposite materials and laminated structures, applied in chemical instruments and methods, chemical/physical processes, physical/chemical process catalysts, etc., can solve problems such as insufficient active sites, easy aggregation of sheets, and limited improvement. Achieve the effects of improving electrochemical performance, increasing specific surface area, and improving conductivity

Active Publication Date: 2020-05-08
XI AN JIAOTONG UNIV
View PDF13 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But MoS 2 The sheets are easy to agglomerate, resulting in insufficient exposed active sites, and electrons in MoS 2 The transition efficiency between nanosheet layers is low; secondly, bulk MoS 2 The poor conductivity of the material and the low electron transfer efficiency seriously restrict the application in the field of electrochemistry.
[0003] CN201710397526.1 discloses the preparation method of carbon composite material, this method will MoS 2 It is made into a hollow structure and the outer layer is covered with a carbon layer. Although it can improve conductivity and reduce agglomeration to a certain extent, the degree of improvement is limited, and it still cannot overcome the constraints and limitations of its application in the field of electrochemistry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Molybdenum disulfide-based nano composite material with hollow sandwich laminated structure and preparation method thereof
  • Molybdenum disulfide-based nano composite material with hollow sandwich laminated structure and preparation method thereof
  • Molybdenum disulfide-based nano composite material with hollow sandwich laminated structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] The invention provides a hollow sandwich structure MoS 2 A method for preparing a base nanocomposite, the method comprising the following steps:

[0039] Step 1, prepare SiO 2 Microsphere powder, as a growth template for subsequent material preparation;

[0040] Step 2, the appropriate amount of SiO 2The microsphere powder and a certain mass of PDA are dissolved in an appropriate amount of Tris buffer solution, mixed and ultrasonically dispersed to obtain a mixed solution A;

[0041] Step 3, transfer the mixed solution A to a magnetic stirrer, add a certain amount of ammonium persulfate solution, and continue stirring for a certain period of time;

[0042] Step 4, collect the product of step 3, and carry out annealing treatment, obtain black powder sample A, set aside;

[0043] Step 5, take an appropriate amount of sample A and mix molybdate and thiourea powder in a certain amount of glucose solution, and ultrasonically stir until it is in a uniform state to obtain ...

Embodiment 1

[0067] Take 1g of SiO 2 The nano-microsphere material was dissolved in 50 mL of Tris buffer solution with a concentration of 50 mmol / L and 200 mg of dopamine hydrochloride, and ultrasonicated for 25 min until the solution was uniformly dispersed. The obtained homogeneously mixed solution was transferred to a magnetic stirrer, and 10 mL of ammonium persulfate solution with a concentration of 65 mg / mL was added dropwise while stirring, and the stirring was continued for 12 h. Then it was collected by centrifugation at 8000r / min, washed four times with ultrapure aqueous solution and twice with ethanol solution, and the centrifugation time was 5 minutes each time. Finally, put the precipitate collected by washing into a vacuum oven and keep it at 60°C for vacuum drying for 10 hours. Under an argon atmosphere, it was annealed at 550°C for 3 hours. After cooling, a black powdery sample A was obtained for future use. Get 55mg sample A and 80mg (NH 4 ) 2 Mo 2 o 7 , 160mg thiourea...

Embodiment 2

[0069] Take 1.5g of SiO 2For the nanosphere material, dissolve it and 250mg of dopamine hydrochloride in 45mL, 40mmol / L Tris buffer solution, and sonicate for 25min until the solution is uniformly dispersed. The obtained homogeneous mixed solution was transferred to a magnetic stirrer, and 18 mL of ammonium persulfate solution with a concentration of 70 mg / mL was added dropwise while stirring, and the stirring was continued for 12 h. Then it was collected by centrifugation at 8000r / min, washed four times with ultrapure aqueous solution and twice with ethanol solution, and the centrifugation time was 5 minutes each time. Finally, put the precipitate collected by washing into a vacuum oven and keep it at 60°C for vacuum drying for 10 hours. Under an argon atmosphere, it was annealed at 550°C for 3 hours. After cooling, a black powdery sample A was obtained for future use. Get 60mg sample A and 100mg (NH 4 ) 2 Mo 2 o 7 , 20mgNi(CHCOO) 2 4H 2 0, 200mg thiourea, it is dissol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of preparation of two-dimensional MoS2-based nano composite materials, and relates to a molybdenum disulfide-based nano composite material with a hollow sandwich laminated structure and a preparation method of the molybdenum disulfide-based nano composite material, and the molybdenum disulfide-based nano composite material is of a hollow structure and sequentially comprises a carbon layer, a MoS2 layer and a carbon layer from inside to outside. SiO2 microspheres are adopted as a temboard, the carbon layer, the MoS2 layer and the carbon layer sequentially coat the temboard, and then the MoS2-based nano composite material with the hollow sandwich laminated structure is prepared after SiO2 is etched. The obtained product has a unique hollow sandwich laminated structure, so that more active sites can be exposed, the conductivity is improved, agglomeration is reduced, and the electro-catalytic performance of the material is improved. Therefore, the preparation of the composite material provides possibility for potential application of the composite material in various fields.

Description

technical field [0001] The present invention belongs to two-dimensional MoS 2 The technical field of nano-composite material preparation relates to a hollow sandwich structure MoS 2 Nanocomposite materials and methods for their preparation. Background technique [0002] MoS 2 It is a two-dimensional layered nanomaterial with a graphene-like structure, which is a typical representative of the transition metal chalcogenide family. The atoms in the layers are bonded by covalent bonds, and the layers interact by van der Waals forces. It has many advantages in the fields of energy, sensing, etc. For example, it is easier to modify the electrode surface, has hydrogen adsorption free energy similar to metal platinum, can exist stably in strong acidic solutions, and is rich in resources. But MoS 2 The sheets are easy to agglomerate, resulting in insufficient exposed active sites, and electrons in MoS 2 The transition efficiency between nanosheet layers is low; secondly, bulk M...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/24B01J27/051
CPCB01J27/24B01J27/0515B01J35/33
Inventor 马飞罗巧梅王琛
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com