Phosphorus-containing flame retardant nylon and its preparation method and application

A technology of flame retardant nylon and flame retardant is applied in the field of phosphorus-containing flame retardant nylon and its preparation, and achieves the effects of excellent application prospects, little impact on mechanical properties, and lasting flame retardant effect.

Active Publication Date: 2022-07-12
JIANGSU HAIYANG CHEM FIBERS
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to overcome the problems of large amount of flame retardants used in the prior art, melt dripping and poor spinnability of flame retardant polymers, the present invention provides a phosphorus-containing flame retardant nylon, its preparation method and application, that is, in nylon polymerization The introduction of macromolecular phosphine-containing components in the process can maximize the compatibility of the system, reduce the problems that are prone to occur in blending modification, and especially significantly improve the flame retardancy and spinnability of nylon, and this method Simple process and easy mass production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphorus-containing flame retardant nylon and its preparation method and application
  • Phosphorus-containing flame retardant nylon and its preparation method and application
  • Phosphorus-containing flame retardant nylon and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] Example 1: Flame Retardant Nylon I

[0069] 1880g of solid caprolactam was taken, melted at 130°C, 120g of polyphosphonate (Nofia OL1001 from FRX Polymer Company) was added, and after it was fully dissolved, the material was put into a 5L autoclave, and 60g of deionized water was added. Replace the air in the kettle with nitrogen, turn on stirring, heat up to 250 °C, keep the pressure in the kettle at 0.5 MPa, open the ring for 3 hours, and then release the pressure and pass nitrogen for 5 hours. , finally vacuumed for 0.5h, left to discharge, cast tape, cut into pellets, extracted with deionized water at 90°C for 12h, and vacuum dried at 80°C for 12h to obtain flame retardant nylon 6 slices.

Embodiment 2

[0070] Example 2: Flame Retardant Nylon II

[0071] 1840g of solid caprolactam was taken, melted at 130°C, 160g of polyphosphonate (Nofia OL1001 from FRX Polymer Company) was added, and after it was fully dissolved, the material was put into a 5L autoclave, and 60g of deionized water was added. Replace the air in the kettle with nitrogen, turn on stirring, heat up to 250 °C, keep the pressure in the kettle at 0.5 MPa, open the ring for 3 hours, and then release the pressure and pass nitrogen for 5 hours. , finally vacuumed for 0.5h, left to discharge, cast tape, cut into pellets, extracted with deionized water at 90°C for 12h, and vacuum dried at 80°C for 12h to obtain flame retardant nylon 6 slices.

Embodiment 3

[0072] Example 3: Flame Retardant Nylon III

[0073] 1800g of solid caprolactam was taken, melted at 130°C, 200g of polyphosphonate (Nofia OL1001 from FRX Polymer Company) was added, and after it was fully dissolved, the material was put into a 5L autoclave, and 60g of deionized water was added. Replace the air in the kettle with nitrogen, turn on stirring, heat up to 250 °C, keep the pressure in the kettle at 0.5 MPa, open the ring for 3 hours, and then release the pressure and pass nitrogen for 5 hours. , finally vacuumed for 0.5h, left to discharge, cast tape, cut into pellets, extracted with deionized water at 90°C for 12h, and vacuum dried at 80°C for 12h to obtain flame retardant nylon 6 slices.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
melting pointaaaaaaaaaa
limiting oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention provides a phosphorus-containing flame-retardant nylon, a preparation method and application thereof, namely, a macromolecular phosphine-containing component is introduced into the nylon polymerization process to maximize the compatibility of the system and reduce the blending modification. It can significantly improve the flame retardancy and spinnability of nylon, and this method is simple in process, easy to produce on a large scale, and more suitable for applications in the field of spinning-fiber, wire and cable, and 3D printing.

Description

technical field [0001] The invention relates to a phosphorus-containing flame-retardant nylon and a preparation method and application thereof, in particular to a phosphorus-containing flame-retardant and anti-dripping nylon material which can be prepared by a polymerization method. Background technique [0002] Polyamide (PA, commonly known as nylon) has good comprehensive properties and is an important raw material for synthetic fibers. When used as fibers, it has the advantages of good wear resistance, high resilience, high breaking strength, and good dyeability. However, when polyamide is used in synthetic fibers, it has poor heat resistance and may be flammable in harsh environments, which limits its application in many fields. Therefore, the flame-retardant modification and anti-drip modification of nylon are particularly important. . [0003] In the field of engineering plastics, flame retardant modification of nylon is mainly carried out by twin-screw melt blending ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G69/42C08G69/16C08L77/02C08L85/02D01F6/80D01F6/90D01F1/07B33Y70/00
CPCC08G69/42C08G69/16C08L77/02D01F6/80D01F6/90D01F1/07B33Y70/00C08L2201/02C08L85/02
Inventor 林云志周波谢丰鸣
Owner JIANGSU HAIYANG CHEM FIBERS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap