A sintered aluminum electrolytic capacitor ultra-high voltage anode foil and preparation method thereof

A technology of aluminum electrolytic capacitors and anode foils, applied in electrolytic capacitors, capacitors, circuits, etc., can solve the problems of difficulty in increasing the surface area of ​​corroded foils, achieve high capacity, reduce burden, and improve working life

Active Publication Date: 2022-03-01
XI AN JIAOTONG UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problem that the increase of the expansion ratio of aluminum foil by traditional corrosion process is close to the limit, and it is very difficult to increase the surface area of ​​the corrosion foil, the present invention uses additive manufacturing technology to propose a sintered aluminum electrolytic capacitor ultra-high voltage anode foil and its Preparation method, which is a more environmentally friendly (does not require acid-base corrosion) method for increasing the surface area of ​​the anode foil

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A sintered aluminum electrolytic capacitor ultra-high voltage anode foil and preparation method thereof
  • A sintered aluminum electrolytic capacitor ultra-high voltage anode foil and preparation method thereof
  • A sintered aluminum electrolytic capacitor ultra-high voltage anode foil and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] A method for preparing an ultra-high voltage anode foil of a sintered aluminum electrolytic capacitor of the present invention comprises the following steps:

[0045] 1) Mix spherical high-purity aluminum powder with a particle size of 0.5-20 μm with solvent and binder to prepare aluminum powder slurry.

[0046] The preparation of aluminum powder slurry requires the use of one or more of water, glycerol, ethylene glycol, terpineol, ketones, and castor oil as solvents, and the use of carboxycellulose, sodium alginate, starch, and vinyl polymers , epoxy resin, carbon nanotubes, graphene, silicone resin, organic fluoropolymer or fluorine resin as a binder;

[0047] 2) The coating method of aluminum powder slurry can be roller coating, spray coating or screen printing. Finally, carry out vacuum drying at 50-150°C to remove the organic or inorganic solvent components in the slurry;

[0048] Under the formation voltage of ultra-high voltage, the grown oxide film is very thick...

Embodiment 1

[0063] 1) The spherical high-purity aluminum powder with a particle size of 0.5 μm is mixed with a solvent and a binder to make an aluminum powder slurry.

[0064] The preparation of aluminum powder slurry requires the use of water as a solvent and carboxycellulose as a binder;

[0065] 2) The coating method of aluminum powder slurry can be roller coating, spray coating or screen printing. The thickness of one side of the coating is 20 μm, and the thickness of the aluminum foil substrate is selected to be 10 μm. After coating, vacuum drying is carried out at 50 ° C. Treatment to remove the organic or inorganic solvent components in the slurry;

[0066] 3) the aluminum foil coated in the previous step according to figure 1 The program set in the sintering process, such as figure 1 shown in;

[0067] First at HT 1 During the process, the aluminum foil is raised from room temperature to 300°C at a rate of 1°C / min. At this time, the temperature is T1, and 1h of HT is carried o...

Embodiment 2

[0078] A method for preparing an ultra-high voltage anode foil of a sintered aluminum electrolytic capacitor of the present invention comprises the following steps:

[0079] 1) The spherical high-purity aluminum powder with a particle size of 5 μm is mixed with a solvent and a binder to make an aluminum powder slurry.

[0080] To prepare aluminum powder slurry, glycerin and ethylene glycol are used as solvents, and carboxycellulose and sodium alginate are used as binders;

[0081] 2) The coating method of aluminum powder slurry can be roller coating, spray coating or screen printing, etc. The thickness of one side of the coating is 40 μm, and the thickness of the aluminum foil substrate is selected to be 15 μm, and vacuum drying is carried out at 80 ° C after coating Treatment to remove the organic or inorganic solvent components in the slurry;

[0082] 3) the aluminum foil coated in the previous step according to figure 1 The program set in the sintering process, such as f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultra-high voltage anode foil for a sintered aluminum electrolytic capacitor and a preparation method thereof, comprising: 1) mixing spherical aluminum powder with a solvent and a binder to prepare an aluminum powder slurry; 2) selecting an aluminum foil base material, and Coating the surface of the anode foil with aluminum powder slurry; vacuum drying after coating; 3) sintering the coated and dried aluminum foil; The sintered aluminum electrolytic capacitor anode foil is obtained after the last anodizing process. In the present invention, high-purity aluminum powder, solvent and binder are made into aluminum powder slurry, and then the slurry is evenly coated on the surface of the aluminum foil base, and sintered under certain conditions, so that the gap between the aluminum powder and the aluminum powder, the aluminum powder It is sintered with the aluminum foil substrate to form a three-dimensional porous aluminum foil. The method has simple process, is environmentally friendly, saves raw materials, and avoids the generation of a large amount of acid and alkaline waste liquid containing metal ions produced by the traditional corrosion process.

Description

technical field [0001] The invention belongs to the field of aluminum electrolytic capacitors, and in particular relates to an ultra-high voltage anode foil of a sintered aluminum electrolytic capacitor and a preparation method thereof. Background technique [0002] Aluminum electrolytic capacitors are widely used in household appliances, automotive electronics, industrial control, aerospace and military due to their high capacity per unit volume, strong breakdown resistance, "self-healing" characteristics during work, and low price In the field, it is often used in the circuit for filtering, coupling, bypass timing and energy storage. The capacity of an aluminum electrolytic capacitor is determined by the capacity of the anode foil. In the current traditional process, in order to increase the capacity of the anode foil, it is necessary to perform electrochemical corrosion and chemical conversion treatment on the aluminum foil. [0003] With the continuous development of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G9/045H01G9/052
CPCH01G9/045H01G9/052H01G9/0525
Inventor 徐友龙杨时伦姚向华
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com