Moisture-curable polyurethane hot melt adhesive as well as preparation method and application thereof

A polyurethane hot-melt adhesive and moisture-curing technology, which is applied in the direction of polyurea/polyurethane adhesives, adhesives, adhesive types, etc., can solve the problem of poor compatibility of polyurethane, difficult to uniform and stable systems, and inability to adapt to textiles. Industry development needs and other issues

Active Publication Date: 2020-04-07
SHANGHAI HUIDE TECH CO LTD
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN109609074A discloses a preparation method of a one-component moisture-curing polyurethane hot-melt adhesive. The specific steps include: mixing polyether polyol, polyester polyol, tackifier and antioxidant, vacuum dehydration, and then adding isocyanate and catalyst react, then add chain extender and filler in turn, and react to obtain hot melt adhesive; wherein, the tackifier is a copolyamide hot melt adhesive resin, which can be specially modified to the traditional one-component moisture-curing polyurethane hot melt adhesive system properties, making the bonding of hot melt adhesives to nylon fabrics more targeted; however, copolyamides have a high melting point and poor compatibility with polyurethane, making it difficult to obtain a uniform and stable system, and the viscosity of the obtained hot melt adhesives is 5000 ~6500mPa s / 120℃, while the viscosity of the hot melt adhesive used for laminating fabrics and polymer films is 1000~3000mPa s / 120℃, the viscosity of the hot melt adhesive is too high, which limits its application range
CN1261519C discloses a kind of polyurethane adhesive that is used for nylon film compounding, described polyurethane adhesive is by main agent and curing agent with mass ratio 100:(10~20); Described main agent comprises polyurethane prepolymer, polyamide and organic solvent, and the curing agent is an adduct of polyisocyanate and polyol; the polyurethane adhesive can improve the peel strength and flexibility of the nylon composite film, but its essence is a solvent-based adhesive, which cannot adapt to the current development of the textile industry need

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moisture-curable polyurethane hot melt adhesive as well as preparation method and application thereof
  • Moisture-curable polyurethane hot melt adhesive as well as preparation method and application thereof
  • Moisture-curable polyurethane hot melt adhesive as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] This embodiment provides a moisture-curing polyurethane hot-melt adhesive, and the preparation raw materials are as follows:

[0072]

[0073] Concrete preparation steps are as follows:

[0074] (1) 650 parts by weight of polyoxypropylene glycol (4000), 150 parts by weight of polyester polyol, 0.22 parts by weight of antioxidant YS245 and 0.05 parts by weight of phosphoric acid are added to the reaction vessel and mixed and dehydrated so that the water content≤500ppm, Then add 117 parts by weight of MDI, react at 75°C for 3h, then raise the temperature to 95°C for 1h;

[0075] (2) Add 126 parts by weight of MDI to the reacted material in step (1), stir for 0.5 h and mix well, then add 67.87 parts by weight of chain extender polyoxypropylene glycol (400), and react at 95°C for 2 hours;

[0076] (3) Cool the material after the reaction in step (2) to 75°C, then add 3.17 parts by weight of isopropanol, and react at 75°C for 0.5h;

[0077] (4) Add 0.55 parts by weight ...

Embodiment 2

[0079] This embodiment provides a moisture-curing polyurethane hot-melt adhesive, and the preparation raw materials are as follows:

[0080]

[0081] Concrete preparation steps are as follows:

[0082] (1) 700 parts by weight of polyoxypropylene glycol (4000), 100 parts by weight of polyester polyol, 0.21 parts by weight of antioxidant YS245 and 0.05 parts by weight of phosphoric acid are added to the reaction vessel and mixed and dehydrated so that the water content≤500ppm, Then add 103.12 parts by weight of MDI, react at 70°C for 3h, then raise the temperature to 90°C for 1h;

[0083] (2) Add 146.58 parts by weight of MDI to the reacted material in step (1), stir for 0.5 h to mix, add 38 parts by weight of chain extender dipropylene glycol, and react at 90° C. for 1 h;

[0084] (3) Cool the material after the reaction in step (2) to 70°C, then add 3.02 parts by weight of isopropanol, and react at 70°C for 0.5h;

[0085] (4) Add 0.52 parts by weight of bismorpholinyl die...

Embodiment 3

[0087] This embodiment provides a moisture-curing polyurethane hot-melt adhesive, and the preparation raw materials are as follows:

[0088]

[0089] Concrete preparation steps are as follows:

[0090] (1) 800 parts by weight of polyoxypropylene diol (4000), 0.25 parts by weight of antioxidant YS245 and 0.06 parts by weight of phosphoric acid are added to the reaction vessel and mixed and dehydrated to make the water content≤500ppm, then add 75 parts by weight of MDI, 80 ℃ for 3 hours, and then heated to 100 ℃ for 1 hour;

[0091] (2) Add 217.5 parts by weight of MDI to the reacted material in step (1), stir for 0.5 h to mix, add 181.8 parts by weight of chain extender polyoxypropylene glycol (400), and react at 100 ° C for 2 h;

[0092] (3) Cool the material after the reaction in step (2) to 80°C, then add 5.27 parts by weight of morpholine, and react at 80°C for 0.5h;

[0093] (4) Add 0.6 parts by weight of bismorpholino diethyl ether to the reacted material in step (3)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Water pressureaaaaaaaaaa
Login to view more

Abstract

The invention provides a moisture-curable polyurethane hot melt adhesive as well as a preparation method and application thereof. The moisture-curable polyurethane hot melt adhesive is prepared from the following raw material components in parts by weight: 500 to 800 parts by weight of polyether polyol, 30 to 200 parts by weight of a chain extender, 200 to 300 parts by weight of polyisocyanate, 3to 8 parts by weight of a monofunctional end-capping reagent and 0.1 to 0.6 part by weight of a catalyst, the monofunctional end-capping reagent can block part of NCO groups in a system, so that the hot melt adhesive still keeps certain viscosity after being cured and converted into a solid state, and can be stably bonded with nylon taffeta, thereby avoiding infirm bonding caused by volume changein the curing process of a polyurethane system and improving the curing effect of the polyurethane system. The bonding strength and the bonding stability are obviously improved. The moisture-curable polyurethane hot melt adhesive has proper viscosity and initial bonding strength and relatively high final bonding strength and bonding stability, and can fully meet the requirement for compounding nylon taffeta fabrics.

Description

technical field [0001] The invention belongs to the technical field of adhesives, and in particular relates to a moisture-curing polyurethane hot-melt adhesive and a preparation method and application thereof. Background technique [0002] As one of the most widely used raw materials in the textile industry, adhesives play an irreplaceable role in the production, processing and application of textiles. In terms of their chemical composition, textile adhesives include polymers such as polyurethane, acrylic polymers, polyethylene, and polyvinyl alcohol. In the production process of nylon fabric (nylon fabric), traditional solvent-based adhesives have a significant effect on nylon fabric compounding, but solvent-based adhesives will emit a large amount of organic volatile gases during use, which not only causes It not only wastes resources, but also brings environmental pollution that cannot be ignored. As the country attaches great importance to environmental protection in r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J175/08C08G18/66C08G18/48C08G18/42C08G18/32C08G18/28
CPCC09J175/08C08G18/6607C08G18/4018C08G18/4825C08G18/42C08G18/3206C08G18/282
Inventor 钱建中钱洪祥陈旭亮蔡华兵周文
Owner SHANGHAI HUIDE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap