Special binder for corundum slag pellets and its preparation and use method

A technology of corundum slag pellets and binders, which is applied in the field of comprehensive utilization and processing of secondary resources, can solve the problem of low (initial strength 1.5m broken, later strength 2m falling broken, product quality can not meet the technical requirements of processing technology, unfavorable Step drying and other issues to achieve the effect of ensuring ball forming performance, reducing drying costs, and improving viscosity

Active Publication Date: 2021-08-24
PANZHIHUA GANGCHENG GROUP
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the fine particle size, light specific gravity, poor hydrophilicity and small compression ratio of the corundum slag material, during the test production period, plant starch was used as the binder, and the amount of binder added reached 5.0% of the total weight of the material. During the production process, there are still poor material viscosity, large amount of water added (about 20%, which is not conducive to the next step of drying), poor ball forming (initial ball forming rate is less than 80%), and low strength (the initial strength is broken at 1.5m, and the later strength is 2m Falling and breaking, the powder surface ratio is greater than 20%), which directly leads to the failure of product quality to meet the technical requirements of post-processing technology, resulting in high cost of binder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special binder for corundum slag pellets and its preparation and use method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Special binder for corundum slag pellets in this embodiment: the raw materials are: 66% of plant starch, 5% of polymer polyanion cellulose, 16% of plant dextrin, and 13% of sodium fluorosilicate.

[0022] The preparation method of the special binder for corundum slag pellets in this embodiment: add the raw materials in a closed mixing and milling equipment in order of weight ratio from high to low, and grind them evenly.

[0023] The method of using the special binder for corundum slag pellets in this embodiment: add the corundum slag to the mixer and stir for 1 minute, add water with a weight ratio of 8% of the corundum slag and mix for 2 minutes, add 1.5% of the special adhesive for corundum slag pellets The mixture was stirred for 2 minutes, then water with a total weight of 4 was added and stirred for 2 minutes to obtain a mixture, which was extruded into balls.

Embodiment 2

[0025] Special binder for corundum slag pellets in this embodiment: the raw materials are calculated by weight percentage: 68% of plant starch, 4% of polymer polyanion cellulose, 17% of plant dextrin, and 11% of sodium carbonate.

[0026] The preparation method of the special binder for corundum slag pellets in this embodiment: add the raw materials in a closed mixing and milling equipment in order of weight ratio from high to low, and grind them evenly.

[0027] The method of using the special binder for corundum slag pellets in this example: add the corundum slag to the mixer and stir for 1 minute, add water with a weight ratio of 9% of the corundum slag and mix for 2 minutes, add 2.0% of the special adhesive for corundum slag pellets The mixture was stirred for 2 minutes, then water with a total weight of 4 was added and stirred for 2 minutes to obtain a mixture, which was extruded into balls.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of comprehensive utilization and processing of secondary resources, and relates to a special binder for corundum slag pellets and a preparation and use method thereof. The technical problem to be solved by the present invention is to provide a special binder for corundum slag pellets that can improve the pelletizing rate and strength of the pellets. The special binder is prepared from the following raw materials in weight ratio: 65-70% of plant starch, 4-5% of high molecular polyanion cellulose, 16-18% of plant dextrin and 10-12% of curing agent. The special binder for corundum slag pellets of the present invention has high viscosity, which can improve the viscosity of corundum slag materials, ensure the ball forming performance, initial strength and later drying strength, the ball forming rate can reach more than 95%, and the initial strength can reach 2 meters high. Drop once without breaking, and later drying strength reaches 2 meters high, drop 3 times naturally without breaking. The use of the binder of the invention significantly improves product quality, reduces the cost of the binder by 50 yuan / ton, and has broad application prospects.

Description

technical field [0001] The invention belongs to the technical field of comprehensive utilization and processing of secondary resources, and relates to a special binder for corundum slag pellets and a preparation and use method thereof. Background technique [0002] The aluminothermic method is currently the main method for producing ferrovanadium in China. The aluminothermic method uses aluminum particles as a reducing agent to produce ferrovanadium. Lime is used to adjust the composition of the slag to reduce the melting point and viscosity of the slag. At the same time, it is used as a coolant to adjust the excess heat energy. The main component of the slag (corundum slag) produced by the above process is Al2O 3 , there is a certain amount of calcium magnesium oxide and other impurities, and the scope of comprehensive utilization is narrow. [0003] At present, there are studies on crushing and processing corundum slag into materials with a particle size of 0-2mm, and pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B1/242
CPCC22B1/2406C22B1/242
Inventor 陈桂卫严翀陈涛毛朋张远春
Owner PANZHIHUA GANGCHENG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com