Solvent type polyurethane resin and preparation method thereof, and fluoride-free clothes with lotus leaf effect

A polyurethane resin and solvent-based technology, which is applied in the field of polyurethane resin, can solve the problems that fluoride cannot be used, and achieve good hydrolysis resistance, water resistance, and low surface energy.

Active Publication Date: 2020-02-21
JIANGSU HUADA NEW MATERIAL CO LTD
View PDF14 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, due to environmental and health issues, fluoride cannot be used in clothing textiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solvent type polyurethane resin and preparation method thereof, and fluoride-free clothes with lotus leaf effect
  • Solvent type polyurethane resin and preparation method thereof, and fluoride-free clothes with lotus leaf effect
  • Solvent type polyurethane resin and preparation method thereof, and fluoride-free clothes with lotus leaf effect

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] For the solvent-based polyurethane resin provided in this embodiment, the composition of the raw material formula used is shown in Table 1, wherein,

[0040] The number average molecular weight of polycarbonate polyol is 2000, purchased from Japan Ube Company.

[0041] The number-average molecular weight of polytetrahydrofuran ether glycol is 2000, purchased from BASF, Germany.

[0042] The isocyanate is 4,4-diphenylmethane diisocyanate.

[0043] The additive is antioxidant, specifically CHINOX 1010 with double bond chemistry.

[0044] The catalyst is bismuth carboxylate.

[0045] The number average molecular weight of polyethylene glycol is 2000.

[0046] The reactive silicone is X-22-176DX from Japan's Shin-Etsu.

[0047] The fumed silica is DM-10 from Tokusei Co., Ltd., Japan.

[0048] The solvent-based polyurethane resin is prepared by the following method:

[0049] In the reactor, add 25% N,N-dimethylformamide of formula quantity, the polytetrahydrofuran ethe...

Embodiment 2

[0051] For the solvent-based polyurethane resin provided in this example, the composition of raw materials used is shown in Table 1, and the others are the same as in Example 1.

[0052] In this example, the reactive silicone is made up of X-22-176DX and X-22-176F from Shin-Etsu Japan in a mass ratio of 1:1; the fumed silica is DM-20S and DM- 10 according to the mass ratio of 1:1 composition.

Embodiment 3

[0054] For the solvent-based polyurethane resin provided in this example, the composition of raw materials used is shown in Table 1, and the others are the same as in Example 1.

[0055] In this example, the reactive silicone is X-22-176F from Shin-Etsu Japan; the fumed silica is DM-20S from Tokusei Corporation.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to solvent type polyurethane resin and a preparation method thereof, and fluoride-free clothes with a lotus leaf effect. The polyurethane resin is prepared from the following rawmaterials according to a formula: polycarbonate polyol, polyether polyol, polyethylene glycol, micromolecular polyol, isocyanate, a solvent, a catalyst, reactive organic silicon oil, fumed silica, aterminating agent and an auxiliary agent. According to the invention: the polycarbonate polyol, the polyether polyol and the polyethylene glycol are combined according to a specific ratio to constitute a macromolecular polyol mixture, while the micromolecular polyol in a specific proportion is matched, and specifically the reactive organic silicon oil and the fumed silica in a certain proportion are matched, so the coating formed by the polyurethane resin prepared by using the preparation method provided by the invention has the advantages of good hydrolysis resistance, aging resistance, moisture penetrability and low surface energy, wherein the surface energy of the coating is 15 to 20N / m, while the surface energy of water is 60 N / m.

Description

technical field [0001] The invention belongs to the technical field of polyurethane resins, and in particular relates to a solvent-based polyurethane resin, its preparation method and its application. Background technique [0002] The biggest use of down jackets is to keep warm, but the rainproof effect is not good. Traditional down jacket fabrics are wet when exposed to water. Especially in the south, it often encounters rainy days in winter, and an environmentally friendly (mainly for human health) is needed. The fabric can be worn in rainy days as well as in snowy days. Rainwater or melted snow can slide off clothes instantly like water droplets on lotus leaves. [0003] With the gradual improvement of the living standards of the general public, physical health has become the main pursuit of the current society. Everyone needs to go outdoors for running and fitness, and necessary outdoor equipment is essential. Outdoor clothing needs to have waterproof and breathable fun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G18/76C08G18/66C08G18/61C08G18/44C08G18/48C08G18/32D06N3/14D06N3/00
CPCC08G18/7671C08G18/6607C08G18/61C08G18/4854C08G18/44C08G18/3206D06N3/147D06N3/146D06N3/0063D06N2211/10D06N2209/128D06N2209/123
Inventor 史振涛蒋明
Owner JIANGSU HUADA NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More