Water-based self-luminous elastic coating, and preparation method and application thereof

An elastic coating and self-luminous technology, which is applied in the direction of luminescent coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of no self-luminous performance, poor wear resistance, poor adhesion, etc., and achieve fine and smooth hand feeling Cool, good elasticity, good luminous intensity effect

Active Publication Date: 2020-02-14
HUNAN SOKAN NEW MATERIAL
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a water-based self-luminous elastic coating and its preparation method and application to solve the existing water-based elastic coatings with poor adhesion, poor hand feeling, low hardness, poor wear resistance, and no self-luminous performance. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based self-luminous elastic coating, and preparation method and application thereof
  • Water-based self-luminous elastic coating, and preparation method and application thereof
  • Water-based self-luminous elastic coating, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] According to another aspect of the present invention, also provide a kind of preparation method as above-mentioned waterborne self-luminous elastic paint, comprise the following steps:

[0035] (1), mixing the modified oily elastic resin, an emulsifier and water for emulsification to obtain an emulsion;

[0036] (2), add water-based polyurethane elastic resin to the emulsion in step (1) while stirring and mix, then add substrate wetting agent, dispersant, matting powder and some auxiliary agents to mix and disperse to obtain a mixed solution;

[0037] (3), adding water-based energy storage material, luminescent material and remaining additives to the mixed solution in step (2) while stirring, dispersing and filtering to obtain the coating component;

[0038] (4) Mix the coating components and the curing agent components to obtain the water-based self-luminous elastic coating.

[0039] The preparation method of the water-based self-luminous elastic coating of the presen...

Embodiment 1

[0057] The parts by weight of the components of the water-based self-luminous elastic coating in Example 1 are shown in Table 1.

[0058] Table 1: The parts by weight of each component in the water-based self-luminous elastic coating of embodiment and the coating of comparative example

[0059]

[0060]

[0061] The preparation method of above-mentioned water-based self-luminous elastic paint, comprises the following steps:

[0062] (1), anionic polycarbonate polyurethane resin, emulsifier and water are mixed for emulsification, and the emulsification condition is 850r / min to disperse for 25min until full emulsification is completed to obtain an emulsion;

[0063] (2), add water-based aliphatic anionic polyurethane resin to the emulsion in step (1) while stirring, and then add acetylenic glycol surfactants, dispersants, silicon dioxide and part of polysiloxane-polyether Copolymer and polyether siloxane copolymer, dispersed, dispersed at 1300r / min for 23min to a fineness...

Embodiment 2

[0068] The parts by weight of the components of the water-based self-luminous elastic coating in Example 2 are shown in Table 1. The preparation method and application of the water-based self-luminous elastic coating are the same as those in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
adhesivityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-based self-luminous elastic coating, and a preparation method and an application thereof. The water-based self-luminous elastic coating comprises a coating component and a curing agent component; the coating component comprises the components in parts by mass: 10-20 parts of modified oily elastic resin, 10-30 parts of water-based polyurethane elastic resin, 1-2 parts of an emulsifier, 0.3-0.6 part of a base material wetting agent, 30-40 parts of a water-based energy storage material, 0.01-2 parts of a water-based luminous material, 1-3 parts of a dispersing agent, 1-3 parts of extinction powder, 0.7-2 parts of an auxiliary agent and 20-40 parts of water. According to the water-based self-luminous elastic coating, modified oily elastic resin and water-based polyurethane elastic resin are used as main film-forming resin and are subjected to reaction with molecules of the curing agent component, and a compact net-shaped structure is formed, so that the hardness, boiling resistance and wear resistance of the coating are remarkably improved, a formed paint film is good in elasticity and fine and smooth in hand feeling, has the advantages of boiling resistance, weather resistance, wear resistance and the like, has the adhesive force of 5B, the hardness of H and high luminous intensity, and can emit light for 12 h or more after absorbing light for 10-20min.

Description

technical field [0001] The invention relates to the field of water-based paints, in particular to a water-based self-luminous elastic paint. In addition, the present invention also relates to a preparation method and application of the above-mentioned water-based self-luminous elastic coating. Background technique [0002] With the continuous improvement of people's awareness of environmental protection, water-based coatings are accepted by more people as a more environmentally friendly coating material, and the prospects for water-based coatings are getting better and better. Water-based coatings eliminate the risk of fire during construction and reduce air pollution. Water-based coatings use water as a solvent, which saves a lot of resources. Only a small amount of low-toxic alcohol ether organic solvents are used, which improves the working environment and has a significant effect on reducing pollution and saving resources. [0003] However, there are many gaps between ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D5/22
CPCC08L2205/025C09D5/22C09D175/04C08L75/04
Inventor 陈旭王卫国李平吕国强缪培凯凌云剑符饶生杨波曾煜李玉良邓磊乔臧亦武傅碧容戴磊符新约
Owner HUNAN SOKAN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com