A kind of ferroferric oxide ceramsite and its preparation method and application

A technology of ferroferric oxide and ceramsite, which is applied in the direction of chemical instruments and methods, applications, ceramic products, etc., can solve the problem of degrading airborne endotoxin without microwave radiation, achieve good application prospects, easy preparation, and high reflection loss Effect

Active Publication Date: 2022-03-04
TIANJIN UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although some researchers have used the thermal and non-thermal effects of microwaves to inactivate bioaerosols, there has been no research on combining microwave technology with microwave-absorbing fillers to improve their inactivation performance.
In addition, so far, there is no research on the degradation of airborne endotoxin by microwave radiation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ferroferric oxide ceramsite and its preparation method and application
  • A kind of ferroferric oxide ceramsite and its preparation method and application
  • A kind of ferroferric oxide ceramsite and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A microwave reaction device for removing bioaerosols, comprising a shell, a quartz tube 3 fixedly arranged in the shell, and quartz wool filled between the quartz tube 3 and the shell, the top of the quartz tube 3 is fixed with The infrared temperature measurement module 5 is fixed with a magnetron 6 for generating microwaves at the bottom, and a porous sieve plate 8 is arranged inside the quartz tube 3 to divide the quartz tube 3 into an upper chamber and a lower chamber. The side wall of the chamber is provided with an air inlet 1 communicating with it, the upper chamber is used for filling wave-absorbing filler and at least one air outlet 2 communicating with it is provided on the side wall, and the housing is provided with There is an observation port 7 for observing the wave-absorbing filler.

[0038] As a preferred manner, the number of the gas outlets 2 is two, which are respectively located at different heights of the quartz tube 3 .

[0039] As a preferred met...

Embodiment 2

[0045] Weigh 40g of ferric oxide powder, 10g of bentonite, NaHCO 3 0.25g, mix thoroughly and add water and mix thoroughly. Use the above-mentioned mixed materials to make a single pellet with a diameter of 5-10mm, put it in an oven at 150°C for 30 minutes, then put it into a muffle furnace, bake it at 200°C for 30 minutes, and naturally cool to room temperature to obtain tetraoxide Tri-iron ceramsite with a porosity of 4.7%.

[0046] The above-mentioned ferroferric oxide ceramsite is packed into the reaction device of embodiment 1 as a microwave filler, the total power of the magnetron 6 with a set frequency of 2.45GHz is 700W, and the initial concentration of treatment is 10 5.8 CFU / m 3About Escherichia coli bioaerosol (Escherichia coli CMCC1.3373), when described Escherichia coli bioaerosol is under the condition of 20 seconds residence time in the reaction device of embodiment 1, the Escherichia coli biogas of export Sol concentration is 10 1.7 CFU / m 3 About, inactivat...

Embodiment 3

[0048] Weigh 80g of ferric oxide powder, 20g of bentonite, NaHCO 3 0.5g, mix thoroughly and add water and mix thoroughly. Use the above-mentioned mixed materials to make a single pellet with a diameter of 5-10mm, put it in an oven at 150°C for 30 minutes, then put it into a muffle furnace, bake it at 200°C for 30 minutes, and naturally cool to room temperature to obtain tetraoxide Tri-iron ceramsite with a porosity of 4.7%.

[0049] The above-mentioned ferroferric oxide ceramsite is packed into the reaction device of embodiment 1 as a microwave filler, the total power of the magnetron 6 with a set frequency of 2.45GHz is 700W, and the initial concentration of treatment is 10 6.1 CFU / m 3 About Bacillus subtilis bioaerosol (Bacillus subtilis CMCC1.4255), when described Bacillus subtilis bioaerosol residence time is under the condition of 20 seconds in the reaction device of embodiment 1, the Bacillus subtilis organism of export Aerosol concentration is 10 2.9 CFU / m 3 About,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ferroferric oxide ceramsite and its preparation method and application. The preparation method of the ferroferric oxide ceramsite includes the following steps: step 1, weighing four Ferric oxide powder and bentonite, then add 0.4-0.6% NaHCO of the total mass of the two 3 , mix well, add water and mix thoroughly; step 2, use the pelletizing machine to make the mixture obtained in step 1 into a single pellet with a diameter of 5-10mm; step 3, dry the pellet prepared in step 2 at 120-180°C 20-40 minutes; step 4, seal the dried pellets, bake at 150-250°C for 20-40 minutes, then cool naturally to room temperature 20-30°C to obtain ferric oxide ceramsite. The ferroferric oxide ceramsite can be used as a microwave-absorbing material to inactivate biological aerosols by microwave radiation.

Description

technical field [0001] The invention relates to the technical field of air pollution control, in particular to a ferroferric oxide ceramsite and a preparation method and application thereof. Background technique [0002] There are a large number of microorganisms and their secretions (biological particles) in the air, including: bacteria, viruses, chlamydia, mycoplasma, fungal spores, algae and plant cells (including pollen), insects (including mites) and their fragments and secretions The two-phase dispersion system formed by these biological particles suspended in the air and the air is called bioaerosol. The aerodynamic equivalent diameter of the bioaerosol is between 0.5-100 μm, and the equivalent diameter of the bacteria-carrying particles is generally between 4-20 μm, among which the bacteria-carrying particles with an equivalent diameter of 1-5 μm can directly invade the alveoli and cause the initial lung infection. Harmful to human health. [0003] Endotoxin is a h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/02C04B35/26B01D39/06C09K3/00
CPCC04B38/009C04B38/02C04B35/26B01D39/06C09K3/00C04B2235/349C04B38/0074
Inventor 王灿张郅巍路思艺
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com