A kind of preparation method of graphene-coated manganese dioxide composite wave absorbing agent

A technology of graphene coating and manganese dioxide, applied in the direction of graphene, manganese oxide/manganese hydroxide, nanotechnology for materials and surface science, etc., can solve the problem of poor composite interface performance and weak bonding force of heterogeneous materials , secondary agglomeration and other issues, to achieve the effects of optimized impedance matching performance, good dispersion performance, and excellent composite interface

Active Publication Date: 2021-12-07
SHANXI INST OF COAL CHEM CHINESE ACAD OF SCI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the deficiencies in the prior art and solve the technical problems of weak bonding force of heterogeneous materials, poor composite interface performance, and serious secondary agglomeration, the invention provides a preparation method of graphene-coated manganese dioxide composite wave absorbing agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of graphene-coated manganese dioxide composite wave absorbing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation method of graphene-coated manganese dioxide composite wave absorbing agent, comprising the following steps:

[0024] S1, take by weighing manganese sulfate and ammonium persulfate of certain quality respectively, wherein the mol ratio of manganese sulfate and ammonium persulfate is 0.1:1, leave it for later use;

[0025] S2. Slowly add the manganese sulfate weighed in step S1 into the graphene oxide aqueous solution with a concentration of 3 mg / mL for 3 minutes, and at the same time perform magnetic stirring for 30 minutes to form a gel, which will be reserved for later steps use;

[0026] S3. Slowly add the ammonium persulfate weighed in step S1 into the gel prepared in step S2 at a uniform speed for 15 minutes, and at the same time perform magnetic stirring for 1 hour to prepare a mixed solution, which will be used in the next step;

[0027] S4, subjecting the mixed solution prepared in step S3 to hydrothermal treatment, the heating temperature is 100° ...

Embodiment 2

[0030] A preparation method of graphene-coated manganese dioxide composite wave absorbing agent, comprising the following steps:

[0031] S1, take by weighing manganese sulfate and ammonium persulfate of certain quality respectively, and wherein the mol ratio of manganese sulfate and ammonium persulfate is 10:1, leave it for later use;

[0032] S2. Slowly add the manganese sulfate weighed in step S1 into the graphene oxide aqueous solution with a concentration of 0.5 mg / mL for 5 minutes, and at the same time, perform magnetic stirring for 50 minutes to make a gel and leave it for later Step use;

[0033] S3. Slowly add the ammonium persulfate weighed in step S1 to the gel prepared in step S2 at a uniform speed for 25 minutes, and at the same time perform magnetic stirring for 30 minutes to prepare a mixed solution, which will be used in the next step;

[0034] S4, subjecting the mixed solution prepared in step S3 to hydrothermal treatment, the heating temperature is 120° C., ...

Embodiment 3

[0037] A preparation method of graphene-coated manganese dioxide composite wave absorbing agent, comprising the following steps:

[0038] S1, take by weighing manganese sulfate and ammonium persulfate of a certain quality respectively, wherein the mol ratio of manganese sulfate and ammonium persulfate is 6:1, leave it for later use;

[0039] S2. Slowly add the manganese sulfate weighed in step S1 into the graphene oxide aqueous solution with a concentration of 10 mg / mL for 30 min, and at the same time perform magnetic stirring for 1 h to form a gel, which will be reserved for the next step use;

[0040] S3. Slowly add the ammonium persulfate weighed in step S1 into the gel prepared in step S2 at a uniform speed for 10 minutes, and magnetically stir at the same time for 1.2 hours to prepare a mixed solution, which will be used in the next step;

[0041] S4, subjecting the mixed solution prepared in step S3 to hydrothermal treatment, the heating temperature is 200° C., and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a graphene-coated manganese dioxide composite wave-absorbing agent, which belongs to the technical field of electromagnetic wave-absorbing materials, and solves the technical problems of weak bonding force of heterogeneous materials, poor composite interface performance, and serious secondary agglomeration, specifically The preparation process includes: S1, weighing manganese sulfate and ammonium persulfate; S2, adding manganese sulfate into the graphene oxide aqueous solution slowly at a uniform speed, and magnetically stirring at the same time to obtain a gel; S3, adding ammonium persulfate slowly at a uniform speed In the prepared gel, magnetic stirring is performed at the same time; S4, the mixed solution is subjected to hydrothermal treatment; S5, the reaction product is separated, washed with deionized water to neutrality, and freeze-dried to obtain a graphene-coated manganese dioxide composite absorber agent. The invention makes the two components tightly combined by chemical bonds, which not only exerts the dielectric loss performance of manganese dioxide on incident electromagnetic waves, but also combines the multiple scattering performance of reduced graphene on incident electromagnetic waves, and has a simple preparation process and is easy to realize. industrialization.

Description

technical field [0001] The invention belongs to the technical field of electromagnetic wave-absorbing materials, relates to the cross technical field of material science and chemical synthesis preparation, and specifically relates to a preparation method of a graphene-coated manganese dioxide composite wave-absorbing agent for electromagnetic wave absorption. Background technique [0002] In the current society, electromagnetic pollution has become another major pollution after water pollution, air pollution, and noise pollution. It not only poses a threat to human health, but also interferes with the normal operation of other electronic equipment, which brings great harm to the information security of individuals, enterprises and even the country. serious threat. Electromagnetic wave absorption is one of the effective ways to prevent electromagnetic pollution. In the electromagnetic wave absorbing material, the wave absorbing agent is the key point, which directly determin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G45/02C01B32/184B82Y40/00B82Y30/00H05K9/00
CPCB82Y30/00B82Y40/00C01G45/02C01P2004/16C01P2004/80C01B32/184H05K9/0081
Inventor 陈成猛刘卓孔庆强李晓明郭晓倩
Owner SHANXI INST OF COAL CHEM CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More