A kind of preparation method of molybdenum powder with low oxygen content

A technology of low oxygen content and molybdenum powder, which is applied in metal processing equipment, transportation and packaging, etc., can solve the problems of limiting the performance of molybdenum alloy products, achieve large-scale production and environmental protection, unlimited production capacity, and simple process Effect

Active Publication Date: 2022-01-11
FUJIAN ACETRON NEW MATERIALS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Molybdenum powder with small particle size, especially molybdenum powder with an average particle size below 10-20 microns, can easily absorb oxygen in the air environment, causing the oxygen content of molybdenum powder to easily reach more than 500ppm, which seriously limits its application and molybdenum alloy products. performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of molybdenum powder with low oxygen content
  • A kind of preparation method of molybdenum powder with low oxygen content

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] A method for preparing molybdenum powder with low oxygen content, comprising the following steps: using 2-10 micron molybdenum powder as a raw material, forming it through a cold isostatic press at 150-300 MPa, and then crushing it to 100-200 mesh with a disc grinder and passing through 100 mesh Sieve, hydrogenate the powder at 1000-1500°C, keep it warm for 1-5h, cool the powder to room temperature, crush it in a nitrogen atmosphere, and pass through a 100-mesh sieve to obtain molybdenum powder with an average particle size of 100 mesh and an oxygen content of 50-150ppm. Such as figure 1 shown.

[0032] The molybdenum powder used in the present invention is molybdenum oxide, ammonium molybdate and other molybdenum powder obtained after hydrogen reduction at a high temperature of 500-1200 ° C. The raw material of this molybdenum powder generally has a particle size of 2-10 microns. The use of products is also because the preparation process determines that the particle ...

Embodiment 1

[0037] The molybdenum powder raw material is selected as molybdenum powder with D50=4.5 microns, and the oxygen content is 680ppm.

[0038] Weigh 15kg of molybdenum powder into the rubber sheath, and vibrate it with a vibration platform. After sealing, mold it in a cold isostatic press at 285MPa, and the pressure holding time is 2 minutes. After the pressing is completed, the density of the molybdenum block is tested as 67%.

[0039] Continue to put the molybdenum block into the rubber sheath and hit it with a hammer to break the molybdenum block into small pieces, then transfer the molybdenum block to a zirconia grinding machine for further crushing, and the crushed particles pass through a 100-mesh sieve network.

[0040] Place the crushed and sieved molybdenum powder on a molybdenum boat tray with a size of 300*500mm to prevent uniformity, and then calcinate and keep it warm for 3 hours in a hydrogen environment at 1350°C.

[0041] After the calcination is completed, lowe...

Embodiment 2

[0044] The molybdenum powder raw material is selected as molybdenum powder with D50=4.5 microns, and the oxygen content is 680ppm.

[0045] 1. Weigh 15kg of molybdenum powder into the rubber sheath, and vibrate it with a vibration platform. After sealing, mold it in a cold isostatic press at 150MPa. The holding time is 2 minutes. After pressing, test the molybdenum block. The density is 53%.

[0046] 2. Continue to put the molybdenum block into the rubber sheath, hit it with a hammer to break the molybdenum block into small pieces, and then transfer the molybdenum block to a zirconia grinding machine for further crushing. The crushed particles are over 100 mesh screen.

[0047] 3. Place the crushed and sieved molybdenum powder on a molybdenum boat tray with a size of 300*500mm to prevent uniformity, and then calcinate and keep it warm for 2 hours in a hydrogen environment at 1150°C.

[0048] 4. After the calcination is completed, lower it to room temperature, smash the bonde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing molybdenum powder with low oxygen content, comprising the following steps: using 2-10 micron molybdenum powder as a raw material, forming it through a cold isostatic pressing machine at 150-300 MPa, and then crushing it to 100-200 mesh with a disc grinder and Pass through a 100-mesh sieve, hydrogenate the powder at 1000-1500°C, keep it warm for 1-5 hours, cool the powder to room temperature, and then crush it in a nitrogen atmosphere and pass through a 100-mesh sieve to obtain a powder with an average particle size of 100 mesh and an oxygen content of 50-150ppm Molybdenum powder. The process of the present invention is simple, directly extends the process on the traditional preparation technology, only requires a small amount of investment, and the production capacity is not limited; more importantly, the oxygen content is extremely low, and the oxygen content of the molybdenum powder can be reduced from the general 500-700ppm to 50- 150ppm. The effect and benefit of the present invention are that it exhibits significant competitive advantages and profit margins in terms of manufacturing cost, product performance, large-scale production, environmental friendliness and the like.

Description

technical field [0001] The invention relates to the technical field of preparation of functional inorganic materials, in particular to a method for preparing molybdenum powder with low oxygen content. Background technique [0002] In the powder metallurgy preparation process of molybdenum products, the raw material performance of molybdenum powder greatly affects the quality of subsequent processed products. In the production process from raw material ammonium molybdate to molybdenum deep-processed products, the preparation of molybdenum powder is relatively important link. [0003] According to the use of molybdenum powder, the main preparation methods of molybdenum powder are divided into three categories: molybdenum powder for pressing, spherical molybdenum powder for thermal spraying and ultra-fine molybdenum powder for special conditions. In order to meet the needs of different types of molybdenum powders, it is necessary to study the process of preparing various molyb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F3/04B22F9/04B22F1/00
CPCB22F3/04B22F9/04B22F2009/045B22F2009/044B22F2998/10B22F2999/00B22F1/145B22F2201/013
Inventor 侯庆龙陈钦忠张科吴荣祯蔡小勇张梦兰
Owner FUJIAN ACETRON NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com