A kind of ultra-low carbon high temperature resistant welding wire and preparation method thereof

A high-temperature-resistant, ultra-low-carbon technology, applied in welding equipment, welding media, manufacturing tools, etc.

Active Publication Date: 2020-11-13
常州长海焊材有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Reducing the carbon content in the welding wire can effectively reduce the carbon content in the weld seam, but the reduction of the carbon content in the welding wire affects the mechanical properties of the welding wire. Therefore, while ensuring the low carbon content of the welding wire, improving the mechanical properties of the welding wire is currently a problem that needs to be solved question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-low carbon high temperature resistant welding wire and preparation method thereof
  • A kind of ultra-low carbon high temperature resistant welding wire and preparation method thereof
  • A kind of ultra-low carbon high temperature resistant welding wire and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The chemical composition of an ultra-low carbon high temperature resistant welding wire is calculated by mass percentage: C is 0.02%, Cr is 23.5%, Si is 2.5%, Ni is 13.2%, Ti is 0.8%, Mn is 0.28%, Zr is 0.35% %, Sc is 0.45%, Mo is 0.22%, Nb is 0.41%, Mg is 4.3%, Al is 0.9%, P is 0.05%, S is 0.04%, V is 0.33%, B is 1.45%, and the balance is Fe and other unavoidable impurity elements.

[0035] The preparation method of the ultra-low carbon high temperature resistant welding wire specifically includes the following steps:

[0036] Step 1. Ingredients smelting: Weigh each component according to the ratio, and then put it into a heating furnace for smelting, and the smelting temperature is 1850°C;

[0037] Step 2. Refining: After all the components in the heating furnace are melted, add a refining agent and stir evenly. The refining agent accounts for 0.3% of the total mass of the alloy liquid, and the refining temperature is 1600°C;

[0038] Step 3. Casting: After refinin...

Embodiment 2

[0043] The chemical composition of an ultra-low carbon high temperature resistant welding wire is calculated by mass percentage: C is 0.03%, Cr is 22.8%, Si is 2.8%, Ni is 13.6%, Ti is 0.6%, Mn is 0.35%, Zr is 0.41% %, Sc is 0.52%, Mo is 0.22%, Nb is 0.41%, Mg is 4.3%, Al is 0.9%, P is 0.05%, S is 0.04%, V is 0.33%, B is 1.45%, and the balance is Fe and other unavoidable impurity elements.

[0044] The preparation method of the ultra-low carbon high temperature resistant welding wire specifically includes the following steps:

[0045] Step 1. Ingredients smelting: weigh each component according to the ratio, and then put them into the heating furnace for smelting;

[0046] Step 2, refining: After all the components in the heating furnace are melted, add a refining agent and stir evenly, and the refining agent accounts for 0.4% of the total mass of the alloy liquid;

[0047] Step 3, Casting: After refining, let it stand for 30 minutes, remove the slag on the surface of the al...

Embodiment 3

[0052] The chemical composition of an ultra-low carbon high temperature resistant welding wire is calculated by mass percentage: C is 0.01%, Cr is 22.0%, Si is 3.5%, Ni is 12.0%, Ti is 1.2%, Mn is 0.1%, Zr is 0.5% %, Sc is 0.6%, Mo is 0.1%, Nb is 0.5%, Mg is 3.0%, Al is 1.2%, P is 0.07%, S is 0.05%, V is 0.4%, B is 1.6%, and the balance is Fe and other unavoidable impurity elements.

[0053] The preparation method of the ultra-low carbon high temperature resistant welding wire specifically includes the following steps:

[0054] Step 1. Ingredients smelting: weigh each component according to the ratio, and then put them into the heating furnace for smelting;

[0055] Step 2, refining: After all the components in the heating furnace are melted, add a refining agent and stir evenly, the refining agent accounts for 0.5% of the total mass of the alloy liquid;

[0056] Step 3. Casting: After refining, let it stand for 20 minutes, remove the slag on the surface of the alloy liquid,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to an ultralow-carbon high-temperature-resistant welding wire and a preparation method thereof. The ultralow-carbon high-temperature-resistant welding wire comprises the following chemical components, in percentage by mass, of 0.01%-0.04% of C, 22.0%-24.0% of Cr, 1.5%-3.5% of Si, 12.0%-14.0% of Ni, 0.5%-1.2% of Ti, 0.1%-0.4% of Mn, 0.2%-0.5% of Zr, 0.3%-0.6% of Sc, 0.1%-0.3%of Mo, 0.3%-0.5% of Nb, 3.0%-5.0% of Mg, 0.6%-1.2% of Al, 0.03%-0.07% of P, 0.02%-0.05% of S, 0.2%-0.4% of V, 1.3%-1.6% of B, and the balance Fe and other inevitable impurity elements. According to the method, the mechanical property of the welding wire can be improved while the low carbon of the welding wire is ensured.

Description

technical field [0001] The invention relates to the technical field of welding wire, in particular to an ultra-low carbon high temperature resistant welding wire and a preparation method thereof. Background technique [0002] Welding wire is used as filler metal or as conductive wire welding material at the same time. In gas welding and gas tungsten arc welding, welding wire is used as filler metal. In submerged arc welding, electroslag welding and other gas shielded arc welding , the wire is both the filler metal and the conductive electrode. Stainless steel is widely used in many fields due to its good corrosion resistance, durability, wear resistance and other properties. In the process of industrial application of stainless steel, in order to meet some large-scale requirements, stainless steel needs to be welded, and the intergranular corrosion of stainless steel welds is a major problem for the chemical industry. [0003] When the stainless steel with intergranular co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/54C22C38/50C22C38/48C22C38/46C22C38/44C22C38/02C22C38/04C22C38/06C22C38/60C21D8/06B21C37/04B23K35/30
CPCB21C37/047B23K35/0261B23K35/3086C21D8/065C22C38/002C22C38/005C22C38/04C22C38/06C22C38/34C22C38/44C22C38/46C22C38/48C22C38/50C22C38/54C22C38/60
Inventor 毛兰秀
Owner 常州长海焊材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com