Vacuum-plated UV-cured primer, preparation method therefor and application of vacuum-plated UV-cured primer

A technology of vacuum electroplating and epoxy acrylate, used in primers, coatings, epoxy coatings, etc., can solve problems such as poor leveling effect and easy cracking, and achieve low cost, improved adhesion, and heat resistance. Good results

Active Publication Date: 2019-12-03
HUNAN SOKAN NEW MATERIAL
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a vacuum electroplating UV curing primer and its preparation method and application to solve the technical problems of poor leveling effect after film formation on the surface of the coating used for vacuum coating and easy cracking when bent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vacuum-plated UV-cured primer, preparation method therefor and application of vacuum-plated UV-cured primer
  • Vacuum-plated UV-cured primer, preparation method therefor and application of vacuum-plated UV-cured primer
  • Vacuum-plated UV-cured primer, preparation method therefor and application of vacuum-plated UV-cured primer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] The parts by weight of each component in the vacuum electroplating UV curing primer of Example 1 are shown in Table 1 respectively.

[0048] Table 1: Parts by weight of each component in the vacuum electroplating UV curing primer of Examples 1-3

[0049]

[0050]

[0051] The preparation method of above-mentioned vacuum electroplating UV curing primer

[0052] S1. Preheat low-functionality acrylate B-221, epoxy acrylate 6215-100, and epoxy acrylate HE429. The preheating temperature is 50°C and the preheating time is 60 minutes. Mix and dissolve them with butyl acetate to form the first mixed solution;

[0053] S2. Add propoxylated neopentyl glycol diacrylate and HMPF to the first mixed solution in step S1 and stir, the stirring temperature is 450°C, the stirring time is 30min, and the stirring speed is 500 rpm, forming the second mixture;

[0054] S3, add BYK-306 and ethyl acetate, butanone, cyclohexanone and methyl isobutyl ketone to the second mixed solution ...

Embodiment 2

[0060] The parts by weight of each component in the vacuum electroplating UV curing primer of this embodiment 2 are respectively shown in Table 1. The preparation method and application of the vacuum electroplating UV curing primer and the vacuum electroplating UV curing paint are the same as in Example 1.

Embodiment 3

[0062] The parts by weight of each component in the vacuum electroplating UV curing primer of this embodiment 3 are shown in Table 1 respectively. The preparation method and application of the vacuum electroplating UV curing primer and the vacuum electroplating UV curing paint are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Functional group degreeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a vacuum-plated UV-cured primer, a preparation method therefor and an application of the vacuum-plated UV-cured primer. The vacuum-plated UV-cured primer comprises the ingredients in parts by weight: 8-30 parts of low-functionality acrylate, 3-12 parts of reactive diluent, 10-30 parts of epoxy acrylate, 0.01-0.5 part of auxiliaries, 2-3 parts of photoinitiator and 40-60 parts of organic environment-friendly solvent, wherein the low-functionality acrylate is aliphatic polycarbonate acrylate with the functionality of 1 to 4; and the epoxy acrylate is modified epoxy acrylate with the functionality of 1 to 4. According to the vacuum-plated UV-cured primer disclosed by the invention, the low-functionality acrylate, the reactive diluent and the epoxy acrylate serve as primary film forming matters, the reactive diluent can neutralize two kinds of prepolymers, and two kinds of prepolymers of different molecular structures can be rapidly crosslinked together to form cross-linked network knots and be cured to form a film, so that the vacuum-plated UV-cured primer is high in leveling and covering power and good in plating property.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a vacuum electroplating UV curing primer. In addition, the present invention also relates to a preparation method and application of the above-mentioned vacuum electroplating UV curing primer. Background technique [0002] At present, with the continuous progress of society and the continuous improvement of people's living standards, various electronic or electrical products, cosmetic packaging, digital cameras, notebook computers, mobile phones, cameras, MP3, MP4, electric toothbrushes, smart speakers, etc. have been widely used in people's daily life. The shells of these products are mostly made of plastic or plastic materials. In order to increase the diversification of product appearance and make the product more beautiful and decent, it is necessary to spray paint on the surface of the substrate to achieve a decorative effect, and the product without paint protection will ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D169/00C08J7/04C08L69/00
CPCC08J2369/00C08J2463/10C08J2469/00C08L2205/025C08L2205/03C09D5/002C09D163/10C09D169/00C08L63/10C08L69/00
Inventor 卢志林王卫国吕国强缪培凯凌云剑符饶生杨波
Owner HUNAN SOKAN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap