Application of layered double metal hydroxide gas sensor in detection of ethanol

A layered bimetallic, hydroxide technology, applied in the direction of aluminum oxide/aluminum hydroxide, zinc oxide/zinc hydroxide, nickel oxide/nickel hydroxide, etc., can solve the problems that hinder the miniaturization of integrated circuits, do not allow and consume energy and other issues

Active Publication Date: 2022-02-22
TIANJIN UNIV
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In reality, the high temperature condition is a big obstacle. It not only consumes energy but also requires complex structural design in the process of sensor preparation, which greatly hinders the development of integrated circuit miniaturization and greatly increases the cost; in addition , high temperature operation is not allowed in many situations, especially in some flammable and explosive environments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of layered double metal hydroxide gas sensor in detection of ethanol
  • Application of layered double metal hydroxide gas sensor in detection of ethanol
  • Application of layered double metal hydroxide gas sensor in detection of ethanol

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Configure the precursor solution required for hydrothermal reaction

[0027] Add sodium lauryl sulfate powder into 50ml deionized water, stir magnetically for 10min to dissolve it completely, and obtain a 0.45mmol / L sodium lauryl sulfate solution. Mix magnesium nitrate and aluminum nitrate powder according to the ratio of 2:1 Add the molar ratio of magnesium to aluminum into the sodium lauryl sulfate solution, keep stirring, weigh 6mmol of urea and dissolve it in 10ml of deionized water, add the obtained urea solution to the above solution drop by drop, and then continue magnetic stirring for 20min .

[0028] (2) Preparation of magnesium-aluminum layered double metal hydroxide by hydrothermal method

[0029] The final solution after (1) stirring is transferred to a 100ml high-pressure reactor lined with polytetrafluoroethylene, and after sealing, the reactor is placed in an oven for hydrothermal reaction. The oven operating temperature is 150 ° C, and the heating t...

Embodiment 2

[0040] (1) Configure the precursor solution required for hydrothermal reaction

[0041] Add sodium lauryl sulfate powder into 50ml of deionized water, stir magnetically for 10 minutes, and dissolve it completely to obtain a 0.9mmol / L sodium lauryl sulfate solution. Mix zinc nitrate and aluminum nitrate powder in a ratio of 3:1 Add the molar ratio of zinc to aluminum into the sodium lauryl sulfate solution, keep stirring, weigh 6mmol of urea and dissolve it in 10ml of deionized water, add the obtained urea solution to the above solution drop by drop, and then continue magnetic stirring for 20min .

[0042] (2) Preparation of zinc-aluminum layered double metal hydroxides by hydrothermal method

[0043] The final solution after (1) stirring is transferred to a 100ml high-pressure reactor lined with polytetrafluoroethylene, and after sealing, the reactor is placed in an oven for hydrothermal reaction. The oven operating temperature is 150 ° C, and the heating time is 2h.

[004...

Embodiment 3

[0054] (1) Configure the precursor solution required for hydrothermal reaction

[0055] Add sodium lauryl sulfate powder into 50ml of deionized water, stir magnetically for 10min, and dissolve it completely to obtain a 1.8mmol / L sodium lauryl sulfate solution. Mix nickel nitrate and aluminum nitrate powder according to the ratio of 3:1 Add the molar ratio of nickel to aluminum into the sodium lauryl sulfate solution, keep stirring, weigh 6mmol of urea and dissolve it in 10ml of deionized water, add the obtained urea solution to the above solution drop by drop, and then continue magnetic stirring for 20min .

[0056] (2) Preparation of nickel-aluminum layered double hydroxides by hydrothermal method

[0057] The final solution after (1) stirring is transferred to a 100ml high-pressure reactor lined with polytetrafluoroethylene. After sealing, the reactor is placed in an oven for hydrothermal reaction. The operating temperature of the oven is 180 ° C, and the heating time is 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a layered double metal hydroxide gas sensor modified with silver particles on the surface and its preparation method and application. The flower-shaped layered hierarchical nanocomposite of nano silver / layered double hydroxide is prepared by adopting the method of surface modification of noble metals. structure. The huge gas adsorption specific surface area provided by the flower-shaped layered hierarchical structure of LDHs, and the chemical sensitization of nano-silver further improve and enhance the ethanol-sensitive performance of the composite structure system. In the three-dimensional hierarchical composite nanostructure prepared by the present invention, there is a synergistic coupling effect between the layered double metal hydroxide and the noble metal silver, and the formed gas sensor has very high sensitivity and good response recovery characteristics to ethanol at room temperature, Therefore, it is a very potential room temperature ethanol sensitive element.

Description

technical field [0001] The invention belongs to the technical field of gas sensors, and more specifically relates to a preparation method of a layered double metal hydroxide high-performance gas sensor modified by surface silver particles for detecting ethanol at room temperature; high sensitivity to ethanol can be realized at room temperature detection, and has extremely fast response recovery characteristics, and also exhibits good selectivity. Background technique [0002] Every year, traffic accidents caused by drunk driving have brought serious personal and property safety to people. Therefore, in order to reduce drunk driving incidents, the traffic management department has formulated a strict drunk driving management system, and a series of electrochemical sensors for quickly detecting the alcohol concentration in the exhaled breath of the human body have also emerged as the times require. Among them, semiconductor metal oxide gas sensors have been widely prepared an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N27/407C01F7/02C01G9/02C01G53/04
CPCG01N27/4071C01F7/02C01G9/02C01G53/04
Inventor 秦玉香王立萍王霄飞白忆楠
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com