Waterborne environment-friendly paint and preparation method thereof

A water-based, environmentally friendly technology, applied in coatings and other directions, can solve the problems of general mechanical properties, soft paint layer strength, toughness, wear resistance and weak acid resistance, etc., to achieve good dispersion, reduced VOC volatilization, and excellent toughness Effect

Pending Publication Date: 2019-11-05
付江辉
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the toughness, abrasion resistance and acid resistance of water-based paints with acrylic acid as the main component are generally weak, the strength of the paint layer is soft, the mechanical properties are average, and engineering construction is easy to cause defects, which limits its further application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A water-based environmental protection paint with good performance and a preparation method thereof are prepared from the following raw materials in parts by weight:

[0035] 60 parts of polyurethane modified acrylic latex;

[0036] 20 parts of alkylated modified fumed white carbon black;

[0037] 5 parts of aminopropylamine dioleate;

[0038] 5 parts of polyvinylpyrrolidone;

[0039] 3 parts of polyvinyl butyral;

[0040] 3 parts of diacetone alcohol;

[0041] 1 part of simethicone;

[0042] 1 part of tributyl phosphate;

[0043] 20 parts of water.

[0044] The preparation method of above-mentioned water-based environmental protection paint comprises the following steps:

[0045] (1) Preparation of acrylic acid-terminated polyurethane:

[0046] Add 2.4kg of N-methylpyrrolidone, 0.96kg of isophorone diisocyanate and 0.8kg of polycaprolactone diol to the reaction kettle in turn, stir evenly, add 4.2g of dibutyltin dilaurate catalyst, and react at 60°C After 1 ho...

Embodiment 2

[0053] A water-based environmental protection paint with good performance and a preparation method thereof are prepared from the following raw materials in parts by weight:

[0054] 70 parts of polyurethane modified acrylic latex;

[0055] 25 parts of alkylated modified fumed white carbon black;

[0056] 6 parts of aminopropylamine dioleate;

[0057] 6 parts of polyvinylpyrrolidone dispersant;

[0058] 4 parts of polyvinyl butyral;

[0059] 4 parts of diacetone alcohol leveling agent;

[0060] 2 parts of simethicone;

[0061] 2 parts of tributyl phosphate;

[0062] 26 parts of water.

[0063] The preparation method of above-mentioned water-based environmental protection paint comprises the following steps:

[0064] (1) Preparation of acrylic acid-terminated polyurethane:

[0065] Add 2.4kg of N-methylpyrrolidone, 1.0kg of isophorone diisocyanate and 0.8kg of polycaprolactone diol to the reaction kettle in turn, stir evenly, add 8.4g of dibutyltin dilaurate catalyst, and ...

Embodiment 3

[0073] A water-based environmental protection paint with good performance and a preparation method thereof are prepared from the following raw materials in parts by weight:

[0074] 80 parts of polyurethane modified acrylic latex;

[0075] Alkylation modified fumed silica 30 parts;

[0076] 10 parts of aminopropylamine dioleate;

[0077] 10 parts of polyvinylpyrrolidone dispersant;

[0078] 5 parts of polyvinyl butyral;

[0079] 5 parts of diacetone alcohol leveling agent;

[0080] 3 parts of simethicone;

[0081] 3 parts of tributyl phosphate;

[0082] 20~30 parts of water.

[0083] The preparation method of above-mentioned water-based environmental protection paint comprises the following steps:

[0084] (1) Preparation of acrylic acid-terminated polyurethane:

[0085] Add 2.4kg N-methylpyrrolidone, 1.04kg isophorone diisocyanate and 0.8kg polycaprolactone glycol successively in reactor, add the dibutyltin dilaurate catalyst of 21.2g 0.5% after stirring, 70 After re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to waterborne environment-friendly paint and a preparation method thereof, and belongs to the field of waterborne paint. The waterborne environment-friendly paint is formed by adopting polyurethane modified acrylic latex as a main raw material, adding alkylate modified gas phase method white carbon black, a dispersing agent, a flatting agent and a defoaming agent and dispersing them in water, and has the excellent tenacity, abrasion resistance, acid resistance and hardness. The adopted alkylate modified gas phase method white carbon black has the thickening and reinforcing effects, and is good in dispersibility. The adopted waterborne amine curing agent has the functions of an emulsifier and a curing agent, and can be mixed with other components to obtain the stable waterborne paint system. The waterborne environment-friendly paint obviously lower VOC volatilization, and transition to the environment-friendly paint from a traditional solvent type paint is achieved, in accordance with the environment-friendly development trend. The preparation method is simple, feasible and good in stability and repeatability and easily achieves industrial production.

Description

technical field [0001] The invention relates to a preparation method of water-based paint, in particular to a water-based environmental protection paint and a preparation method thereof, belonging to the field of water-based paint. Background technique [0002] Paint refers to the resin paint used on wooden furniture, which is divided into two types: water-soluble and oil-soluble. With the continuous progress of society, environmental protection has attracted more and more attention from the world, and people's awareness of environmental protection has also been continuously strengthened. Due to global warming and the destruction of the ozone layer, worldwide industrial environmental protection requirements are getting higher and higher. There will be a large amount of volatile organic solvents in the construction process of oil-soluble paint, which will be discharged into the atmosphere during use, which not only damages the environment and endangers people's health, but a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/08C09D7/62C09D7/47C09D7/65C09D7/63C09D7/20C08F283/00C08F220/14
CPCC08F283/008C08L2205/035C09D7/20C09D7/47C09D7/62C09D7/63C09D7/65C09D151/08C08L39/06C08L29/14C08L83/04C08K13/06C08K5/17C08K9/06C08K7/26C08K5/521C08K5/07C08F220/14
Inventor 石新张仲林付江辉
Owner 付江辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com