A kind of phosphating process of steel pipe

A process and steel pipe technology, which is applied in the phosphating process of steel pipes, can solve the problems of high temperature in the processing workshop, large energy consumption, and harsh working environment for staff

Active Publication Date: 2021-07-30
浙江丰业集团有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the above technical solution, the phosphating process needs to be carried out under the heating condition of 50-75°C. On the one hand, it consumes a lot of energy, and on the other hand, it leads to a higher temperature in the processing workshop, which makes the working environment of the staff worse. ,Room for improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of phosphating process of steel pipe
  • A kind of phosphating process of steel pipe
  • A kind of phosphating process of steel pipe

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A phosphating process for steel pipes, such as figure 1 shown, including the following steps:

[0043] S1, degreasing and derusting treatment;

[0044] S2, washing with water;

[0045] S3, phosphating treatment;

[0046] S4, dry;

[0047] In terms of parts by weight, the components of each liter of phosphating solution are shown in Table 1, and the pH is adjusted to 2.0 with ammonia water.

[0048] Wherein, the phosphating aid adopts citric acid.

Embodiment 2

[0050] The difference from Example 1 is that, in terms of parts by weight, the components of each liter of phosphating solution are shown in Table 1, and ammonia water is used to adjust the pH to 3.0.

Embodiment 3

[0052] The difference from Example 1 is that, in terms of parts by weight, the components of each liter of the phosphating solution are shown in Table 1, and ammonia water is used to adjust the pH to 3.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a steel pipe phosphating process, which relates to a steel pipe treatment process, which comprises the following steps: S1, oil removal and rust removal treatment; S2, water washing; S3, phosphating treatment; S4, drying; Each liter of phosphating solution includes the following components: 30-40 parts of phosphoric acid; 20-25 parts of zinc oxide; 0.2-0.3 parts of sodium chlorate; 0.2-0.3 parts of sodium molybdate; part; 0.5-1.0 part of phosphating aid; adjust the pH to 2.0-3.5 with ammonia water. The invention has the following advantages: the phosphating process can be carried out at normal temperature through the combination and synergy of each component in the system, and the phosphating solution does not contain harmful substances such as nitrate, nitrite, and heavy metals, and has no effect on the operating environment. Pollution, no harm to operators.

Description

technical field [0001] The invention relates to a steel pipe treatment process, more specifically, it relates to a steel pipe phosphating process. Background technique [0002] Phosphating is a process in which chemical and electrochemical reactions form a phosphate chemical conversion film, and the formed phosphate conversion film is called a phosphating film. The purpose of phosphating is mainly to provide protection for the base metal and prevent the metal from being corroded to a certain extent; it is used as a primer before painting to improve the adhesion and anti-corrosion ability of the paint film layer. [0003] The Chinese patent with the publication number CN109013704A discloses a seamless steel pipe manufacturing process, which includes the following steps: a. heating; b. perforation; c. pickling treatment: pickling the pipe material with pickling solution; d. Phosphating treatment: In the step of carrying out phosphating treatment on the pipe material after pic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/42
CPCC23C22/42
Inventor 冯佩姜方武陈晓和
Owner 浙江丰业集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More