Transparent polyimide hardened film with low shrinkage, high hardness and high wear resistance

A transparent polyimide and hardened film technology, applied in polyether coatings, biocide-containing paints, polyurea/polyurethane coatings, etc., can solve problems such as other failures, screen crease damage, volume shrinkage, etc., to achieve Eliminate shrinkage stress, improve hardness, and avoid shrinkage

Active Publication Date: 2019-10-22
新纶光电材料(常州)有限公司
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If it is bent multiple times and used for a long time, after the flexible screen is subjected to multiple compression and tensile stresses, crease damage may appear in the middle of the screen
In addition, circuit boards, components, after being subjected to a lot of bending and non-bending, may also cause damage or other failures during folding
The existing glass panel cannot meet its high frequency requirements, and the transparent polyimide (CPI) film is used to replace the existing glass cover plate because of its good foldability, but polyimide (PI ) The material cannot meet the hardness requirements, and it is necessary to add a hardened film on the surface of the PI film to enhance the hardness
[0003] At present, there are two main problems in the research and development of flexible screen hardening film: one is the contradiction between high hardness and low warpage. Linkage, while conventional vinyl monomers will cause volume shrinkage during the UV curing process, the greater the degree of crosslinking, the more serious the volume shrinkage; the second is the contradiction between high hardness and bendability, through a large number of high-functionality monomers After increasing the cross-linking density to obtain high hardness, the hardened film is usually brittle, and it needs to be properly matched with flexible monomers to improve toughness, and the structure and quantity of flexible monomers will affect whether the hardened film can finally have good bendability. very important

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent polyimide hardened film with low shrinkage, high hardness and high wear resistance
  • Transparent polyimide hardened film with low shrinkage, high hardness and high wear resistance
  • Transparent polyimide hardened film with low shrinkage, high hardness and high wear resistance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention is described in further detail now in conjunction with embodiment.

[0024] The high-functionality urethane acrylate used in this application is 6-functionality urethane acrylate (RJ423), 9-functionality urethane acrylate (RJ4217) and 15-functionality urethane acrylate (RJ4219); The acrylates are BASF's 3.4-functionality polyether acrylate (Laromer LR 8997) and 3.5-functionality polyether acrylate (Laromer PO 94F), and DSM's 4-functionality polyether acrylate (AgiSyn 701) and 4-functionality Polyether acrylate (AgiSyn 703); anti-fingerprint additives are Milo AF-JX 82 perfluoropolyether anti-fingerprint oil and perfluoropolyether anti-fingerprint oil additive HTLC-9633.

[0025] The urethane acrylate used in the comparative example is the 2-functional urethane acrylate (RJ4234) of Liangzhi Chemical; the multi-functional polyether acrylate used in the comparative example is the 2-functional polyether acrylate (AgiSyn 702) of DSM.

[0026] Low shrin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention specifically relates to a transparent polyimide hardened film with low shrinkage, high hardness and high wear resistance, belonging to the technical field of transparent polyimide hardened films. A hardening solution used for preparing the transparent polyimide hardened film comprises, by weight, 50-80 parts of high-functionality urethane acrylate, 10-20 parts of polyfunctional polyether acrylate, 10-20 parts of a flexible monomer, 10-20 parts of a reactive diluent, 0.5-2 parts of a photoinitiator, 0.05-0.2 part of a thermal initiator, 80-150 parts of a good solvent, 2-20 parts of a high-boiling-point poor solvent, 0.05-1 part of an anti-fingerprint agent and 10-30 parts of inorganic nanoparticles. According to the invention, the high-functionality urethane acrylate and the polyfunctional polyether acrylate are adopted to improve the hardness of the hardened film, and the toughness of the hardened film is enhanced by the flexible monomer; and the thermal initiator and thephotoinitiator are added at the same time, and through cooperation between thermal curing and photocuring, shrinkage stress caused by polymerization during curing process is properly released, so warpage is avoided.

Description

technical field [0001] The invention belongs to the technical field of transparent polyimide cured film, in particular to a transparent polyimide cured film with low shrinkage, high hardness and high wear resistance. Background technique [0002] Curved screen technology has been widely valued and sought after by consumers and the industry in recent years. In the future, with the continuous development and improvement of fixed-curvature curved screen technology, flexible touch screens that can be bent arbitrarily will become an important development direction. Although the flexible screen can be bent, if it is bent frequently, it will have the same fatigue problem as metal paper. If it is bent multiple times and used for a long time, the flexible screen may be damaged by creases in the middle of the screen after being subjected to multiple compression and tensile stresses. In addition, circuit boards, components, after being subjected to a lot of bending and non-bending, m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D171/00C09D7/20C09D5/16C09D7/61C08J7/04C08L79/08
CPCC09D175/14C09D7/20C09D5/1687C08K2201/011C08K2003/2227C08J2379/08C08J2475/14C08J7/0427C08L71/00C08K3/36C08K3/22
Inventor 王权
Owner 新纶光电材料(常州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products