Alkali-containing alumina silicate glass, and product, strengthening method and application thereof

A technology of silicate glass and glass products, applied in the field of flat glass manufacturing, can solve problems such as affecting the display effect of display products, scribing sharp objects, endangering the service life, etc. The effect of layer compression depth

Active Publication Date: 2019-10-11
CAIHONG GRP SHAOYANG SPECIAL GLASS CO LTD
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of modern display technology, a large number of flat panel display products such as LCD monitors, cash machine protection screens, touch screen information inquiry machines and media advertising players have emerged and entered our daily lives. Some electronic display products often encounter some harsh problems. The use environment, such as sharp object scoring, in addition to the impact of human damage
In addition, some touch screens and handheld computers often have some dangerous operations, such as writing, scratching and impacting on the display screen with fingers, electronic pens, signature pens or even keys, which will cause damage to the screen of electronic display products and surface scratches. Injury, affecting the display effect of display products, and even endangering their service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alkali-containing alumina silicate glass, and product, strengthening method and application thereof
  • Alkali-containing alumina silicate glass, and product, strengthening method and application thereof
  • Alkali-containing alumina silicate glass, and product, strengthening method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The present invention will be further described in detail below in conjunction with specific embodiments, which are explanations of the present invention rather than limitations.

[0025] A chemically strengthenable alkali-containing aluminosilicate glass of the present invention, including flat glass and glass products, including SiO in mass percentage 2 52%~68%, Al 2 o 3 10%~23%,Na 2 O 8%~13%, Li 2 O 0~6%, P 2 o 5 2%~5%, ZrO 2 0~5%, ZnO 0~3%; addition of SnO can also be included 2 , by mass percent SnO 2 0.1% to 1%.

[0026] The function and specific content of each component in the above-mentioned alkali-containing aluminosilicate glass are discussed below, and the unit of content is mass percent.

[0027] SiO 2 : 52% to 68%.

[0028] SiO 2 It is a necessary component to constitute the glass skeleton. The higher the content, the better the chemical durability of the glass and the higher the mechanical strength of the glass. In addition, since SiO 2 I...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to alkali-containing alumina silicate glass, and a product, a strengthening method and application thereof. The alkali-containing alumina silicate glass is sequentially subjectedto ion exchange in a salt bath of sodium nitrate and potassium nitrate at 350-450 DEG C for two times to obtain the chemically strengthened alumina silicate glass product. The glass comprises 52-68%of SiO2, 10-23% of Al2O3, 8-13% of Na2O, 0-6% of Li2O, 2-5% of P2O5, 0-5% of ZrO2 and 0-3% of ZnO. The surface pressure stress of the chemically strengthened alumina silicate glass product is greaterthan 600 MPa, the stress layer compression depth thereof is greater than 50 micrometers, the bending strength thereof is greater than 600 MPa, and the Vickers hardness thereof is greater than 600 MPa.The chemically strengthened alkali-containing alumina silicate glass product is applied to an electronic device.

Description

technical field [0001] The invention relates to the technical field of flat glass manufacturing, in particular to an alkali-containing aluminosilicate glass and its product, strengthening method and application. Background technique [0002] With the development of modern display technology, a large number of flat panel display products such as LCD monitors, cash machine protection screens, touch screen information inquiry machines and media advertising players have emerged and entered our daily lives. Some electronic display products often encounter some harsh problems. The environment of use, such as sharp object scoring, in addition to the impact of man-made damage. In addition, some touch screens and handheld computers often have some dangerous operations, such as writing, scratching and impacting on the display screen with fingers, electronic pens, signature pens or even keys, which will cause damage to the screen of electronic display products and surface scratches. d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C21/00C03C3/097C03C1/00
CPCC03C21/002C03C3/097C03C1/004
Inventor 王志安薛新建冯勃
Owner CAIHONG GRP SHAOYANG SPECIAL GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com