A core-shell type surface sizing enhancer and preparation method thereof

A surface sizing and strengthening agent technology, applied in the direction of water repellent addition, papermaking, coating, etc., can solve the problems of insufficient crosslinking network, low solid content of emulsion, and easy separation of chemical crosslinking, so as to improve film formation performance, improvement of surface strength, and improvement of flexibility

Active Publication Date: 2021-11-23
ZHEJIANG HENGDA NEW MATERIAL CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, some studies have prepared cationic modified alkyd / acrylic resins by chemical modification methods, but there are still low solid content in the emulsion, insufficient crosslinking network, and good chemical crosslinking between alkyd resin and acrylic resin. As a result, it is easy to split into other problems, and the research on introducing vinyl monomers into alkyd molecular segments and obtaining core-shell emulsions through step-by-step polymerization has basically not been reported.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A core-shell type surface sizing enhancer and preparation method thereof
  • A core-shell type surface sizing enhancer and preparation method thereof
  • A core-shell type surface sizing enhancer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] A preparation method of a core-shell type surface sizing enhancer of the present invention comprises the following steps:

[0037] 1) mix the alkyd resin and diglyme in a mass ratio of 1:0.3-1 to obtain the alkyd resin diglyme solution;

[0038] 2) Heat up the alkyd resin diethylene glycol dimethyl ether solution (including 100 parts of alkyd resin) to 50-75° C., add 15-30 parts of isocyanate monomer, and react for 1-2 hours. Then add 1-3 parts of hydroxyl-containing vinyl monomers into the reaction solution, and continue the reaction for 1 hour to obtain component A.

[0039] 3) Mix 1-5 parts of vinyl monomers containing long side chain groups, 3-5 parts of vinyl monomers containing hydroxyl groups, 0.5-2 parts of vinyl monomers containing epoxy groups, 1-3 parts of ring Oxygen resin, 10-20 parts of other types of vinyl monomers and 1-3 parts of oil-soluble initiator are mixed to obtain mixed liquid B.

[0040] 4) Mix 1 / 2 of component A, 2-10 parts of anionic monomer...

Embodiment 1

[0058] 1) Mix alkyd resin (oleic acid iodine value 155, acid value 18, mass fraction 98%) and diglyme in a mass ratio of 1:0.5 to obtain alkyd resin diglyme solution;

[0059] 2) The alkyd resin diethylene glycol dimethyl ether solution (including 100 parts of alkyd resin) was heated to 60° C., 17.5 parts of MDI trimer was added, and reacted for 1 hour. Then, 1.5 parts of hydroxyethyl methacrylate was added into the reaction liquid, and the reaction was continued for 1 hour to obtain component A.

[0060] 3) 2 parts of vinyl monomer of isooctyl methacrylate, 3 parts of hydroxypropyl methacrylate, 1 part of glycidyl acrylate, 1.5 parts of epoxy resin E44, 12 parts of styrene and 2 parts of benzene peroxide Formyl is mixed to obtain a mixed liquid B.

[0061] 4) Mix 1 / 2 of component A, 4 parts of acrylic acid, 2 parts of isooctyl methacrylate, 2 parts of hydroxypropyl methacrylate, 1.5 parts of glycidyl acrylate, 2 parts of epoxy resin E44, 1.2 parts of ethylene Tripropoxysil...

Embodiment 2

[0066] 1) Mix alkyd resin (oleic acid iodine value 180, acid value 20, mass fraction 99%) and diglyme in a mass ratio of 1:0.7 to obtain alkyd resin diglyme solution;

[0067] 2) The alkyd resin diethylene glycol dimethyl ether solution (including 100 parts of alkyd resin) was heated to 70° C., 20 parts of HDI trimer was added, and reacted for 1.5 hours. Then, 3 parts of hydroxypropyl acrylate were added into the reaction solution, and the reaction was continued for 1 hour to obtain component A.

[0068] 3) Mix 4 parts of hexyl methacrylate, 5 parts of hydroxyethyl acrylate, 1.6 parts of glycidyl methacrylate, 2 parts of epoxy resin E51, 15 parts of methyl methacrylate and 2 parts of azobisisobutyronitrile Mix to obtain Mixture B.

[0069] 4) Mix 1 / 2 of component A, 5 parts of methacrylic acid, 3 parts of butyl methacrylate, 3 parts of hydroxyethyl acrylate, 1.5 parts of glycidyl acrylate, 2 parts of epoxy resin E44, 2 parts of vinyl Trimethoxysilane, 18 parts of styrene an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a core-shell type surface sizing enhancer and a preparation method thereof. Firstly, isocyanate is added to a diethylene glycol dimethyl ether solution of an alkyd resin, and after the reaction, a vinyl monomer containing a hydroxyl group is added, and then reacted. Finally, a polymerizable alkyd resin component containing a vinyl segment is obtained; then the polymerizable alkyd resin component is distributed and polymerized; finally, an organic acid and a drier are added to the system, and after fully reacting, add water to disperse to obtain a core Shell type surface sizing enhancer. The self-crosslinking and interpenetrating network chemical structure of multi-components and multi-active points of the product of the present invention can realize the unity of hydrophobic performance, adhesive performance and film-forming performance, and solve the problems of poor water resistance, poor surface strength, lint and powder falling of paper, etc. Common technical issues in the industry, it is used for paper surface sizing, which can greatly improve the surface strength, water resistance and folding resistance of paper.

Description

technical field [0001] The invention relates to the field of paper surface sizing agents, in particular to a core-shell type surface sizing enhancer and a preparation method thereof. Background technique [0002] Alkyd resin has excellent bonding strength and film-forming properties, and has been used in the field of coatings for a long time, but it is rarely used in paper surface sizing agents. Acrylic resin has long been used in the development and application of paper surface sizing agents due to its good waterproof performance, weather resistance and mechanical strength. At present, some studies have prepared cationic modified alkyd / acrylic resins by chemical modification methods, but there are still low solid content in the emulsion, insufficient crosslinking network, and good chemical crosslinking between alkyd resin and acrylic resin. As a result of its easy separation and other problems, the research on introducing vinyl monomers into alkyd molecular segments and ob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F285/00C08F220/06C08F220/18C08F220/20C08F220/32D21H19/20D21H21/16
CPCC08F285/00D21H19/20D21H21/16C08F220/06
Inventor 伊财富杨菊红徐冰丁济正张海波
Owner ZHEJIANG HENGDA NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com