Cold-construction non-curable rubber modified asphalt coating for waterproofing and preparation method thereof

A technology of asphalt waterproof coating and non-curing rubber, applied in asphalt coatings, unspecified rubber coatings, coatings, etc., can solve the problems of temperature resistance, low fluidity and high viscosity, use restrictions, high pollution, etc. Viscosity, solve difficult dispersion, improve the effect of flow properties

Inactive Publication Date: 2019-08-16
山东省金帅防水材料有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to its temperature resistance, low fluidity and high viscosity, the spraying of non-curing spray rubber asphalt waterproof coating must be carried out at a high temperature of 180-220 ° C, but high temperature construction is accompanied by high energy consumption and a large amount of volatilization due to high temperature High pollution caused by sulfur, carbon, nitrate and other toxic gases
Therefore above-mentioned non-curing spraying rubber asphalt waterproof coating is restricted in the engineering of roofing and underground waterproofing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: A cold construction non-curing rubber asphalt waterproof coating, its raw materials are counted as follows in terms of mass parts: 25 parts of asphalt, 15 parts of thermoplastic rubber, 23 parts of solvent, 10 parts of softening oil, 1.5 parts of viscosity regulator, phosphating 9 parts of nano-silica, 4 parts of lauryl alcohol fat, 16 parts of calcium carbonate powder, and 1 part of mineral fiber.

[0023] The pitch has a penetration of 150, a softening point of 34° C., and a ductility of more than 100 cm.

[0024] Described solvent is to be selected from xylene, 120# solvent naphtha.

[0025] The viscosity regulator is a sulfonated styrene-maleic anhydride copolymer.

[0026] The mineral fiber is selected from light asbestos powder.

[0027] Preparation method, concrete steps are as follows:

[0028] (1) Weigh asphalt, solvent, softening oil, viscosity modifier, phosphating nano-silica, lauryl alcohol fat, calcium carbonate powder and mineral fiber in...

Embodiment 2

[0033] A cold construction non-curing rubber asphalt waterproof coating, its raw materials are calculated in parts by mass: 20 parts of asphalt, 10 parts of thermoplastic rubber, 15 parts of solvent, 8 parts of softening oil, 1 part of viscosity regulator, 8 parts of phosphating nano silicon oxide 1 part, 3 parts of lauryl alcohol fat, 15 parts of calcium carbonate powder, 1 part of mineral fiber.

[0034] The pitch has a penetration of 170, a softening point of 44° C., and a ductility of more than 100 cm.

[0035] The solvent is a mixture of 120# solvent naphtha and 200# solvent naphtha.

[0036] The viscosity modifier includes a mixture of lignosulfonate and polypropylene resin in a ratio of 3:1.

[0037] The mineral fiber is asbestos.

[0038] Preparation method, concrete steps are as follows:

[0039] (1) Weigh asphalt, solvent, softening oil, viscosity modifier, phosphating nano-silica, lauryl alcohol fat, calcium carbonate powder and mineral fiber in proportion for us...

Embodiment 3

[0044] A cold construction non-curing rubber asphalt waterproof coating, its raw materials are calculated in parts by mass: 40 parts of asphalt, 15 parts of thermoplastic rubber, 30 parts of solvent, 12 parts of softening oil, 2.5 parts of viscosity regulator, 10 parts of phosphating nano-silicon oxide 3-6 parts of lauryl alcohol fat, 30 parts of calcium carbonate powder, 3 parts of mineral fiber,

[0045] Preparation method, concrete steps are as follows:

[0046] (1) Weigh asphalt, solvent, softening oil, viscosity modifier, phosphating nano-silica, lauryl alcohol fat, calcium carbonate powder and mineral fiber in proportion for use;

[0047] (2) Mix the thermoplastic rubber with an appropriate amount of solvent, stir at room temperature until completely dissolved;

[0048] (3) Mix and heat asphalt, viscosity modifier and remaining solvent to 120°C, stir and cool down to 90°C after complete dissolution;

[0049] (4) Add the rubber-solvent premix prepared in step (2), miner...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a cold-construction non-curable rubber modified asphalt coating for waterproofing and a preparation method thereof, and belongs to the technical field of chemical engineering.The coating composition is prepared from the following raw materials in parts by mass: 20-40 parts of asphalt, 10-15 parts of thermoplastic rubber, 15-30 parts of a solvent, 8-12 parts of softening oil, 1-2.5 parts of a viscosity regulator, 8-10 parts of phosphated nano silicon oxide, 3-6 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 15-30 parts of calcium carbonate powder and 1-3 parts of mineral fibers. According to the invention, the softening oil, the phosphated nano silicon oxide and the 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate are added into the waterproof coating tomodify the waterproof coating, so that viscosity of the coating is reduced, the flowing property of the coating is improved, the coating can be sprayed under a relatively low-temperature condition of60 DEG C or below, and high energy consumption and high pollution caused by high-temperature spraying are avoided. The coating can be widely applied to waterproofing, dampproofing and seepage proofingof important projects such as high-speed rails, subways, high ways, airports, underground pipe galleries, bridges, tunnels and the like.

Description

technical field [0001] The invention belongs to the technical field of chemical industry and relates to a cold applied non-curing rubber asphalt waterproof coating and a preparation method thereof. Background technique [0002] Non-curable Rubber Modified Asphalt Coating for Waterproofing (Non-curable Rubber Modified Asphalt Coating for Waterproofing) is a new type of waterproof material with rubber powder, asphalt and special additives as the main raw materials. The state of the body, the creep is better. Due to its state in engineering application, it has the characteristics of "permeable", does not cure, can be used in various difficult construction conditions, and can adapt to lower temperatures. Due to its "pervasive" characteristics, the sealing effect is better, which solves the problem of water channeling. [0003] Due to its temperature resistance, low fluidity and high viscosity, the spraying of non-curing spray rubber asphalt waterproof coating must be carried o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D121/00C09D191/00C09D7/65C09D7/61C09D7/63
CPCC08K2003/265C08K2201/011C08L2201/08C08L2205/035C09D7/61C09D7/63C09D7/65C09D7/70C09D195/00C08L21/00C08L91/00C08L35/06C08L23/12C08L97/005C08K13/04C08K7/12C08K5/103C08K3/34C08K3/26
Inventor 郑国令
Owner 山东省金帅防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com