Terahertz silica gel material
A technology of terahertz and silica gel, which is applied in the field of terahertz silica gel materials, can solve problems such as not being suitable for summer or high temperature environments, affecting the mechanical properties and softness of silica gel, reducing wear resistance and comfort, and achieving improved chemical properties. Reactivity, improvement of tear strength and water repellency, effect of improving slipperiness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0034] A terahertz silica gel material, which is made of the following components in parts by weight: 80 parts of silica gel main material, 4 parts of terahertz mineral powder, 2 parts of magnetic graphene, 8 parts of hollow porous carbon nanospheres, negative ion powder 2 parts, 1 part of nano silver, 4 parts of hydroxyl silicone oil, 8 parts of white carbon black, 2 parts of high vinyl silicone oil, 13 parts of EVA resin, 10 parts of spherical alumina, 0.5 parts of KH-550 silane coupling agent, dimethyl 1 part of dimethoxysilane, 0 part of pigment, 0.2 part of vulcanizing agent, and 0.1 part of accelerator.
[0035] Further, the terahertz mineral powder is medical stone capable of emitting terahertz waves, orthoclase, and meteorite in a weight ratio of 1:1:2.
[0036] Further, the preparation method of the magnetic graphene is to add graphite oxide into ethylene glycol and ultrasonically peel off to obtain a graphene oxide dispersion, then add ferric chloride hexahydrate, stir...
Embodiment 2
[0049] A terahertz silica gel material, which is made of the following components in parts by weight: 90 parts of silica gel main material, 7 parts of terahertz mineral powder, 4 parts of magnetic graphene, 10 parts of hollow porous carbon nanospheres, negative ion powder 4 parts, 3 parts of nano silver, 5 parts of hydroxyl silicone oil, 17 parts of white carbon black, 3 parts of high vinyl silicone oil, 16 parts of EVA resin, 18 parts of spherical alumina, 0.9 parts of KH-550 silane coupling agent, dimethyl 2 parts of dimethoxysilane, 1 part of pigment, 0.3 part of vulcanizing agent, and 0.6 part of accelerator.
[0050] Further, the terahertz mineral powder is capable of emitting terahertz allophane and germanium ore in a weight ratio of 1:1.
[0051] Further, the preparation method of the magnetic graphene is to add graphite oxide into ethylene glycol and ultrasonically peel off to obtain a graphene oxide dispersion, then add ferric chloride hexahydrate, stir and dissolve, ...
Embodiment 3
[0064] A terahertz silica gel material, which is made of the following components in parts by weight: 100 parts of silica gel main material, 9 parts of terahertz mineral powder, 5 parts of magnetic graphene, 12 parts of hollow porous carbon nanospheres, negative ion powder 5 parts, 4 parts of nano silver, 6 parts of hydroxyl silicone oil, 23 parts of white carbon black, 5 parts of high vinyl silicone oil, 19 parts of EVA resin, 24 parts of spherical alumina, 1.2 parts of KH-550 silane coupling agent, dimethyl 3 parts of dimethoxysilane, 2 parts of pigment, 0.5 part of vulcanizing agent, and 1.5 parts of accelerator.
[0065] Further, the terahertz mineral powder is medical stone, orthoclase, meteorite, Guiyang stone, allophane, wood fish stone, tourmaline, and germanium ore that can emit terahertz waves. The weight ratio is 1:1. :1:1:1:1:1:1.
[0066] Further, the preparation method of the magnetic graphene is to add graphite oxide into ethylene glycol and ultrasonically peel...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
tensile strength at break | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com