Octadecanol methyl propionate, preparation method thereof, water-soluble thickener and preparation method of water-soluble thickener
A technology of alcohol methyl propionate and water-soluble thickener, applied in the field of thickener, can solve problems such as poor adaptability, inability to meet oil field development, enhanced oil recovery, inability to meet application requirements, etc., and achieves good viscosity, The method is simple and easy to implement and the effect of the method is simple
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] Example 1, the octadecyl alcohol methyl propionate is obtained according to the following preparation method: first step, first prepare stearyl alcohol and methacrylic acid according to the molar ratio of 1:1, and then add the prepared stearyl alcohol to the reaction vessel stearyl alcohol, and heat stearyl alcohol to 45°C to 55°C, then continue to add the prepared methacrylic acid to the reaction vessel under stirring and stir evenly; in the second step, continue to add A sulfuric acid solution with 1.1% of the total mass of stearyl alcohol and methacrylic acid, slowly warming up to 85°C to 95°C, and reacting for 4 hours to 6 hours; the third step, then continue to add the mass of stearyl alcohol and methacrylic acid to the reaction vessel The total amount of 1% nonylphenol polyoxyethylene ether is reacted for 40 minutes to 70 minutes; the fourth step, after the completion of the third step reaction, cool the material in the reaction vessel to below 50°C to obtain stear...
Embodiment 2
[0017] Example 2, the octadecyl alcohol methyl propionate is obtained according to the following preparation method: first step, first prepare stearyl alcohol and methacrylic acid according to the molar ratio of 1:1, and then add the prepared stearyl alcohol into the reaction vessel stearyl alcohol, and heat stearyl alcohol to 45°C or 55°C, then continue to add the prepared methacrylic acid to the reaction vessel under stirring and stir evenly; the second step, then continue to add to the reaction vessel A sulfuric acid solution of 1.1% of the total mass of stearyl alcohol and methacrylic acid, slowly warming up to 85°C or 95°C, and reacting for 4 hours or 6 hours; the third step, then continue to add the mass of stearyl alcohol and methacrylic acid to the reaction vessel The total amount of 1% nonylphenol polyoxyethylene ether is reacted for 40 minutes or 70 minutes; the fourth step, after the completion of the third step reaction, cool the material in the reaction vessel to b...
Embodiment 3
[0018] Embodiment 3, the water-soluble thickener prepared by the stearyl methyl propionate described in embodiment 1 or embodiment 2, its raw materials include by weight percentage: 3% to 20% acrylamide, 2% to 20% 2-acrylamido-2-methylpropanesulfonic acid, 3% to 15% stearyl methyl propionate, 1% to 10% cetyltrimethylammonium chloride, 0.01% to 0.2% sodium bisulfite, 0.02% to 0.4% ammonium persulfate, 0% to 0.002% disodium edetate, 0% to 6% urea, 3% to 10% carbonic acid Sodium and balance deionized water.
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com