A kind of preparation method of epoxy zinc olefin heavy-duty anti-corrosion coating

A heavy-duty anti-corrosion and epoxy zinc technology, which is applied in the direction of anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems that affect the ability of the paint film to resist water penetration, reduce the utilization rate of zinc powder, and difficult to disperse the coating, etc., to achieve Good physical shielding effect, improved interfacial compatibility, and low zinc powder content

Active Publication Date: 2021-05-28
SHANGHAI ZHENHUA HEAVY IND CHANGZHOU COATINGS CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, both graphene and zinc powder have a large specific surface area, are difficult to disperse directly in the coating, and are prone to agglomeration, which will affect the ability of the paint film to resist water penetration, and the metal zinc near the surface and interface of the coating The powder will be consumed, reducing the utilization rate of zinc powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of epoxy zinc olefin heavy-duty anti-corrosion coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Step 1: Preparation of modified graphene-zinc composite powder

[0027] (1) According to the mass ratio of 1:25, graphene and zinc powder were weighed respectively, added to the ball mill jar successively, and ethanol was added, the ball mill jar was evacuated and filled with nitrogen, and the ball milled under the protection of nitrogen atmosphere for 2h and then discharged to obtain Slurry, the slurry is placed in a vacuum drying oven to dry, and the graphene-zinc composite powder is obtained after drying completely;

[0028] (2) Weigh 5g of graphene-zinc composite powder into a three-necked flask, add 30g of toluene diisocyanate and 80g of isopropanol, ultrasonically disperse for 15min under nitrogen protection, heat to 90°C after dispersion, stir for 1h, and filter with suction , put the filter residue into a vacuum drying oven, and dry it at 50° C. to obtain a modified graphene-zinc composite powder.

[0029] Step 2: Preparation of epoxy zincene heavy-duty anti-co...

Embodiment 2

[0035] Step 1: Preparation of modified graphene-zinc composite powder

[0036] (1) According to the mass ratio of 1:27, graphene and zinc powder were weighed respectively, added to the ball mill jar successively, and ethanol was added, the ball mill jar was evacuated and filled with nitrogen, and the ball mill was discharged for 3 hours under the protection of nitrogen atmosphere to obtain Slurry, the slurry is placed in a vacuum drying oven to dry, and the graphene-zinc composite powder is obtained after drying completely;

[0037] (2) Weigh 7g of graphene-zinc composite powder into a three-necked flask, add 40g of toluene diisocyanate and 100g of isopropanol, ultrasonically disperse for 17min under the protection of nitrogen, heat to 95°C after dispersion, stir for 1.5h, pump Filter to obtain the filter residue, put it in a vacuum drying oven, and dry it at 50° C. to obtain a modified graphene-zinc composite powder.

[0038] Step 2: Preparation of epoxy zincene heavy-duty a...

Embodiment 3

[0044] Step 1: Preparation of modified graphene-zinc composite powder

[0045] (1) According to the mass ratio of 1:30, graphene and zinc powder were weighed respectively, added to the ball mill jar successively, and ethanol was added, the ball mill jar was evacuated and filled with nitrogen, and the ball mill was discharged for 4 hours under the protection of nitrogen atmosphere to obtain Slurry, the slurry is placed in a vacuum drying oven to dry, and the graphene-zinc composite powder is obtained after drying completely;

[0046] (2) Weigh 10g of graphene-zinc composite powder into a three-necked flask, add 50g of toluene diisocyanate and 120g of isopropanol, ultrasonically disperse for 20min under nitrogen protection, heat to 100°C after dispersion, stir for 2h, and filter with suction , put the filter residue into a vacuum drying oven, and dry it at 50° C. to obtain a modified graphene-zinc composite powder.

[0047] Step 2: Preparation of epoxy zincene heavy-duty anti-cor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of epoxy zincene heavy-duty anti-corrosion paint, which belongs to the technical field of paint preparation. In the present invention, graphene and zinc powder are first ground and compounded to obtain graphene-zinc composite powder, and the surface of graphene-zinc composite powder is modified by toluene diisocyanate, which can effectively prevent graphene and zinc powder from being deposited on the resin The reunion in the medium greatly improves the dispersibility of the composite powder in the resin, thereby fully exerting the anticorrosion effect of the graphene composite powder and enhancing the anticorrosion of the epoxy resin coating. Component A is obtained after mixing ethylene-zinc composite powder and other components, and the curing agent is used as component B. After mixing, epoxy zinc ene heavy-duty anti-corrosion coating is obtained. The coating has good flexibility, good anti-corrosion performance, and the salt spray resistance time is long. Reach more than 3000h.

Description

technical field [0001] The invention belongs to the technical field of paint preparation, and in particular relates to a preparation method of epoxy zincene heavy-duty anti-corrosion paint. Background technique [0002] In recent years, the research on heavy-duty anti-corrosion coatings has been very rapid. On the basis of traditional conventional anti-corrosion coatings, many varieties with excellent performance have been developed. Among them, the commonly used heavy-duty anti-corrosion coating is epoxy zinc-rich coating. Epoxy zinc-rich coating is a heavy-duty anti-corrosion coating with excellent corrosion resistance, which is widely used in the field of metal heavy-duty anti-corrosion. Zinc in epoxy zinc-rich paint is a sacrificial anode, and its content in the paint is usually greater than 70%. However, due to the high content of zinc powder in the coating, the coating is easily porous and the adhesion is reduced, and the zinc-rich coating produces more zinc salts wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D5/10C09D7/61C09D7/62C09D7/63C09D7/65
Inventor 杨敏辉卞庆娅刘政超崔国鹏
Owner SHANGHAI ZHENHUA HEAVY IND CHANGZHOU COATINGS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com