A kind of environment-friendly anti-slip ultra-thin sealing layer material and preparation method thereof

An environmentally friendly, layered material technology, applied in coatings, anti-corrosion coatings, asphalt coatings, etc., can solve the problems of difficulty in meeting the requirements of versatility, long closed construction time, high sealing cost, and achieve short construction and open traffic time. Good adhesion and good peeling resistance

Active Publication Date: 2021-01-26
中山市易路美新材料科技有限公司 +1
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Epoxy asphalt sealant is expensive and takes a long time to seal
[0004] At present, the existing preventive maintenance materials for asphalt pavement have single functions and obvious shortcomings, and it is difficult to meet the multifunctional requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of environment-friendly anti-slip ultra-thin sealing layer material and preparation method thereof
  • A kind of environment-friendly anti-slip ultra-thin sealing layer material and preparation method thereof
  • A kind of environment-friendly anti-slip ultra-thin sealing layer material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] Preparation of High Viscosity Special Composite Modified Asphalt Emulsion

[0056] Weigh each component according to the formula quantity, base asphalt 55%, SBS 1%, softening oil 3%, tackifier 0.5%, cationic emulsifier 1.3%, hydrochloric acid 0.5%, water 36.7%, SBR styrene-butadiene latex 2%.

[0057] (1) Preparation of SBS modified asphalt: Add base asphalt and softened oil to the swelling tank, stir at 185°C to 195°C for 20 minutes to ensure uniform mixing; add SBS and tackifier for swelling under stirring, the time is 30 Minutes, temperature 185 ℃ ~ 195 ℃; after swelling, carry out colloid mill shearing (determine whether to perform secondary or multiple shearing according to the shearing effect); pump the sheared modified asphalt to the development tank for development, and the time is 1.5 ~ 2 hours, the temperature is 180°C, and the modified asphalt for emulsification is made after the development is completed.

[0058] (2) Preparation of high-viscosity special co...

Embodiment 2

[0070] Preparation of High Viscosity Special Composite Modified Asphalt Emulsion

[0071] Weigh each component according to the formula quantity, base asphalt 58%, SBS 2%, softening oil 4%, tackifier 0.7%, cationic emulsifier 1.5%, hydrochloric acid 0.8%, water 30.5%, SBR styrene-butadiene latex 2.5%.

[0072] (1) Preparation of SBS modified asphalt: Add base asphalt and softened oil to the swelling tank, stir at 185°C to 195°C for 20 minutes to ensure uniform mixing; add SBS and tackifier for swelling under stirring, the time is 30 Minutes, temperature 185 ℃ ~ 195 ℃; after swelling, carry out colloid mill shearing (determine whether to perform secondary or multiple shearing according to the shearing effect); pump the sheared modified asphalt to the development tank for development, and the time is 1.5 ~ 2 hours, the temperature is 180°C, and the modified asphalt for emulsification is made after the development is completed.

[0073] (2) Preparation of high-viscosity special ...

Embodiment 3

[0085] Preparation of High Viscosity Special Composite Modified Asphalt Emulsion

[0086] Weigh each component according to the formula quantity, base asphalt 60%, SBS 3%, softening oil 5%, tackifier 1%, cationic emulsifier 1.8%, hydrochloric acid 1%, water 25.2%, SBR styrene-butadiene latex 3%.

[0087] (1) Preparation of SBS modified asphalt: Add base asphalt and softened oil to the swelling tank, stir at 185°C to 195°C for 20 minutes to ensure uniform mixing; add SBS and tackifier for swelling under stirring, the time is 30 Minutes, temperature 185 ℃ ~ 195 ℃; after swelling, carry out colloid mill shearing (determine whether to perform secondary or multiple shearing according to the shearing effect); pump the sheared modified asphalt to the development tank for development, and the time is 1.5 ~ 2 hours, the temperature is 180°C, and the modified asphalt for emulsification is made after the development is completed.

[0088] (2) Preparation of high-viscosity special compos...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
tensile strengthaaaaaaaaaa
freezing pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly anti-skid ultra-thin sealing layer material and a preparation method thereof. The invention solves the problems of water seepage disease, insufficient anti-skid performance, slight pitting and tiny cracks of the asphalt pavement, and provides a stable and durable sealing layer to protect the asphalt pavement, which can lock the aggregate of the original asphalt pavement, repair poor oil, and facilitate construction. The open traffic time is short, the impact on traffic is small, and it has great technical and social significance. The preventive maintenance process of the present invention can not only maintain the service level of the road surface and delay the maintenance time of major and medium repairs, but also save the whole Maintenance costs during the life cycle.

Description

technical field [0001] The invention relates to the technical field of road building materials, in particular to an environment-friendly anti-skid ultra-thin sealing layer material and a preparation method thereof. Background technique [0002] The performance attenuation of the asphalt pavement surface, insufficient anti-skid performance, secondary diseases such as micro-cracks, pockmarks, threshing and water seepage of the pavement seriously affect the service level, driving safety and service life of the pavement, especially for the aging of the pavement caused by ultraviolet rays. The durability of the asphalt pavement is insufficient, and many preventive maintenance processes at this stage cannot solve the problem very well. There is an urgent need for a preventive maintenance process that can solve various minor diseases of asphalt pavement, so as to solve the problem of excessive water seepage coefficient, insufficient skid resistance, Environmentally friendly cold co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D195/00C09D5/08C09D5/14C09D7/61C09D7/65
CPCC08K2201/014C08L2205/035C09D5/08C09D5/14C09D195/005C09D7/61C09D7/65C08L53/02C08L91/00C08L9/08C08L45/00C08L19/003C08L25/14C08K13/02C08K5/47C08K3/346C08K3/36C08K3/34
Inventor 刘威牛洪芝姜万双
Owner 中山市易路美新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com