6082S aluminum alloy sheet for stamping and processing technology thereof

A processing technology, aluminum alloy technology, applied in the field of aluminum alloy processing, can solve problems such as easy to become crack source, difficult to dissolve aluminum matrix, stamping cracking, etc., achieve the effect of improving organizational coordination ability, improving mechanical properties, and reducing the possibility of stamping cracking

Inactive Publication Date: 2019-03-15
TIANJIN ZHONGWANG ALUMINUM IND CO LTD
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, in order to solve the problem that the existing 6082 aluminum alloy has a wide composition range, due to the existence of Fe and Mn elements, micron-sized AlFeSi, AlMnSiFe, and Al are often precipitated during the solidification process. 6 Mn phase, and these coarse primary solidification precipitates are hard and brittle, and it is difficult to dissolve into the aluminum matrix in the subsequent homogenization and solid solution treatment. A kind of 6082S aluminum alloy sheet for stamping and its processing technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 6082S aluminum alloy sheet for stamping and processing technology thereof
  • 6082S aluminum alloy sheet for stamping and processing technology thereof
  • 6082S aluminum alloy sheet for stamping and processing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A processing technology of 6082S aluminum alloy thin plate for stamping, comprising the following steps:

[0032] A. According to the predetermined weight percentage, the ingredients of the above-mentioned 6082S aluminum alloy sheet are put into a melting furnace for melting, and after slag removal and filtration, the molten aluminum is cast into an aluminum alloy ingot;

[0033] B. Cut off the head and tail of the aluminum alloy ingot after melting and casting, perform face milling, and then use a milling machine to mill out the solidified shell layer on the surface of the aluminum alloy ingot;

[0034] C. Place the milled aluminum alloy ingot in a heating furnace for homogenization heat treatment. The process of homogenization heat treatment is: the aluminum alloy ingot is heated to 560 ° C, kept for 8 hours, then cooled to 500 ° C, kept for 2 hours, after heating Immediately after the ingot is released from the furnace, it is hot-rolled into a coil, and the thickness...

Embodiment 2

[0040] A processing technology of 6082S aluminum alloy thin plate for stamping, comprising the following steps:

[0041] A. According to the predetermined weight percentage, the ingredients of the above-mentioned 6082S aluminum alloy sheet are put into a melting furnace for melting, and after slag removal and filtration, the molten aluminum is cast into an aluminum alloy ingot;

[0042] B. Place the melted aluminum alloy ingot in a heating furnace for homogenization heat treatment and cut off the head and tail for face milling. The homogenization heat treatment process is that the melted aluminum alloy ingot is heated to 530°C, kept for 8 hours, and then cooled To 500 ℃, keep warm for 2 hours, and take out;

[0043] C. The aluminum alloy ingot after face milling is hot-rolled into a coil after being released from the furnace, and the thickness of the coil is 7mm;

[0044] D. Cold-roll the hot-rolled coil to the intermediate annealing thickness, wherein the annealing temperatu...

Embodiment 3

[0049] A processing technology of 6082S aluminum alloy thin plate for stamping, comprising the following steps:

[0050] A. According to the predetermined weight percentage, the ingredients of the above-mentioned 6082S aluminum alloy sheet are put into a melting furnace for melting, and after slag removal and filtration, the molten aluminum is cast into an aluminum alloy ingot;

[0051] B. Cut off the head and tail of the aluminum alloy ingot after melting and casting, perform face milling, and then use a milling machine to mill out the solidified shell layer on the surface of the aluminum alloy ingot;

[0052] C. Place the milled aluminum alloy ingot in a heating furnace for homogenization heat treatment. The process of homogenization heat treatment is: the aluminum alloy ingot is heated to 560 ° C, kept for 10 hours, then cooled to 500 ° C, kept for 4 hours, after heating Immediately after the ingot is released from the furnace, it is hot-rolled into a coil, and the thicknes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of aluminum alloy processing, and relates to a 6082S aluminum alloy sheet for stamping and a processing technology thereof. The 6082S aluminum alloy sheetis prepared from the following elements of, in percentage by weight, 0.9-1.2% of Si, 0.1-0.25% of Fe, less than or equal to 0.1% of Cu, 0. 5-0.6% of Mn, 0.8-1.1% of Mg, less than or equal to 0.1%of Cr, less than or equal to 0.1% of Zn, 0.01-0.02% of Ti, less than or equal to 0.05% of a single impurity, less than or equal to 0.15% of total impurities, and the balance Al. The defect that the existing 6082 aluminum alloy is wide in range is solved, due to the existence of Fe and Mn elements in the alloy, micron-scale AlFeSi, AlMnSiFe and Al6Mn phases are often separated out in the solidificationprocess, the coarse one-time solidification phases is hard and brittle, is difficult to dissolve in an aluminum matrix in subsequent homogenization and solid solution treatment, in the stamping process, a crack source can be easily formed, so that stamping cracking is caused; by controlling the component range of 6082 aluminum alloy, a thin plate with good stamping performance is obtained.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy processing, and relates to a 6082S aluminum alloy sheet for stamping and a processing technology thereof. Background technique [0002] 6xxx series alloys are the most important press-worked alloys in wrought aluminum alloys. They are aluminum alloys with magnesium and silicon as the main alloying elements. The main strengthening phase is the intermetallic compound Mg formed by magnesium and silicon. 2 Si is an aluminum alloy that can be strengthened by heat treatment. 6xxx series alloys have medium strength, good plasticity, excellent weldability and corrosion resistance, and no tendency to stress corrosion cracking. Therefore, 6xxx series alloys are the most widely used aluminum alloys in the world. 6082 aluminum alloy is the main alloy member in 6xxx alloy, 6082 alloy usually has good processing characteristics and excellent bending performance. In O state and T4 state, it has good be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/02C22C21/08C22F1/043C22F1/047C22F1/05C22C1/06
CPCC22C1/06C22C21/02C22C21/08C22F1/043C22F1/047C22F1/05
Inventor 刘俊涛赵俊才宋扬蔡鹏程郭富安马青梅
Owner TIANJIN ZHONGWANG ALUMINUM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com