A kind of method of coating zinc oxide graphene reinforced magnesium alloy composite material

A technology for strengthening magnesium alloys and composite materials, which is applied in the field of preparation of magnesium alloy composite materials to achieve the effects of improving the quality of interface bonding, improving uniform dispersion, and greatly improving the range.

Active Publication Date: 2020-02-14
JIANGXI TIANYUE AUTOMOBILE PARTS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Currently, research on graphene-reinforced magnesium alloy composites is still in its infancy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method of coating zinc oxide graphene reinforced magnesium alloy composite material
  • A kind of method of coating zinc oxide graphene reinforced magnesium alloy composite material
  • A kind of method of coating zinc oxide graphene reinforced magnesium alloy composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The method for coating the zinc oxide graphene reinforced magnesium alloy composite material comprises the following steps.

[0021] (1) Coated zinc oxide graphene pre-dispersion: According to the concentration ratio of 1g / L, the coated zinc oxide graphene was added to ethanol or distilled water, and ultrasonically 0.5h to obtain a uniformly dispersed reinforcement phase dispersion.

[0022] (2) According to the ratio of the mass ratio of coated zinc oxide graphene to pure aluminum powder of 10:90, add the pure aluminum powder with a particle size of less than 400 mesh into the dispersion obtained in step (1), ultrasonically and mechanically stir for 0.5h A uniformly mixed slurry of coated zinc oxide graphene-aluminum powder is obtained.

[0023] (3) After filtering the slurry obtained in step (2), vacuum drying is performed to obtain a mixed powder coated with zinc oxide graphene-aluminum powder which is pre-dispersed uniformly.

[0024] (4) Use the mixed powder obtai...

Embodiment 2

[0031] The method for coating the zinc oxide graphene reinforced magnesium alloy composite material comprises the following steps.

[0032] (1) Coated zinc oxide graphene pre-dispersion: according to the concentration ratio of 2g / L, the coated zinc oxide graphene is added to ethanol or distilled water, and ultrasonicated for 1 hour to obtain a uniformly dispersed reinforcement phase dispersion.

[0033] (2) According to the mass ratio of coated zinc oxide graphene and pure aluminum powder as 15:85, add pure aluminum powder with a particle size of less than 400 meshes to the dispersion obtained in step (1), ultrasonically and mechanically stir for 1 hour to obtain A uniformly mixed slurry of coated zinc oxide graphene-aluminum powder.

[0034] (3) After filtering the slurry obtained in step (2), vacuum drying is performed to obtain a mixed powder coated with zinc oxide graphene-aluminum powder which is pre-dispersed uniformly.

[0035] (4) Use the mixed powder obtained in step...

Embodiment 3

[0042] The method for coating the zinc oxide graphene reinforced magnesium alloy composite material comprises the following steps.

[0043] (1) Coated zinc oxide graphene pre-dispersion: according to the concentration ratio of 5g / L, the coated zinc oxide graphene is added to ethanol or distilled water, and ultrasonicated for 2 hours to obtain a uniformly dispersed reinforcement phase dispersion.

[0044](2) According to the mass ratio of coated zinc oxide graphene and pure aluminum powder as 25:75, add pure aluminum powder with a particle size of less than 400 meshes to the dispersion obtained in step (1), ultrasonically and mechanically stir for 2 hours to obtain A uniformly mixed slurry of coated zinc oxide graphene-aluminum powder.

[0045] (3) After filtering the slurry obtained in step (2), vacuum drying is performed to obtain a mixed powder coated with zinc oxide graphene-aluminum powder which is pre-dispersed uniformly.

[0046] (4) Use the mixed powder obtained in ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Vickers hardnessaaaaaaaaaa
yield strengthaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for reinforcing a magnesium alloy compound material through zinc oxide-covering graphene. The method comprises the following steps that a liquid-state dispersion method is adopted for firstly preparing a preform green body with a mass ratio of the zinc oxide-covering graphene to pure aluminum powder equal to 10-25%, then the preform green body is added into magnesium alloy melt, and after ultrasonic dispersion treatment with power of 500-1000 W is conducted for 120 min, under a condition of 550-630 DEG C, a casting method is adopted for preparing the AZ91 magnesium alloy compound material reinforced by the zinc oxide-covering graphene with a content of 0.1-5%. By means of the method for reinforcing the magnesium alloy compound material through the zinc oxide-covering graphene, the even dispersion of the graphene in a magnesium matrix can be effectively improved, the interface bonding quality of the graphene and the magnesium matrix is improved, meanwhile, a good crystal grain refining effect is obtained, and the mechanical performance of the compound material is greatly improved, so that the method for reinforcing the magnesium alloy compound material through the zinc oxide-covering graphene is suitable for preparing the graphene-magnesium alloy compound material excellent in performance on a large scale.

Description

technical field [0001] The invention belongs to the field of metal composite material preparation, in particular to a preparation method of magnesium alloy composite material. Background technique [0002] Magnesium alloy composites have a series of advantages such as high specific strength, high specific stiffness, good shock absorption and wear resistance, making them have huge potential application prospects in the fields of electronics, aerospace and automobiles. How to develop lightweight, high-strength and high-toughness magnesium alloy composites has become one of the research hotspots in the field of materials. As an obvious member of the nanocarbon family, graphene is considered to be an excellent reinforcement for magnesium alloys due to its good electrical and thermal conductivity and excellent mechanical properties. Currently, research on graphene-reinforced magnesium alloy composites is still in its infancy. Like carbon nanotubes, graphene has weak interfacial...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/10C22C1/02C22C1/06C22C23/00
CPCC22C1/06C22C1/1036C22C23/00
Inventor 袁秋红廖琳周国华林泉博
Owner JIANGXI TIANYUE AUTOMOBILE PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com