Wide and thin specification NM450 wear-resistant steel plate and fabrication method

A manufacturing method and thin gauge technology, applied in the field of metallurgy, can solve the problems of difficulty in meeting large-scale, lightweight and long-life, not wide width, not thin thickness, etc., and achieve good development value and market prospects, good unevenness. , the effect of high wear resistance

Inactive Publication Date: 2019-01-11
NANJING IRON & STEEL CO LTD
View PDF12 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there have been many patent reports on low-alloy wear-resistant steel, but the thickness of its production is not thin, and at the same time, it can produce thin specifications but the width is not wide, which is difficult to meet the large-scale, lightweight and long-life manufacturing of equipment manufacturing. demand, especially for low-alloy wear-resistant steel plates with a Brinell hardness of 450HB, there are fewer products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wide and thin specification NM450 wear-resistant steel plate and fabrication method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] This embodiment takes the manufacture of a wide and thin wear-resistant steel plate with a thickness of 6mm, a width of 2600-3100mm, and a Brinell hardness of 450HB as an example. Its chemical composition and mass percentage are as follows: C: 0.19%, Si: 0.33%, Mn: 1.10%, P : 0.011%, S: 0.0020%, Cr: 0.34%, Ti: 0.015%, B: 0.0016%, and the rest are Fe and unavoidable impurities.

[0023] The manufacturing method includes hot metal desulfurization pretreatment-converter smelting-LF+RH refining-continuous casting-slab heating-phosphorus removal-rolling-air cooling-flaw detection-shot blasting-quenching-tempering-strong straightening-cutting-sampling-spraying Print logo-inspection-warehousing.

[0024] The molten steel smelted according to the above ratio is vacuum degassed and then continuously cast. The thickness of the continuous casting slab is 150mm. The steel slab is heated to a furnace temperature of 1220°C. The final rolling thickness of the steel plate is 6mm and t...

Embodiment 2

[0026] This embodiment takes the manufacture of a wide and thin wear-resistant steel plate with a thickness of 6mm, a width of 2600-3100mm, and a Brinell hardness of 450HB as an example. Its chemical composition and mass percentage are as follows: C: 0.20%, Si: 0.34%, Mn: 1.08%, P : 0.010%, S: 0.0015%, Cr: 0.35%, Ti: 0.018%, B: 0.0015%, and the rest are Fe and unavoidable impurities.

[0027] The manufacturing method includes hot metal desulfurization pretreatment-converter smelting-LF+RH refining-continuous casting-slab heating-phosphorus removal-rolling-air cooling-flaw detection-shot blasting-quenching-tempering-strong straightening-cutting-sampling-spraying Print logo-inspection-warehousing.

[0028] The molten steel smelted according to the above ratio is vacuum degassed and then continuously cast. The thickness of the continuous casting slab is 150mm. The steel slab is heated to a furnace temperature of 1230°C. The final rolling thickness of the steel plate is 6mm and t...

Embodiment 3

[0030]This embodiment takes the manufacture of a wide and thin wear-resistant steel plate with a thickness of 6mm, a width of 2600-3100mm, and a Brinell hardness of 450HB as an example. Its chemical composition and mass percentage are as follows: C: 0.19%, Si: 0.34%, Mn: 1.09%, P : 0.010%, S: 0.0020%, Cr: 0.33%, Ti: 0.017%, B: 0.0017%, and the rest are Fe and unavoidable impurities.

[0031] The manufacturing method includes hot metal desulfurization pretreatment-converter smelting-LF+RH refining-continuous casting-slab heating-phosphorus removal-rolling-air cooling-flaw detection-shot blasting-quenching-tempering-strong straightening-cutting-sampling-spraying Print logo-inspection-warehousing.

[0032] The molten steel smelted according to the above ratio is vacuum degassed and then continuously cast. The thickness of the continuous casting slab is 150mm. The steel slab is heated to a furnace temperature of 1220°C. The final rolling thickness of the steel plate is 6 mm and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Widthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Impact energyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a wide and thin specification NM450 wear-resistant steel plate and relates to the technical field of metallurgy. The wide and thin specification NM450 wear-resistant steel plate comprises the following chemical ingredients of, in percentage by mass, 0.18-0.22% of C, 0.20-0.60% of Si, 0.8-1.2% of Mn, less than or equal to 0.012% of P, less than or equal to 0.003% of S, 0.30-0.50% of Cr, 0.008-0.030% of Ti, 0.0008-0.0025% of B and the balance Fe and unavoidable impurities. According to the wide and thin specification NM450 wear-resistant steel plate and a fabrication method, the designed wear-resistant steel reaches the 450 HB grade in brinell hardness and has a chemical ingredient system of good toughness and high strength, a related rolling and heat treating processis simple, the controllable range of heat treating parameters is wide, the comprehensive performance of products is good, and the wide and thin specification NM450 wear-resistant steel plate and thefabrication method have good development value and market prospects.

Description

technical field [0001] The invention relates to the technical field of metallurgy, in particular to a wide and thin NM450 wear-resistant steel plate and a manufacturing method. Background technique [0002] Compared with traditional wear-resistant cast steel, low-alloy wear-resistant steel plate has low alloy content, high low-temperature impact toughness, good comprehensive properties such as bending and forming, flexible and convenient production, and low production cost. It is widely used in work Harsh conditions require high strength and hardness, good wear resistance engineering, mining, construction, agriculture, cement, port, electric power and metallurgy and other machinery and equipment manufacturing, such as bulldozers, loaders, excavators, dump trucks, ball mills and various A variety of mining machinery, grab buckets, stackers and reclaimers, feeding bending structures, etc. Such parts generally work under extremely harsh conditions of dry and wet environments, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21D1/18C21D8/02C22C38/02C22C38/04C22C38/28C22C38/32
Inventor 姜在伟闫强军姜辉侯中华杨柳
Owner NANJING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com