High-permeability coloring environment-friendly ceramic product and making method thereof

A ceramic product, high-penetration technology, applied in the field of ceramics, can solve the problems of difficulty in coloring ceramic products, the pattern is easy to wear off, and there are not too many successful technologies, and achieve the effects of high strength, lower sintering temperature, and lower sintering temperature.

Active Publication Date: 2018-12-21
FUJIAN PROVINCE DEHUA COUNTY GRANGTOP CERAMICS CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, with the development of the economy, colored ceramic products are more and more widely used in people's lives, but it is very difficult to manufacture colored ceramic products with stable coloring and specific patterns, because the painted patterns will be changed during use. prone to wear off
[0004] At the same time, my country is now the largest ceramic producer, and a large amount of ceramic waste is discarded as garbage every day. At present, there are not many successful technologies to learn from the domestic production of ceramic waste into environmentally friendly ceramic products. Therefore, it is necessary to study new alternatives. Improve this issue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-permeability coloring environment-friendly ceramic product and making method thereof
  • High-permeability coloring environment-friendly ceramic product and making method thereof
  • High-permeability coloring environment-friendly ceramic product and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A highly permeable colored environmentally friendly ceramic product, comprising a body and a permeable layer applied on the surface of the body, the body includes the following raw materials in parts by weight:

[0031] 38 parts by weight of kaolin;

[0032] Aluminum oxide 24 parts by weight;

[0033] 10 parts by weight of wollastonite;

[0034] The permeable layer includes the following raw materials in parts by weight:

[0035]

[0036]

[0037] Specifically, the flux is composed of sodium oxide, potassium carbonate and sodium silicate in a mass ratio of 1:2:2.

[0038] Specifically, the particle size of the ceramic waste slag is 12mm.

[0039] Specifically, the ceramic penetrating color aid is fumed white carbon black.

[0040] Specifically, the thickness of the permeable layer is 2.3mm.

[0041] The technique of making described a kind of highly permeable colored environment-friendly ceramic product comprises the following steps:

[0042] S1 Raw material...

Embodiment 2

[0047] A highly permeable colored environmentally friendly ceramic product, comprising a body and a permeable layer applied on the surface of the body, the body includes the following raw materials in parts by weight:

[0048] 28 parts by weight of kaolin;

[0049] Aluminum oxide 19 parts by weight;

[0050] Wollastonite 8 parts by weight;

[0051] The permeable layer includes the following raw materials in parts by weight:

[0052]

[0053]

[0054] Specifically, the flux is composed of sodium oxide, potassium carbonate and sodium silicate in a mass ratio of 1:2:2.

[0055] Specifically, the particle size of the ceramic waste slag is 9mm.

[0056] Specifically, the ceramic penetrating color aid is fumed white carbon black.

[0057] Specifically, the thickness of the permeable layer is 1.8mm.

[0058] The technique of making described a kind of highly permeable colored environment-friendly ceramic product comprises the following steps:

[0059] S1 Raw material prep...

Embodiment 3

[0064] A highly permeable colored environmentally friendly ceramic product, comprising a body and a permeable layer applied on the surface of the body, the body includes the following raw materials in parts by weight:

[0065] 38 parts by weight of kaolin;

[0066] Aluminum oxide 24 parts by weight;

[0067] 10 parts by weight of wollastonite;

[0068] The permeable layer includes the following raw materials in parts by weight:

[0069]

[0070] Specifically, the flux is composed of sodium oxide, potassium carbonate and sodium silicate in a mass ratio of 1:2:2.

[0071] Specifically, the particle size of the ceramic waste slag is 12mm.

[0072] Specifically, the ceramic penetrating color aid is fumed white carbon black.

[0073] Specifically, the thickness of the permeable layer is 2.3mm.

[0074] The technique of making described a kind of highly permeable colored environment-friendly ceramic product comprises the following steps:

[0075] S1 Raw material preparation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of ceramics and in particular relates to a high-permeability coloring environment-friendly ceramic product and a making method thereof. The ceramic productcomprises a blank body and a permeation layer, wherein the permeation layer is arranged on the surface of the blank body; the blank body comprises the following raw materials in parts by weight: 23-38 parts of kaolin, 16-24 parts of aluminum oxide and 6-10 parts of wollastonite; the blank body comprises the following raw materials in parts by weight: 42-55 parts of ceramic waste residue granules,5-14 parts of a fluxing agent, 20-25 parts of albite, 8-16 parts of aluminum oxide, 13-16 parts of zirconium oxide, 6-12 parts of ceramic permeation coloring aids and 10-18 parts of silicon oxide. The making method comprises the following steps: S1, preparing raw materials; S2, making the blank body; S3, making the permeation layer; S4, carrying out firing. The ceramic product provided by the invention has the advantages of being high in permeability and coloring performance.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a highly permeable and colored environment-friendly ceramic product and a manufacturing method thereof. Background technique [0002] The firing and application of ceramic products has a long history in our country. Its various shapes, colorful colors, cool and smooth feel, easy to wash, are deeply loved by the Chinese people. The production methods of ceramic products are divided into three types: over-glaze color, under-glaze color and in-glaze color. Overglaze color ceramics are made of pigments and pasted on the glaze surface or directly painted on the surface of the product with pigments, and then fired at low temperature. Since the firing temperature cannot reach the degree of melting of the glaze layer, the patterned surface cannot Sinks into the glaze. Touch the overglaze color ceramics with your hands, and you can feel the obvious unevenness on the flower surface; the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B41/87C04B33/32
CPCC04B33/131C04B33/32C04B41/009C04B41/5042C04B41/87C04B2235/9661C04B2235/96C04B2235/6567C04B2235/6562C04B2235/3454C04B2235/3217C04B41/5035C04B41/5031C04B41/5024C04B41/4539
Inventor 李桂贤刁龙海
Owner FUJIAN PROVINCE DEHUA COUNTY GRANGTOP CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com