A preparation method of high-temperature-resistant and wear-resistant brake pads

A wear-resistant, brake pad technology, used in chemical instruments and methods, friction linings, mechanical equipment, etc., can solve the problems of insufficient wear resistance and poor high temperature resistance of brake pads, and achieve impact resistance and mechanical strength. Effect of improvement, high temperature resistance and strength improvement, mechanical properties and wear resistance improvement

Active Publication Date: 2018-11-27
山西罗克森实业有限公司
View PDF13 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The technical problem to be solved by the present invention is to provide a method for preparing a high-temperature-resistant wear-resistant brake pad in view of the defects of insufficient wear resistance and poor high-temperature resistance of the current brake pads

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of high-temperature-resistant and wear-resistant brake pads

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029]In terms of parts by weight, weigh 5-7 parts of titanium powder, 5.0-5.5 parts of carbon powder, 10-11 parts of aluminum powder and 12-13 parts of iron powder into a three-dimensional mixer and mix at a speed of 200-300r / min 5 to 6 hours to prepare the solid mixture, in parts by weight, put 3 to 5 parts of the solid mixture, 1 to 2 parts of urea granules and 10 to 11 parts of absolute ethanol in a three-dimensional mixer and mix for 5 to 6 hours to obtain the solid mixture. Liquid mixture; put the above solid-liquid mixture into a muffle furnace, heat up to 220-230°C and preheat for 60-70 minutes. The iron powder is mixed according to the mass ratio of 1:2 to prepare the ignition powder, and the ignition powder with a mass of 50-60% of the solid-liquid mixture is put into the muffle furnace, and the combustion reaction is 40-50 minutes. The metal composite product is obtained, and it is set aside; in parts by weight, 3 to 5 parts of graphite powder, 1.5 to 1.8 parts of p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a high-temperature-resistant and wear-resistant brake pad, belonging to the technical field of brake pad preparation. In accordance with that invention, titanium pow, Carbon powder, aluminum powder and iron powder are mixed, A metal composite product is prepare by adding urea and absolute ethanol, oxidizing graphite powder, A modified mixture is prepared by reduction and modification, A metal composite product of that mix slurry, A high-temperature-resistant and wear-resistant brake pad is obtain by mixing that modify mixture and pressing the mixture into a mold, Volatilization of urea particles, A metal mixture is microscopically porou, in the pores of the metal mixture filled with the modified nano-graphene, making the microstructure of the metal mixture stronger, The impact resistance and mechanical strength of the brake pads are effectively improved, and the high temperature resistance and strength of the metal mixture can be greatlyimproved by the introduction of titanium, and the high temperature resistance of the metal mixture can be further improved by the modified graphene, and the carboxyl and ester groups in tung oil canimprove the mechanical strength and wear resistance of the brake pads, so that the brake pads have a broad application prospect.

Description

technical field [0001] The invention relates to a method for preparing a high-temperature-resistant and wear-resistant brake pad, and belongs to the technical field of brake pad preparation. Background technique [0002] At present, with people's pursuit of modern quality of life, cars have become an indispensable daily necessities in family life. Cars have entered the homes of ordinary people in large numbers. The performance of cars, especially the braking performance, has become a common concern of the society. Because the car brake pad is a key component in the car brake, the performance of the brake pad is directly related to the reliability, stability and safety of the car's operation. [0003] The brake pad is composed of a back plate, an adhesive layer and a friction block, and is the most critical safety part in the automobile braking system. [0004] When braking, it is squeezed on the brake disc or drum to generate friction, so as to achieve the purpose of vehicl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F16D69/02C09K3/14
CPCC09K3/14F16D69/027F16D2200/0008F16D2200/0026F16D2200/003F16D2200/0052F16D2200/0086
Inventor 薛向东蒋梦成陈帅
Owner 山西罗克森实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com