A method for increasing production of butadiene

A technology of butadiene and reactor is applied in the field of selective hydrogenation of highly unsaturated hydrocarbons to increase butadiene production, which can solve the problems of deactivation, easy agglomeration and poisoning of active components, and achieve extended life and hydrogenation stability. And the effect of strong anti-coking performance and high selectivity

Active Publication Date: 2021-06-01
PETROCHINA CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] The active components of conventional noble metal catalysts are prone to agglomeration and poisoning and deactivation during the reaction process, and the dispersion of palladium metal is a problem that many researchers are trying to solve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for increasing production of butadiene
  • A method for increasing production of butadiene
  • A method for increasing production of butadiene

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0056] Embodiment uses the preparation of catalyst 1~6

[0057] Preparation of Catalyst C1:

[0058] Dilute 2L concentration to 100g Al 2 o 3 / L of sodium metaaluminate solution is placed in a stainless steel container with a stirrer and gas can be introduced into the bottom of the tank, the nickel nitrate solution is prepared and placed in a high-position container, a mixed gas of carbon dioxide and air is introduced, and the peristaltic pump is started at the same time Control the flow rate and drop the prepared nickel nitrate solution, the carbon dioxide concentration in the mixed gas is 60v%, and the flow rate is 5Nm 3 / h, the reaction temperature is 40°C, the pH value at the end of the reaction is 9.5, stop feeding carbon dioxide, age for 30 minutes, filter and separate the mother liquor, wash, and dry at 120°C for 5 hours to obtain nickel-containing pseudo-boehmite.

[0059] Mix and knead nickel-containing pseudo-boehmite with nitric acid and water, extrude into strip...

Embodiment 1

[0086] Dilute the alkyne-rich C4 fraction with raffinate C4 and cracked C4, and the weight ratio of the alkyne-rich C4 fraction to (raffinate + cracked C4) is 1:4. The adiabatic reactor adopts a single-stage adiabatic bubbling bed, using catalyst C1, and the catalyst is reduced at 120°C for 6h under a hydrogen atmosphere. The reaction inlet temperature is 50°C, the reaction pressure is 2.0MPa, and the liquid space velocity is 10h -1 , the molar ratio of hydrogen to alkyne is 4.0, Table 2 is the composition of materials before and after the reaction.

[0087] Material composition before and after table 2 reaction

[0088]

Embodiment 2

[0090] The C4 fraction rich in alkynes is diluted with C4 raffinate and C4 cracked, and the weight ratio of the C4 fraction rich in alkynes to (C4 raffinate+C4 cracked) is 1:5. The adiabatic reactor adopts a single-stage adiabatic bubbling bed, using catalyst C2, and the catalyst is reduced at 120°C for 6 hours under a hydrogen atmosphere. The reaction inlet temperature is 45°C, the reaction pressure is 1.5MPa, and the liquid space velocity is 12h -1 , the molar ratio of hydrogen to alkyne is 3.0, Table 3 is the composition of materials before and after the reaction.

[0091] Table 3 Composition of materials before and after reaction

[0092]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

A method for increasing the production of butadiene, using the alkyne-rich C4 fraction after the extraction of butadiene as a raw material, in the presence of a catalyst, using an adiabatic reactor, selective hydrogenation to obtain 1,3-butadiene, The operating conditions for hydrogenation are as follows: the reactor inlet temperature is 20-70°C, the reaction pressure is 0.8-3.0MPa, and the liquid space velocity is 10-30h ‑1 . The catalyst is a palladium-silver-lead catalyst prepared on a nickel-containing alumina carrier with a specific crystal form, which can greatly improve the dispersion and utilization of active metals and improve the hydrogenation performance of the catalyst. Adopting the method of the invention has very obvious good effects on the effective utilization of the C4 fraction rich in alkynes after the extraction of butadiene, the reduction of waste of resources and the improvement of economic benefits.

Description

technical field [0001] The invention relates to a method for increasing the production of butadiene, in particular to a method for increasing the production of butadiene by selective hydrogenation of highly unsaturated hydrocarbons in the C4 fraction. Background technique [0002] The cracked C4 fraction usually contains 40% to 60% butadiene by mass in the pyrolysis of hydrocarbons to produce ethylene. Butadiene is an important monomer in the synthetic rubber industry. The extraction of butadiene from the cracked C4 fraction usually adopts solvent extraction methods, such as acetonitrile method, N-methylpyrrolidone method and dimethylformamide method. Due to the high concentration of alkynes in the extracted C4 fraction, and there is no industrial use value at present, it can only be used for combustion treatment. However, because of the danger of explosion of high-concentration alkynes, it is recommended for safety reasons in industrial production. Considering that when se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07C5/05C07C11/167B01J23/89B01J35/10
CPCB01J23/002B01J23/8966B01J35/1014B01J35/1038B01J35/1042B01J2523/00C07C5/05C07C2523/89C07C11/167B01J2523/824B01J2523/18B01J2523/44B01J2523/847B01J2523/22B01J2523/11B01J2523/3706B01J2523/13B01J2523/3712
Inventor 钱颖郑云弟胡晓丽马好文展学成王斌孙利民蒋彩兰黄德华边虎刘敏尹玲玲
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap