Preparation method of self-slow-setting concrete

A kind of concrete, selected technology, applied in the field of preparation of self-retarding concrete

Inactive Publication Date: 2018-10-19
芜湖恒固混凝土材料有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary concrete cannot meet this requirement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0021] The present invention also provides a kind of preparation method of self-retarding concrete, comprises the following steps:

[0022] (1) Evenly ball-mill bentonite and kaolin and calcinate at 300-450°C for 2-4 hours to obtain a mixed powder, then mill the mixed powder, diethylenetriaminepentamethylenephosphonic acid and gypsum in a ball mill, and then add water, and then microwave reaction at 80-95°C for 5-10 hours to obtain modified mineral powder;

[0023] (2) After uniformly mixing unsaturated glycerol, fatty alcohol polyoxyethylene ether, polyol, acid anhydride and polyamine in water, react at 80-120°C for 2-4 hours to obtain a slow-setting intermediate;

[0024] (3) After uniformly dispersing the retarder intermediate, fly ash, cement, fine sand, clay ceramsite, aluminum silicate fiber, modified mineral powder, and additives in water, continue stirring for 60-150s to obtain the self- retarded concrete.

[0025] In the present invention, first, bentonite, kaolin a...

Embodiment 1

[0028] A self-retarding concrete, made of the following raw materials in parts by weight: 30kg fly ash, 25kg cement, 22kg fine sand, 15kg clay ceramsite, 8kg bentonite, 12kg kaolin, 12kg gypsum, 2kg diethylenetriaminepenta Forkedphosphonic acid, 10kg aluminum silicate fiber, 8kg glycidyl methacrylate, 3kg fatty alcohol polyoxyethylene ether (purchased from Haidongqing Chemical Co., Ltd., AEO-9), 3kg polybutylene terephthalate , 2kg N-(2-aminoethyl)-1,3-propylenediamine, 4kg phthalic anhydride, 0.5kg polycarboxylate superplasticizer (model PASP-Ca, purchased from Shandong Yuanlian Chemical Co., Ltd.) , 1kg sodium dodecylbenzenesulfonate, 0.5kg calcium stearate, 0.5kg hydroxyethyl methyl reinforced cellulose ether, 0.5kg sodium aluminate.

[0029] The preparation steps of described self-retarding concrete are as follows:

[0030] (1) After uniform ball milling of bentonite and kaolin, calcining at 350°C for 3 hours to obtain a mixed powder, then ball milling the mixed powder, d...

Embodiment 2

[0034]A self-retarding concrete, made of the following raw materials in parts by weight: 36kg fly ash, 30kg cement, 16kg fine sand, 18kg clay ceramsite, 6kg bentonite, 8kg kaolin, 6kg gypsum, 2kg diethylene triamine pentamethyl Forkedphosphonic acid, 12kg aluminum silicate fiber, 5kg 2-glycidyl methacrylate, 5kg fatty alcohol polyoxyethylene ether (purchased from Costin Chemical Co., Ltd., AEO-9), 2kg polyoxypropylene glycol, 3kg Diethylenetriamine, 6kg maleic acid, 1kg polycarboxylate water reducer (model PASP-Ca, purchased from Shandong Yuanlian Chemical Co., Ltd.), 1kg sodium dodecylbenzenesulfonate, 1kg stearic acid Calcium, 1kg hydroxyethyl methyl reinforced cellulose ether, 1kg sodium aluminate.

[0035] The preparation steps of described self-retarding concrete are as follows:

[0036] (1) After uniform ball milling of bentonite and kaolin, calcining at 450°C for 2 hours to obtain a mixed powder, then ball milling the mixed powder, diethylenetriaminepentamethylenephosp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of concrete and preparation, and specifically relates to a preparation method of self-slow-setting concrete. The preparation method of the self-slow-setting concrete comprises the following steps: (1) modifying gypsum through roasted bentonite and kaolin and etidronic acid to obtain mineral powder; (2) uniformly mixing unsaturated glyceryl alcohol, fatty alcohol-polyoxyethylene ether, polyhydric alcohol, anhydride and polyamine; and reacting for 2-4h under the temperature of 80-120 DEG C to obtain a slow setting intermediate; and (3) uniformly dispersing the slow setting intermediate, coal ash, cement, fine sand, clay ceramsite, alumina silicate fibers, modified mineral powder and additives in water; and continuously stirring for 60-150s to obtain the self-slow-setting concrete. The self-slow-setting concrete prepared by the method is set for 60-85h, and has a good application prospect, and is low in cost and high in economic benefit.

Description

technical field [0001] The invention relates to the technical field of concrete and its preparation, in particular to a preparation method of self-retarding concrete. Background technique [0002] Concrete has the characteristics of rich raw materials, low price and simple production process, so its consumption is increasing. At the same time, concrete also has the characteristics of high compressive strength, good durability, and a wide range of strength grades. These characteristics make it widely used, not only in various civil engineering, but also in shipbuilding, machinery industry, marine development, geothermal engineering, etc. Concrete is also an important material. [0003] With the continuous development of construction technology, concrete with various special requirements emerges as the times require. At the same time, the improvement of the level of construction equipment and the continuous emergence and promotion of new construction techniques have made con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/02
CPCC04B28/02C04B2201/50C04B18/08C04B14/06C04B18/027C04B14/104C04B14/106C04B14/365C04B24/003C04B14/4656C04B24/045C04B24/32C04B24/283C04B24/121C04B24/04C04B24/16C04B24/085C04B24/383C04B22/08C04B2103/302C04B24/281C04B24/02
Inventor 承忠富
Owner 芜湖恒固混凝土材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com